PREPARATIVE TECHNICS AND CORROSION RESISTANCE OF COMPLEX COATINGS

西安理工大学

Download:

PDF(1351KB)
Export: BibTeX | EndNote (RIS)

Abstract The feasibility of the electrophoresis on micro-arc magnesium alloy was analyzed, and the electrophoresis technology was optimized and simplified. The complex coatings with different colors were finally developed. The complex coatings were studied by acid-resistant and alkali-resistant tests afterwards, and the result demonstrated that the corrosion resistance of the processing magnesium alloy was greatly improved under acidic and alkaline circumstance. It will surely provide necessary academic and technical backups for magnesium alloy’s extensive application.

Key words:

Received: 29 September 2006

	Service

	E-mail this article
	Add to citation manager
	E-mail Alert
	RSS
	（）
	Articles by authors

Cite this article:

. PREPARATIVE TECHNICS AND CORROSION RESISTANCE OF COMPLEX COATINGS. J Chin Soc Corr Pro, 2008, 28(3): 155-160 .

URL:

https://www.jcscp.org/EN/ OR https://www.jcscp.org/EN/Y2008/V28/I3/155

[1]Zhang D F,Peng J,Ding P D.Resource,appliance and develop-ment of magnesium or magnesium alloy[J].Mater.Leading News-paper,2004,18(4):72(张丁非,彭建,丁培道.镁及镁合金的资源、应用及其发展现状[J].材料导报,2004,18(4):72)
[2]Chen X D,Han W Z.Surface Application Technology[M].Bei-jing:China Machine Press,1993,40-42(陈学定,韩文政.表面涂层技术[M].北京:机械工业出版社,1993,40)
[3]Zhang J S,Liu J.Metal Surface Technology[M].Beijing:China Machine Press,1994,82(张继世,刘江.金属表面工艺[M].北京:机械工业出版社,1994,82)
[4]Zhou Y.New Technology of Electrophoresis[M].Beijing:The Ge-ological Publishing House,2004,45-50(周义.电泳涂装新工艺[M].北京:地质出版社,2004,45-50).
[5]Jiang B L,Zhang S F,Wu G J.Study of corrosion resistance onmicro arc oxidation ceramic coatings on magnesium alloy[J].J.Chin.Soc.Corros.Prot.,2002,22(5):301-302(蒋百灵,张淑芬,吴国建.镁合金微弧氧化陶瓷层耐蚀性的研究[J].中国腐蚀与防护学报,2002,22(5):301-302)
[6]Hu C X,Song Y H.Principle and Application of Coating Technol-ogy[M].Beijing:Chemical Industry Press,2000,12(胡传忻,宋幼慧.涂层技术原理及应用[M].北京:化学工业出版社,2000,12)
[7]Jiang B L,Zhang X F.Study of growing process and corrosion re-sistance on micro arc oxidation ceramic coatings on magnesium al-loy[J].J.Chin.Soc.Corros.Prot.,2005,25(2):99(蒋百灵,张先峰.镁合金微弧氧化陶瓷层的生长过程及其耐蚀性[J].中国腐蚀与防护学报,2005,25(2):99)
[8]Li W M,Song Y S,Deng S Z.Corrosion of Coating Metal[M].Changsha:National University of Defense Technology Press,2003,129(黎完模,宋玉苏,邓淑珍.涂装金属的腐蚀[M].长沙:国防科技大学出版社,2003,129)

[1]	. [J]. 中国腐蚀与防护学报, 0, (): 0-0.
[2]	LI Qing, ZHANG Deping, LI Xiaorong, WANG Wei, SUN Baozhuang, AI Chi. Comparison of Stress Corrosion Behavior of TP110TS and P110 Steel in a Simulated Annular Environment of CO₂ Injection Well[J]. 中国腐蚀与防护学报, 2020, 40(4): 302-308.
[3]	LI Qing, ZHANG Deping, WANG Wei, WU Wei, LU Lin, AI Chi. Evaluation of Actual Corrosion Status of L80 Tubing Steel and Subsequent Electrochemical and SCC Investigation in Lab[J]. 中国腐蚀与防护学报, 2020, 40(4): 317-324.
[4]	ZHU Lixia, JIA Haidong, LUO Jinheng, LI Lifeng, JIN Jian, WU Gang, XU Congmin. Effect of Applied Potential on Stress Corrosion Behavior of X80 Pipeline Steel and Its Weld Joint in a Simulated Liquor of Soil at Lunnan Area of Xinjiang[J]. 中国腐蚀与防护学报, 2020, 40(4): 325-331.
[5]	XIE Dongbai, HONG Hao, WANG Wen, PENG Xiao, DUO Shuwang. Oxidation Behavior of Stainless Steel 1Cr11Ni2W2MoV in a Simulated Kerosene Combustion Environment[J]. 中国腐蚀与防护学报, 2020, 40(4): 358-366.
[6]	WANG Haiwei, CHANG Sen, LUAN Xin'gang, SONG Xuemei, WANG Zhen, LI Yanzhang, CHEN Jianli, ZHANG Jirong, HAN Ming, QIU Dangui. Preparation and Properties of Ceramics Composed of Nano-Al₂O₃ and Polysiloxane-polyborosilicate-TiB₂ Modified Polysilborazane as High Temperature Adhesive for SiC Based Ceramics[J]. 中国腐蚀与防护学报, 2020, 40(4): 367-372.
[7]	. [J]. 中国腐蚀与防护学报, 2009, 29(4): 317-318.
[8]	. [J]. 中国腐蚀与防护学报, 2009, 29(4): 315-315.
[9]	. [J]. 中国腐蚀与防护学报, 2009, 29(4): 316-317.
[10]	Yonghua Shu; Hongli LiU; Jing Fan; Jiping Cui; Chong Xie. CONTAMINATION AND EROSION OF MAGNESIUM FLUORIDE COATING OF DIFFUSIVE REFLECTION FLAKES BY NITROGEN TETRAOXIDE[J]. 中国腐蚀与防护学报, 2005, 25(2): 70-73 .
[11]	Xin Zhou; Huaiyu Yang; Duochang Cai; Changbin Shen; Xiaojie Tao; Dongyun Han. THE CORROSION AND INHIBITION OF MILD STEEL IN MONOETHANOLAMINE SOLUTION ABOUNDED WITH H2S[J]. 中国腐蚀与防护学报, 2005, 25(2): 79-83 .
[12]	. CORROSION PRODUCTION ON ARCHAEOLOGICAL BRONZE SURFACE AND ITS DISTRIBUTION WITH DEPTH[J]. 中国腐蚀与防护学报, 2005, 25(3): 163-166 .
[13]	;. EFFECTS OF DISSOLVED OXYGEN ON THE LOW CYCLE CORROSION FATIGUEBEHAVIOR AND SURFACE FILM OF CARBON STEEL TU48 IN HOT WATER[J]. 中国腐蚀与防护学报, 2005, 25(3): 167-170 .
[14]	Yuanshi Li; Yan Niu; Weitao Wu. CORROSION BEHAVIOR OF PURE Cr AND TWO Cr-CONTAINING ALLOYS BENEATH ZnCl2 AND KCl-ZnCl2 DEPOSITS[J]. 中国腐蚀与防护学报, 2002, 22(1): 27-31 .
[15]	Ying Li; Shujiang Geng; Fuhui Wang. CORROSION RESISTANCE OF NANOCRYSTALLIZEDIN738 COATING IN SALT SOLUTION[J]. 中国腐蚀与防护学报, 2002, 22(6): 349-354 .

No Suggested Reading articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed