循环伏安法研究银表面自组装膜的致密性

刘金红; 刘金红顾宁

南京工业大学

CYCLIC VOLTAMMETRY STUDY OF SELF-ASSEMBLED LAYER ON SILVER

;

南京工业大学

全文: PDF(230 KB)

摘要: 在Ag电极表面制备了3-巯基丙基三甲氧基硅烷(MPS)自组装单分子膜，通过循环伏安曲线(CV)、接触角等方法对修饰电极的电化学性能、组装膜的致密性等进行了研究.结果表明：修饰后电极的CV曲线峰电流减小、还原峰位发生负移及峰电位差增大，说明MPS已经在Ag电极表面成膜，对电子传输具有明显的抑制作用.膜的致密性受组装液浓度及组装时间的影响，当MPS的浓度为01 mmol/L、组装时间为6 h时，抑制电化学反应的效果较好，组装膜成膜状况较为理想.对不同水解时间接触角的分析表明，水解时间不同，MPS尾基的水解自聚度不同，延长水解时间能提高组装膜的致密度.

关键词 ：自组装膜, 循环伏安, 3－巯基丙基三甲氧基硅

Abstract：According to SEM observation,the corrosion regulati on of LC4 aluminum alloy with alclad in China water system and the protection of alclad on LC4 were studied.The corrosion experiment was done in seawater of Qin gdao,Zhoushan,Xiamen,salt lake with high salinity of Geermu,and fresh water of C hangjiang River in Hankou.The results of the corrosion experiment of two periods for half a year and one year show the protection of alclad on LC4 aluminum allo y was different because of different water.In seawater and fresh water,aluminum alloy was not corroded as the all protection of alclad.In salt lake,the alclad o n LC4 aluminum alloy remaindered for half a year,and used up for one year.The ba se of LC4 aluminum alloy was corroded seriously.

Key words： self-assembled monolayer cyclic voltammetry 3-mercaptopropyltrimethoxysilane

收稿日期: 2005-09-06

ZTFLH:

O646

通讯作者: 刘金红 E-mail: jinhongkl@163.com

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	刘金红
	刘金红
	顾宁
44.8K

引用本文:

刘金红; 刘金红; 顾宁 . 循环伏安法研究银表面自组装膜的致密性[J]. 中国腐蚀与防护学报, 2006, 26(5): 291-294 .
. CYCLIC VOLTAMMETRY STUDY OF SELF-ASSEMBLED LAYER ON SILVER. J Chin Soc Corr Pro, 2006, 26(5): 291-294 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2006/V26/I5/291

[1]Ulman A.Formation and structure of self-assembled monolayers[J].Chem.Rev.,1996,96:1533-1544
[2]Cao Y H,Li Y S,Tseng J L,et al.Interfacial study of benzene sulfi-nate chemisorbed on silver[J].Spectrochimica Acta Part A,2001,57:27-34
[3]Yu H Z,Shao H B,Luo Y,et al.Evaluation of the tunneling con-stant for long range electron transfer in azobenzene self-assembledmonolayers on gold[J].Langmuir,1997,13:5774-5776
[4]Janek R P,Fawcett W R,Ulman A.Impedance spectroscopy of self-assembled monolayers on Au(111)sodium ferrocyanide chargetransfer at modified electrodes[J].Langmuir,1998,14:3011-3018
[5]Miki Itoh,Hiroshi Nishihara,Kunitsugu Aramki.The protection a-bility of 11-mercapto-1-undecanol self-assembled monolayermodified with alkyltrichlorosilanes against corrosion of copper[J].J.Electrochem.Soc.,1995,142(6):1839-1846
[6]Zamborimi Francis P,Crooks Richard M.Corrosion passivation ofgold by n-alkanethiol self-assembled monolayers:effect of chainlength and end group[J].Langmuir,1998,14:3279-3286
[7]Wade R Thompson,Jeanne E Pemberton.Raman spectroscopy ofcovalently bonded alkylsilane layers on thin silica films immobilizedon silver substrates[J].Anal.Chem.,1994,66:3362-3370

[1]	张浩, 杜楠, 周文杰, 王帅星, 赵晴. 模拟海水溶液中Fe³⁺对不锈钢点蚀的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 517-522.
[2]	卢爽, 任正博, 谢锦印, 刘琳. 2-氨基苯并噻唑与苯并三氮唑复配体系对Cu的缓蚀性能[J]. 中国腐蚀与防护学报, 2020, 40(6): 577-584.
[3]	鲁文晔,陈蝶依,陈步荣,汤涛. 十六硫醇自组装膜对Ag的防变色作用研究[J]. 中国腐蚀与防护学报, 2016, 36(2): 172-176.
[4]	宋芳,陈友媛,常钦鹏,彭涛. 植酸自组装膜对HAl77-2黄铜缓蚀性能的影响[J]. 中国腐蚀与防护学报, 2015, 35(4): 317-325.
[5]	王海杰, 王佳, 彭欣, 山川. 钛合金在3.5%NaCl溶液中的腐蚀行为[J]. 中国腐蚀与防护学报, 2015, 35(1): 75-80.
[6]	潘太军, 汪涛. AZ91镁合金表面合成聚苯胺涂层及其腐蚀性能研究[J]. 中国腐蚀与防护学报, 2014, 34(6): 489-494.
[7]	梁虎, 杜敏, 张有慧. 铝合金牺牲阳极极化性能研究[J]. 中国腐蚀与防护学报, 2014, 34(2): 153-159.
[8]	王海人, 陈凤, 屈钧娥, 聂德键. 430不锈钢表面十四烷基膦酸自组装膜的制备与耐蚀性[J]. 中国腐蚀与防护学报, 2013, 33(5): 383-387.
[9]	万俐杜伟李佳佳丁毅陈步荣. 十八硫醇自组装膜对青铜-银电偶腐蚀的抑制作用[J]. 中国腐蚀与防护学报, 2013, 33(3): 245-250.
[10]	王海人,江燕,屈钧娥,李文维,陈凤,张强. 常用金属表面缓蚀自组装膜及其研究方法[J]. 中国腐蚀与防护学报, 2012, 32(4): 273-284.
[11]	张大全,谢彬,李瑾,何先明,高立新. 谷氨酸自组装膜对铜的缓蚀机理研究[J]. 中国腐蚀与防护学报, 2011, 31(1): 56-61.
[12]	王静,李德刚,于先进,董云会,张丽鹏. 十二烷基硫醇在Fe表面自组装成膜及对其的腐蚀保护[J]. 中国腐蚀与防护学报, 2010, 30(3): 207-212.
[13]	杨长江; 梁成浩 . 自组装膜在金属防护中的应用[J]. 中国腐蚀与防护学报, 2007, 27(5): 315-320 .
[14]	陈玉红; 唐致远; 童汝亭 . 席夫碱结构对铜缓蚀作用的影响[J]. 中国腐蚀与防护学报, 2007, 27(3): 156-161 .
[15]	许淳淳; 池琳; 胡钢; 黄杰; 王紫色 . HCO3-浓度对x70钢阳极反应过程的影响[J]. 中国腐蚀与防护学报, 2005, 25(1): 20-24 .

Viewed

Full text

Abstract

Cited

Shared

Discussed