Corrosion Behavior of N80 Steel in Simulated Water from deep Gaswell Containing Carbon Dioxide
;;;
大庆油田公司采油工程研究院采气工艺研究室
Download:  PDF(2263KB) 
Export:  BibTeX | EndNote (RIS)      
Abstract  Factors influencing corrosion rate of N80 steel in carbon dioxide environment were studied using autoclave,SEM and XRD.The results indicated that the temperature remarkably affects the characterization of corrosion product,and the corrosion rate increases along with the increasing of temperature up to 80℃,then reduces dramatically due to the formation of a protective layer on the surface of steel.Corrosion product was proved to be FeCO3 in higher temperature.Corrosion will be aggravated by reducing pH value and increasing the Cl- concentration,CO2 partial pressure and the flow velocity of solution.
Key words:  CO2 Corrosion      N80 steel      Corrosion rate      Corrosion products      
Received:  29 May 2006     
ZTFLH:  TG172  
Service
E-mail this article
Add to citation manager
E-mail Alert
RSS
Articles by authors

Cite this article: 

;. Corrosion Behavior of N80 Steel in Simulated Water from deep Gaswell Containing Carbon Dioxide. J Chin Soc Corr Pro, 2007, 27(1): 8-13 .

URL: 

https://www.jcscp.org/EN/     OR     https://www.jcscp.org/EN/Y2007/V27/I1/8

[1]Heuer J K,Stubbins J F.An XPS characterization of FeCO3filmsfrom CO2corrosion[J].Corros.Sci.,1999,41(7):1231-1243
[2]Li J.Study on the corrosion behavior and mechanism of tubular steelin carbon dioxide environment[D].Beijing:USTB Doctor Disserta-tion,2000(李静.油管钢CO2腐蚀行为与机理研究[D].北京:北京科技大学博士学位论文,2000)
[3]Zhao J M,Gu M G,Zuo Y.Influencing factors on corrosion of mildsteel in carbon dioxide environment[J].J.Beijing Univ.Chem.Technol.,2005,32(5):71-74(赵景茂,顾明广,左禹.碳钢在二氧化碳溶液中腐蚀影响因素的研究[J].北京化工大学学报,2005,32(5):71-74)
[4]Li C F,Wang B,Zhang Y.Reseach progress of CO2corrosion in oil/gas field exploitation[J].J.Southwest Petroleum Institute,2004,26(2):42-45(李春福,王斌,张颖等.油气田开发中CO2腐蚀研究进展[J].西南石油学院学报,2004,26(2):42-45)
[5]De Waard.Predictive model for CO2corrosion engineering in wetnatural gas pipelines[J].Corrosion,1991,47(12):977-985
[6]Lopez D A,Perez T,Simison S N.The influence of microstructureand chemical composition carbon and low alloy steels in CO2corro-sion.A state-of-the-art appraisal[J].Mater.Des.,2003,24(8):561-575
[7]Wu S L,Cui Z D,He F,Bai Z Q,Zhu S L,Yang X J.Characteriza-tion of the surface film formed from carbon dioxide corrosion on N80steel[J].Mater.Lett.,2004,58(6):1076-1081
[8]Lin G F,Bai QZ,Zhao X W,Zheng MS,Lu MX.Effect of tempera-ture on scales of carbon dioxide corrosion products[J].Acta PetroleiSin.,2004,25(3):101-105(林冠发,白真权,赵新伟,郑茂盛,路民旭.温度对二氧化碳腐蚀产物膜形貌特征的影响[J].石油学报,2004,25(3):101-105)
[9]Wan L P,Meng Y F,Liang F S.Carbon dioxide corrosion and its in-fluence factors in oil/gas field exploitation[J].Total Corrosion andControl,2003,17(2):14-17(万里平,孟英峰,梁发书.油气田开发中的二氧化碳腐蚀及影响因素[J].全面腐蚀控制,2003,17(2):14-17)
[10]Li Q A,Zhang Q,Wen J B,Bai Z Q.Prediction and prevention ofCO2corrosion of oil tubular goods[J].Corros.Sci..Prot.Technol.,2004,16(6):381-384(李全安,张清,文九巴,白真权.CO2对油气管材的腐蚀规律及预测防护[J].腐蚀科学与防护技术,2004,16(6):381-384)
[11]Mao X,Liu X,Revie R W.Pitting corrosion of pipeline steel in di-lute bicarbonate solution with chloride ions[J].Corrosion,1994,50(9):651-657
[1] JIA Shichao, GAO Jiaqi, GUO Hao, WANG Chao, CHEN Yangyang, LI Qi, TIAN Yimei. Influence of Water Quality on Corrosion of Cast Iron Pipe in Reclaimed Water[J]. 中国腐蚀与防护学报, 2020, 40(6): 569-576.
[2] ZHAO Guoxian,HUANG Jing,XUE Yan. Corrosion Behavior of Materials Used for Surface Gathering and Transportation Pipeline in an Oilfield[J]. 中国腐蚀与防护学报, 2019, 39(6): 557-562.
[3] Yongwei SUN,Yuping ZHONG,Lingshui WANG,Fangxiong FAN,Yatao CHEN. Corrosion Behavior of Low-alloy High Strength Steels in a Simulated Common SO2-containing Atmosphere[J]. 中国腐蚀与防护学报, 2019, 39(3): 274-280.
[4] Li LIU,Sirong YU. Effect of Gd Addition on Corrosion Behavior of AM60 Magnesium Alloy[J]. 中国腐蚀与防护学报, 2019, 39(2): 185-191.
[5] Yang LI, Chengyuan LI, Xu CHEN, Jiaxing YANG, Xintong WANG, Nanxi MING, Zhenze HAN. Gray Relationship Analysis on Corrosion Behavior of Super 13Cr Stainless Steel in Environments of Marine Oil and Gas Field[J]. 中国腐蚀与防护学报, 2018, 38(5): 471-477.
[6] Shuaihao HAN,Hongyu CEN,Zhenyu CHEN,Yubing QIU,Xingpeng GUO. Inhibition Behavior of Imidazoline Inhibitor in Corrosive Medium Containing Crude Oil and High-Pressure CO2[J]. 中国腐蚀与防护学报, 2017, 37(3): 221-226.
[7] Fengxuan SONG,Qizhong ZHAO,Feilong LI,Yuelu REN,Kui HUANG,Xinming ZHANG. Effect of Aging Treatment on Corrosion Rate of 7050 Al-alloy Plate[J]. 中国腐蚀与防护学报, 2017, 37(3): 287-292.
[8] Ming ZHU,Yong YU,Huihui ZHANG. Corrosion Behavior of L245 Steel in Simulated Oilfield Produced Water at Different Temperatures[J]. 中国腐蚀与防护学报, 2017, 37(3): 300-304.
[9] Shuangqing SUN,Qifei ZHENG,Chunling LI,Xiumin WANG,Songqing HU. Effect of Corrosion Products on Long-term Atmospheric Corrosion of Pure Aluminum 8A06[J]. 中国腐蚀与防护学报, 2017, 37(2): 110-116.
[10] Ziyang ZHANG,Shanlin WANG,Hengyu ZHANG,Liming KE. Corrosion Behavior of Joints of Mg-alloy AZ31 Fabricated by Friction Stir Welding[J]. 中国腐蚀与防护学报, 2017, 37(2): 117-125.
[11] Qiang BAI,Yan ZOU,Xiangfeng KONG,Yang GAO,Yan LIU,Sheng DONG. Electrochemical Corrosion Behavior in Seawater of Weld Joints of CCSE40 Steel Prepared by Underwater WetWelding with Austenitic Welding Rod[J]. 中国腐蚀与防护学报, 2016, 36(5): 427-432.
[12] Chunxia WANG,Jingping CHEN,Xiaohong ZHANG,Chengyin WANG. Corrosion Inhibition of Octyl Isoquinolinium Bromide on Q235 Carbon Steel in HCl Solution[J]. 中国腐蚀与防护学报, 2016, 36(3): 245-252.
[13] Chen ZHANG,Jingmao ZHAO. Synergistic Inhibition Effect of Imidazoline Ammonium Salt and Three Anionic Surfactants in CO2-saturatedBrine Solution[J]. 中国腐蚀与防护学报, 2015, 35(6): 496-504.
[14] Yucheng ZHANG,Xinhua JU,Xiaolu PANG,Kewei GAO. Effect of O2 Concentration on Corrosion Rate of Steels in Supercritical CO2[J]. 中国腐蚀与防护学报, 2015, 35(3): 220-226.
[15] ZHAO Tong, ZHAO Jingmao, JIANG Ruijing. Effect of Flow Velocity and Carbon Chain Length on Corrosion Inhibition Performance of Imidazoline Derivates in High Pressure CO2 Environment[J]. 中国腐蚀与防护学报, 2015, 35(2): 163-168.
No Suggested Reading articles found!