镁合金微弧氧化过程中不同电压下获得膜层的性能研究

王燕华;王佳;张际标

中科院海洋所

PROPERTIES OF ANODIC COATINGS ON AZ91D Mg ALLOYS DURING MICRO-ARC OXIDATION PROCESS

Yanhua Wang;Jia Wang;Jibiao Zhang

中科院海洋所

全文: PDF(131 KB)

摘要: 采用扫描电镜、电化学阻抗方法，研究了镁合金AZ91D微弧氧化过程中不同电压下获得氧化膜的性能.结果表明，随着氧化电压的升高,可以获得三种不同性能的氧化膜：钝化膜、微火花氧化膜和弧光氧化膜.钝化膜很薄，厚度不足1μm，膜层的阻抗随着氧化电压升高略有增加，仍属于钝化膜性质；微火花放电后期得到的膜层较厚，厚度可达30 μm，表面均匀、结构致密，具有最高的阻抗，可以达到8×107Ω；弧光放电阶段氧化膜最厚，但结构疏松、易碎，阻抗逐渐降低至1×107Ω.结果还指出，硅酸盐体系中微火花放电阶段后期形成的膜层具有最佳的性能；而且膜层的阻抗主要由氧化膜的有效厚度决定，与总厚度关系不大.

关键词 ：微弧氧化, 镁合金, 性能, 阻抗, 电压

Abstract：With scanning electron microscopy (SEM) and electrochemical impedance spectroscopy (EIS) technique,properties of oxide coatings produced at different voltage on AZ91D Mg alloy substrates by micro-arc oxidation technique have been investigated.Three types of oxide coatings,passive film,micro-spark oxide coating and spark oxide coating were formed corresponding to different range of voltages.The results showed that micro-spark oxide coating exhibited the best performance of compact,homogeneous and with high resistance,comparing with other two types of oxide coatings,due to its high effective thickness.

Key words： micro-arc oxidation magnesium alloy properties resistance voltage

收稿日期: 2004-05-20

ZTFLH:

TG146.2

通讯作者: 王燕华 E-mail: wangyanhua@ms.qdio.ac.cn

Corresponding author: Yanhua Wang E-mail: wangyanhua@ms.qdio.ac.cn

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	王燕华
	王佳
	张际标
44.8K

引用本文:

王燕华; 王佳; 张际标 . 镁合金微弧氧化过程中不同电压下获得膜层的性能研究[J]. 中国腐蚀与防护学报, 2005, 25(5): 267-270 .
Yanhua Wang, Jia Wang, Jibiao Zhang. PROPERTIES OF ANODIC COATINGS ON AZ91D Mg ALLOYS DURING MICRO-ARC OXIDATION PROCESS. J Chin Soc Corr Pro, 2005, 25(5): 267-270 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2005/V25/I5/267

[1]Yerokhin A L,Voevodin A A,Lyubimov V V,et al.Plasma elec-trolytic fabrication of oxide ceramic surface layers for tribotechnicalpurposes on aluminium alloys[J].Surf.Coat.Technol.,1998,110:140-146
[2]Butyagin P I,Khokhryakov Ye V,Mamaev A I.Microplasma sys-tems for creating coatings on aluminium alloys[J].Mater.Lett.,2003,57:1748-1751
[3]Zhang Yongjun,Yan Chuanwei,Wang Fuhui,et al.Study on the en-vironmentally friendly anodizing of AZ91D magnesium alloy[J].Surf.Coat.Technol.,2002,161:36-43
[4]Hoche H,Scheerer H,Probst D,et al.Plasma anodisation as an envi-ronmental harmless method for the corrosion protection of magne-sium alloys[J].Surf.Coat.Technol.,2003,174-175:1018-1023
[5]Sundararajan G,Rama Krishna L.Mechanisms underlying the forma-tion of thick alumina coatings through the MAO coating technology[J].Surf.Coat.Technol.,2003,167:269-277
[6]Rama Krishna L,Somaraju K R C,Sundararajan G.The tribologicalperformance of ultra-hard ceramic composite coatings obtainedthrough microarc oxidation[J].Surf.Coat.Technol.,2003,163-164:484-490
[7]Goeminne G,Terryn H,Vereecken J.Characterisation of conversionlayers on aluminum by means of electrochemical impedance spec-troscopy[J].Electr.Acta,1995,40:479-486
[8]Schram T,Goeminne G,Terryn H,et al.Study of the composition ofzirconium-based chromium free conversion layers on aluminum[J].Trans.Inst.Metal Finishing,1995,73:91-95

[1]	戴婷, 顾艳红, 高辉, 刘凯龙, 谢小辉, 焦向东. 水下摩擦螺柱焊接头在饱和CO₂中的电化学性能[J]. 中国腐蚀与防护学报, 2021, 41(1): 87-95.
[2]	韩月桐, 张鹏超, 史杰夫, 李婷, 孙俊才. 质子交换膜燃料电池中TA1双极板的表面改性研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 125-130.
[3]	史昆玉, 吴伟进, 张毅, 万毅, 于传浩. TC4表面沉积Nb涂层在模拟体液环境下的电化学性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 71-79.
[4]	郑黎, 王美婷, 于宝义. 镁合金表面冷喷涂技术研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 22-28.
[5]	魏征, 马保吉, 李龙, 刘潇枫, 李慧. 镁合金表面超声滚压预处理对微弧氧化膜耐蚀性能的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 117-124.
[6]	孙海静, 覃明, 李琳. 深海低溶解氧环境下Al-Zn-In-Mg-Ti牺牲阳极性能研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 508-516.
[7]	贾世超, 高佳祺, 郭浩, 王超, 陈杨杨, 李旗, 田一梅. 再生水水质因素对铸铁管道的腐蚀研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 569-576.
[8]	于浩冉, 张文丽, 崔中雨. 4种镁合金在Cl^--NH₄⁺-NO₃^-溶液体系中的腐蚀行为差异研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 553-559.
[9]	岳亮亮, 马保吉. 超声表面滚压对AZ31B镁合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 560-568.
[10]	刘海霞, 黄峰, 袁玮, 胡骞, 刘静. 690 MPa级高强贝氏体钢在模拟乡村大气中的腐蚀行为[J]. 中国腐蚀与防护学报, 2020, 40(5): 416-424.
[11]	郏义征, 王保杰, 赵明君, 许道奎. 固溶处理制度对挤压态Mg-Zn-Y-Nd镁合金在模拟体液中腐蚀和析氢行为的影响规律研究[J]. 中国腐蚀与防护学报, 2020, 40(4): 351-357.
[12]	胡露露, 赵旭阳, 刘盼, 吴芳芳, 张鉴清, 冷文华, 曹发和. 交流电场与液膜厚度对A6082-T6铝合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(4): 342-350.
[13]	曹京宜, 方志刚, 陈晋辉, 陈志雄, 殷文昌, 杨延格, 张伟. 5083铝合金表面单致密微弧氧化膜的制备及其性能研究[J]. 中国腐蚀与防护学报, 2020, 40(3): 251-258.
[14]	孙硕, 杨杰, 钱薪竹, 常人丽. Ni-Cr-P化学镀层的制备与电化学腐蚀行为[J]. 中国腐蚀与防护学报, 2020, 40(3): 273-280.
[15]	解璇, 刘莉, 王福会. TiO₂的制备及表面修饰工艺对其光电化学阴极保护性能的影响[J]. 中国腐蚀与防护学报, 2020, 40(2): 123-130.

Viewed

Full text

Abstract

Cited

Shared

Discussed