氧乙炔火焰和等离子弧喷焊合金涂层的组织和耐腐蚀磨损性能

中国腐蚀与防护学报

2003, Vol. 23

Issue (5): 307-311

研究报告

本期目录 | 过刊浏览

氧乙炔火焰和等离子弧喷焊合金涂层的组织和耐腐蚀磨损性能

袁晓敏;斯松华;何宜柱

安徽工业大学冶金与材料学院

MICROSTRUCTURE AND CORROSION WEAR PERFORMANCE OF ALLOY LAYERS OF OXY-ACETYLENE FLAME AND PLASMA ARC SPRAYING WELDING

Xiaomin Yuan;Songhua Si;Yizhu He

安徽工业大学冶金与材料学院

全文: PDF(212 KB)

摘要: 研究了用氧乙炔火焰和等离子弧喷焊两种方法在16M n钢基材表面制备的自熔性铁基合金涂层和镍基合金涂层的显微组织、相组成、硬度和不同腐蚀介质下的腐蚀磨损性能.发现两种合金涂层组织都具有枝晶生长特征，枝晶间存在细小的共晶组织，涂层均由γ固溶体和多种共晶化合物相所组成；铁基合金涂层枝晶发达，镍基合金涂层枝晶细小；涂层硬度越高，其耐磨性越好.几种涂层的硬度和耐磨性由高到低的顺序为：HNi60→DFe55→DNi60→HFe55.合金涂层在酸碱腐蚀介质中的耐磨性与在中性水中的耐磨性相比都降低，在酸性腐蚀介质中更差.〖JP〗

关键词 ：氧乙炔火焰喷焊, 等离子弧喷焊, 组织, 硬度, 耐

Abstract：Microstructure,phase constitution,hardness and corr osion wear test of the different corrosion media of Fe-base self-fluxing alloy layers (HFe55 and DFe55) and Ni-base layers(HNi60 and DNi60) by oxy-acetylene f lame and plasma arc had been studied on the 16Mn steel substrate.Results show th at the microstructure of the layers all have characteristic of dendrites,and the layers are consisted of γ dendritic solid solution and fine eutectic structure between the dendrites.The dendrite of Fe-base layers is flourishing,but Ni-bas e layer is finer.The higher the hardness of the layers,the better the corrosion wear resistance of the layers.The order of the hardness and wear resistance from high to low is HNi60,DFe55,DNi60 and HFe55.The corrosion wear resistance of the layers in 4%HCl (pH6) and 4%NaOH (pH8) liquid media is lower than that in water,especially in 4%HCl acid media.

Key words： oxy-acetylene flame spraying welding plasma arc sprayi ng welding microstructure hardness corrosion

收稿日期: 2002-07-29

ZTFLH:

TG174.442

通讯作者: 斯松华

Corresponding author: Songhua Si

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	袁晓敏
	斯松华
	何宜柱
44.8K

引用本文:

袁晓敏; 斯松华; 何宜柱 . 氧乙炔火焰和等离子弧喷焊合金涂层的组织和耐腐蚀磨损性能[J]. 中国腐蚀与防护学报, 2003, 23(5): 307-311 .
Xiaomin Yuan, Songhua Si, Yizhu He. MICROSTRUCTURE AND CORROSION WEAR PERFORMANCE OF ALLOY LAYERS OF OXY-ACETYLENE FLAME AND PLASMA ARC SPRAYING WELDING. J Chin Soc Corr Pro, 2003, 23(5): 307-311 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2003/V23/I5/307

[1]AhaHS ,KwonOK .Wearbehaviorofplasma-sprayedpartiallystabilizedzirconiaonasteelsubstrate[J].Wear,1993,162-164:636
[2]BiXiaofang,GuoHongbo,GongShengkai,etal.InvestigationofhightemperaturehotcorrosionbehaviorofthermalbarriercoatingspreparedbyEB -PVD[J].J.Chin.Soc.Corros.Prot.,2002,22(4):84.(毕晓方,郭供波,宫声凯等电子束气相沉积热障涂层抗高温腐蚀性能的研究[J]中国腐蚀与防护学报,2002,22(2):84)
[3]WangChangsheng,LuoMeihua,YangYunlin,etal.Abrasiveresis tanceofflame-sprayingself-meltingalloycoating[J].Exploita tionandApplicationofMaterials,1997,12(4):6(王长生,罗美华,杨蕴林等.几种火焰喷焊自熔性合金层的耐磨性能[J]材料开发与应用,1997,12(4):6)
[4]SiSonghua,HeYizhun,etal.Studyonmicrostructureandcorrosion-wearperformanceofplasmasurfacingalloydeposits[J].Transac tionsoftheChinaWeldingInstitution,2002,23(2):40(斯松华,何宜柱,等.离子堆焊合金层组织及腐蚀磨损性能[J]焊接学报,2002,23(2):40)
[5]YangYongqiang.Microstructureandpropertiesoflasercladhigh-temperaturewear-resistantalloys[J].Appl.Surf.Sci.,1999,140:19
[6]SiSonghua,HeYizhu,YuanXiaomin,etal.Researchonmicrostruc turesandpropertiesoflasercladNi-basedmetal-ceramicslayers[J].ChineseJ .Lasers,2002,A29(8):759(斯松华,何宜柱,袁晓敏等激光熔覆镍基金属陶瓷涂层的组织性能研究[J].中国激光,2002,A29(8):759)
[7]DingZhangxiong,ZheQingjian.Abrasivewearcharacteristicsofself-fluxingalloysprayweldingoverlay[J].Mater.Mechanic.Eng.,1994,18(5):48(丁彰雄,曾庆健自熔合金喷焊层耐磨粒磨损特性[J].机械工程材料,1994,18(5):48)
[8]ZhangYimin,WangShunxing,XuGuizhen,etal.EffectofWCcon tentonwear-corrosionbehaviorsoflaserremeltedcoatingsofNi-basedalloy[J].Mater.Mechanic.Eng.,1994,18(5):45(张一名,王顺兴,徐桂珍等.WC加入量对镍基合金激光熔敷层腐蚀磨损性能的影响[J].机械工程材料,1994,18(5):45)

[1]	魏征, 马保吉, 李龙, 刘潇枫, 李慧. 镁合金表面超声滚压预处理对微弧氧化膜耐蚀性能的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 117-124.
[2]	黄鹏, 高荣杰, 刘文斌, 尹续保. 盐溶液刻蚀-氟化处理制备X65管线钢镀镍超双疏表面及其耐蚀性研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 96-100.
[3]	韩月桐, 张鹏超, 史杰夫, 李婷, 孙俊才. 质子交换膜燃料电池中TA1双极板的表面改性研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 125-130.
[4]	史昆玉, 吴伟进, 张毅, 万毅, 于传浩. TC4表面沉积Nb涂层在模拟体液环境下的电化学性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 71-79.
[5]	包任, 周根树, 李宏伟. 恒电位脉冲电沉积高锡青铜耐蚀镀层工艺研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 585-591.
[6]	刘海霞, 黄峰, 袁玮, 胡骞, 刘静. 690 MPa级高强贝氏体钢在模拟乡村大气中的腐蚀行为[J]. 中国腐蚀与防护学报, 2020, 40(5): 416-424.
[7]	李聪玮, 杜双明, 曾志琳, 刘二勇, 王飞虎, 马付良. 电流密度对Ni-Co-B镀层微观结构及磨蚀性能的影响[J]. 中国腐蚀与防护学报, 2020, 40(5): 439-447.
[8]	曹京宜, 方志刚, 陈晋辉, 陈志雄, 殷文昌, 杨延格, 张伟. 5083铝合金表面单致密微弧氧化膜的制备及其性能研究[J]. 中国腐蚀与防护学报, 2020, 40(3): 251-258.
[9]	王英君, 刘洪雷, 王国军, 董凯辉, 宋影伟, 倪丁瑞. 新型高强稀土Al-Zn-Mg-Cu-Sc铝合金的阳极氧化及其抗腐蚀性能研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 131-138.
[10]	郑艳欣, 刘颖, 宋青松, 郑峰, 贾玉川, 韩培德. 含铁铜基陶瓷复合材料高温氧化行为与耐磨性研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 191-198.
[11]	王乐,易丹青,刘会群,蒋龙,冯春. Ru对Ti-6Al-4V合金腐蚀行为的影响及机理研究[J]. 中国腐蚀与防护学报, 2020, 40(1): 25-30.
[12]	武栋才,韩培德. 中温时效处理对SAF2304双相不锈钢耐蚀性的影响[J]. 中国腐蚀与防护学报, 2020, 40(1): 51-56.
[13]	杨寅初,傅秀清,刘琳,马文科,沈莫奇. 喷射电沉积Ni-P-BN(h)-Al₂O₃复合镀层的耐腐蚀性能研究[J]. 中国腐蚀与防护学报, 2020, 40(1): 57-62.
[14]	苏小红,胡会娥,孔小东. W颗粒/Zr_41.2Ti_13.8Cu_12.5Ni₁₀Be_22.5基非晶复合材料在3%NaCl溶液中的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(1): 70-74.
[15]	姜冬雪,付颖,张峻巍,张伟,辛丽,朱圣龙,王福会. 钛合金表面Al₂O₃陶瓷膜制备及性能研究[J]. 中国腐蚀与防护学报, 2019, 39(6): 469-476.

Viewed

Full text

Abstract

Cited

Shared

Discussed