环境促进开裂中裂纹扩展速度的测定方法述评

牛林;林海潮;曹楚南;宋光铃;史志明

中国科学院金属腐蚀与防护研究所;金属腐蚀与防护国家重点实验室沈阳110015;中国科学院金属腐蚀与防护研究所;金属腐蚀与防护国家重点实验室沈阳110015;中国科学院金属腐蚀与防护研究所;金属腐蚀与防护国家重点实验室沈阳110015;中国科学院金属腐蚀与防护研究所;金属腐蚀与防护国家重点实验室沈阳110015;中国科学院金属腐蚀与防护研究所;金属腐蚀与防护国家重点实验室沈阳110015

EVALUATION OF DETERMINATION METHODS OF CRACK PROPAGATION RATE IN ENVIRONMENTALLY ASSISTED CRACKING

NIU Lin LIN Hai-chao CAO Chu-nan SONG Guang-ling SHI Zhi-ming(The Institute of Corrosion and Protection of Metals; Chinese Academy of Sciences; State Key Laboratory of Corrosion and Protection; Shenyang 110015)

全文: PDF(614 KB)

摘要: 文中综述了环境促进开裂中几种有代表性的裂纹扩展速度的确定方法及有关模型,并对这些方法和模型的使用范围及其优缺点进行了分析和评价。

关键词 ：裂纹扩展速度, 环境促进开裂, 方法

Abstract：The determination methods and relevant models of crack propagation rate in environmentally assisted cracking were summed up and reviewed. The advantages and shortcomings as well as application range of these methods and models were analyzed and evaluated. The main purpose of the review was to provide convincing basis not only for the most suitable determination of crack propagation rate in various complex material/environment combinations but also for the life-prediction of components in practical service.

Key words： Crack propagation rate Environmentally assisted cracking Method

收稿日期: 1998-06-25

基金资助:国家自然科学基金;;中国科学院“百人计划”资助项目

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	牛林
	林海潮
	曹楚南
	宋光铃
	史志明
44.8K

引用本文:

牛林;林海潮;曹楚南;宋光铃;史志明. 环境促进开裂中裂纹扩展速度的测定方法述评[J]. 中国腐蚀与防护学报, 1998, 18(3): 214-220.
. EVALUATION OF DETERMINATION METHODS OF CRACK PROPAGATION RATE IN ENVIRONMENTALLY ASSISTED CRACKING. J Chin Soc Corr Pro, 1998, 18(3): 214-220.

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y1998/V18/I3/214

1 Brown B F. Stress Corrosion Cracking in High Strength Steels, and in Titanium and Aluminum Alloys, NRL, Washington D C. 1972
2 Chu W, Hsiao C, Tu S, et al. Corrosion, 1982, 38:446
3 Wendier-Kalsch E. Werkstoffe and Corrosion, 1978, 29:703
4 Speidel M O. Corrosion, 1977, 33:199
5 Haruna T, Shibata T. Corrosion, 1994, 50:785
6 Speidel M O. Metall. Trans. A, 1981, 12A: 779
7 Speidel M O. The Theory of Stress Corrosion Cracking in Alloys, eds. Scully J C, NATO, Scientific Affairs Division, Brussels, 1971. p289
8 Parking R N. Brit. Corros. J., 1979, 14:5
9 Ford F P. Corrosion Processes, eds. Parkins R N, Applied Science, New York, NY, 1982. p271
10 Ford F P. EPRI Report NP2589, Palo Alto, CA: EPRI, 1982
11 Ford F P, et al. Corrosion/85, Paper no. 352, Boston, 1985
12 Ford F P. Corrosion/86, Paper no. 327, Houston, 1986
13 Parkins R N. Proc. 3rd Int. Conf. Mechanical Behavior of Materials, Cambridge, U. K, August 1979, eds. K. J. Miller et al., Pergamon Press, 1980. p139
14 Ford F P. Corrosion, 1996, 52:375
15 Congleton J, et al. Corros. Sci., 1985, 25:633
16 Parkins R N, et al. Metal Sci., 1977, 11:405
17 Parkins R N. Corrosion, 1990, 46:178
18 Turnbull A. Corros. Sci., 1993, 34:921
19 Parkins R N. Environment-induced Cracking of Metals, eds. Gangloff R Petal., NACE, Houston,1990, pl
20 Scully J C. Corros. Sci., 1968, 8:513
21 Parkins R N. Corros. Sci., 1980, 20:147
22 Jones D A. Metall. Trans. A, 1985, 16A: 1133
23 Ford F P, Burstein G T, Hoar T P. J.Electrochem. Soc., 1980, 127:6
24 Hagyard T, Earl W B. J. Electrochem. Soc., 1968, 115:623
25 Less D J, Hoar T P. Corrs. Sci., 1980, 20:723
26 Newman R C, Burstein G T. Corros. Sci., 1981, 21:119
27 Diegle R B, Lineman D M. J. Electrochem. Soc., 1984, 131:106
28 Diegle R B, Vermilyea D A. J. Electrochem. Soc., 1975, 122:180
29 Ford F P, Silverman M. Corrosion, 1980, 36:558
30 Carranza R M, Galvele J R. Corros. Sci., 1988, 28:233
31 Carranza R M, Galvele J R. Corros. Sci., 1988, 28:851
32 Galvele J R, Torresi R M, Caxrauza R M. Corros. Sci.,1990, 31:536
33 Beck T R. J. Electrochem. Soc., 1982, 129:2500
34 Beck T R. Corrosion, 1974, 30:408
35 Wei R P, Alavi A. Scrip. Metall. 1988, 22:969

[1]	寇杰, 张新策, 崔淦, 杨宝安. 储罐底板阴极保护电位分布研究进展[J]. 中国腐蚀与防护学报, 2017, 37(4): 305-314.
[2]	林翠,赵晓斌,张翼飞. 金属材料的空化腐蚀行为及影响因素研究进展[J]. 中国腐蚀与防护学报, 2016, 36(1): 11-19.
[3]	李明丽, 刘丹, 曹淑云, 彭坤, 梁平, 史艳华, 桂建舟, 刘峰. 盐酸介质中Brönsted酸离子液体对Q235钢的缓蚀行为[J]. 中国腐蚀与防护学报, 2015, 35(5): 400-406.
[4]	王凤平,刘岚,丁言伟,胡隋军,刘照斌,刘丹,张丽. 油气田H₂S腐蚀体系模拟方法探究[J]. 中国腐蚀与防护学报, 2015, 35(3): 251-256.
[5]	李强, 唐晓, 李焰. 冲刷腐蚀研究方法进展[J]. 中国腐蚀与防护学报, 2014, 34(5): 399-409.
[6]	张华孙大同张贺赵衍华马芳芳许可人. 铝合金搅拌摩擦焊接接头腐蚀行为研究进展[J]. 中国腐蚀与防护学报, 2013, 33(3): 175-181.
[7]	王海人,江燕,屈钧娥,李文维,陈凤,张强. 常用金属表面缓蚀自组装膜及其研究方法[J]. 中国腐蚀与防护学报, 2012, 32(4): 273-284.
[8]	汪广进,潘牧. IrO₂复合涂层电极的研究进展[J]. 中国腐蚀与防护学报, 2012, 32(2): 85-89.
[9]	董亮,路民旭,杜艳霞,姜子涛. 埋地管道交流腐蚀的研究进展[J]. 中国腐蚀与防护学报, 2011, 31(3): 173-178.
[10]	曲良山,李晓刚,杜翠薇,李双林. 区域土壤电阻率参数的空间分析软件开发与应用[J]. 中国腐蚀与防护学报, 2011, 31(1): 23-27.
[11]	徐珊,杜楠,赵晴,叶明阳. 激光电子散斑干涉技术监测奥氏体不锈钢在NaCl溶液中的点蚀敏感性[J]. 中国腐蚀与防护学报, 2010, 30(5): 403-409.
[12]	翁永基李维锋李相怡. 电化学噪声方法比较石油用钢的临界点蚀温度[J]. 中国腐蚀与防护学报, 2009, 29(6): 421-425.
[13]	罗宏. SUS304ss包埋粉末渗铝的耐蚀性能[J]. 中国腐蚀与防护学报, 2009, 29(5): 344-348.
[14]	杜艳霞 . 阴极保护电位分布的数值计算[J]. 中国腐蚀与防护学报, 2008, 28(1): 53-58 .
[15]	王春雨 . 铝基复合材料的腐蚀与防护研究现状[J]. 中国腐蚀与防护学报, 2008, 28(1): 59-64 .

Viewed

Full text

Abstract

Cited

Shared

Discussed