IMPROVEMENT OF OXIDATION RESISTANCE OF Ti47Al1Cr2Nb BY APPLYING MnCl2 ON ALLOY SURFACE
Li Xin;;;
中国科学院金属研究所
Download:  PDF(111KB) 
Export:  BibTeX | EndNote (RIS)      
Abstract  The effect of MnCl2 applied on surface of Ti47Al2Cr2Nb quaternary alloy on its isothermal oxidation behavior at 900℃ has been studied.The presence of MnCl2 reduced the oxidation rate of the alloy by a factor of 3,and changed the scale composition from a mixture of TiO2 and Al2O3 to basically pure Al2O3.The reason for the improvement of oxidation resistance of the alloy due to MnCl2 was discussed.At the beginning of oxidation titanium in the alloy reacted with Cl to form substable titanium chloride.which vaporized and left alloy surface.As a result,a layer of compact Al2O3 scale formed on the alloy asuface and prevented the outward diffudion of titanium.
Key words:  TiAl-base alloy      surface applied MnCl2      oxidation      
Received:  18 November 1998     
Corresponding Authors:  Li Xin   

Cite this article: 

Li Xin. IMPROVEMENT OF OXIDATION RESISTANCE OF Ti47Al1Cr2Nb BY APPLYING MnCl2 ON ALLOY SURFACE. J Chin Soc Corr Pro, 1999, 19(5): 311-314 .

URL: 

https://www.jcscp.org/EN/     OR     https://www.jcscp.org/EN/Y1999/V19/I5/311

1 Ogden HR,et al.Trans.AIME,1953 ,19 :267 
2 Taniguchi S. Materials and Corrosion,1997 ,48 :1 
3 熊谷正树,涉江和久,金睦淳.日本金属学会志,1993 ,57 :721 
4 Schmutzler HJ,Zheng N, Quadakkers WJ.Stroosnijder M F.Surface and Coatings Technology,1996,83:212 
5 Mckee D W, Huang SC.Corrosion Science,1992,33(12) :1899 
6 Taniguchi S,Shibata T.Intermetallics,1996 ,4:s85 
7 Doychak J,Smialek JL,Barrett CA.In: Grobstein T,Doychak Jed .,Oxidation of High TemperatureIntermetallics,TMS, Warrendale DA.1988 ,41 
8 Taylor TN,Paffett M T. Mater.Sci.Eng.,1992 ,A153 :584 
9 Kofstad P. High Temperature Corrosion,Elsevier Applied Science,London and New York ,1988 ,504 
10 George Y L. High Temperature Corrosion of Engineering Alloys, ASMInternational Materials Park OH.,1990 ,88 
11 梁英教,车荫昌主编.无机物热力学数据手册,沈阳:东北大学出版社,1996
[1] WEI Zheng, MA Baoji, LI Long, LIU Xiaofeng, LI Hui. Effect of Ultrasonic Rolling Pretreatment on Corrosion Resistance of Micro-arc Oxidation Coating of Mg-alloy[J]. 中国腐蚀与防护学报, 2021, 41(1): 117-124.
[2] LIU Xiao, WANG Hai, ZHU Zhongliang, LI Ruitao, CHEN Zhenyu, FANG Xudong, XU Fanghong, ZHANG Naiqiang. Oxidation Characteristics of Austenitic Heat-resistant Steel HR3C and Sanicro25 in Supercritical Water for Power Station[J]. 中国腐蚀与防护学报, 2020, 40(6): 529-538.
[3] XIE Dongbai, HONG Hao, WANG Wen, PENG Xiao, DUO Shuwang. Oxidation Behavior of Stainless Steel 1Cr11Ni2W2MoV in a Simulated Kerosene Combustion Environment[J]. 中国腐蚀与防护学报, 2020, 40(4): 358-366.
[4] CAO Jingyi, FANG Zhigang, CHEN Jinhui, CHEN Zhixiong, YIN Wenchang, YANG Yange, ZHANG Wei. Preparation and Properties of Micro-arc Oxide Film with Single Dense Layer on Surface of 5083 Aluminum Alloy[J]. 中国腐蚀与防护学报, 2020, 40(3): 251-258.
[5] FANG Xudong, LIU Xiao, XU Fanghong, LI Ruitao, ZHU Zhongliang, ZHANG Naiqiang. Oxidation Behavior in Supercritical Water of Domestic Austenitic Steel C-HRA-5 for Uultra-supercritical Power Stations[J]. 中国腐蚀与防护学报, 2020, 40(3): 266-272.
[6] ZHENG Yanxin, LIU Ying, SONG Qingsong, ZHENG Feng, JIA Yuchuan, HAN Peide. High-temperature Oxidation Behavior and Wear Resistance of Copper-based Composites with Reinforcers of C, ZrSiO4 and Fe[J]. 中国腐蚀与防护学报, 2020, 40(2): 191-198.
[7] XU Xunhu,HE Cuiqun,XIANG Junhuai,WANG Ling,ZHANG Honghua,ZHENG Xiaodong. High Temperature Oxidation Behavior of Co-20Re-25Cr-1Si Alloy in 0.1 MPa Pure Oxygen[J]. 中国腐蚀与防护学报, 2020, 40(1): 75-80.
[8] JIANG Dongxue,FU Ying,ZHANG Junwei,ZHANG Wei,XIN Li,ZHU Shenglong,WANG Fuhui. Preparation and Properties of Alumina Ceramic Film on Ti-alloy Surface[J]. 中国腐蚀与防护学报, 2019, 39(6): 469-476.
[9] XIAO Jintao,CHEN Yan,XING Mingxiu,JU Pengfei,MENG Yingen,WANG Fang. Effect of Process Parameters on Corrosion Resistance of Anodizing Film on 2195 Al-Li Alloy[J]. 中国腐蚀与防护学报, 2019, 39(5): 431-438.
[10] AI Peng,LIU Lixiang,LI Xiaogang,JIANG Wentao. Influence of TiAlSiN Coatings on High Temperature Oxidation Resistance of γ-TiAl Based Alloys[J]. 中国腐蚀与防护学报, 2019, 39(4): 306-312.
[11] Yunhai MA. Effect of Shot Peening on Oxidation Resistance of Super 304H Steel in Supercritical Steam[J]. 中国腐蚀与防护学报, 2019, 39(3): 245-252.
[12] Junjie XIA,Hongzhi NIU,Min LIU,Huazhen CAO,Guoqu ZHENG,Liankui WU. Enhancement of High Temperature Oxidation Resistance of Ti48Al5Nb Alloy via Anodic Anodization in NH4F Containing Ethylene Glycol[J]. 中国腐蚀与防护学报, 2019, 39(2): 96-105.
[13] Dongbai XIE,Youyu ZHOU,Jintao LU,Wen WANG,Shenglong ZHU,Fuhui WANG. Effect of Al/Si Content on Corrosion of Ni-based Alloys in Supercritical Water[J]. 中国腐蚀与防护学报, 2019, 39(1): 68-76.
[14] Ling WANG,Junhuai XIANG,Honghua ZHANG,Songlin QIN. High Temperature Oxidation Behavior of Three Co-20Re-xCr Alloys in 3.04×10-5 Pa Oxygen at 1000 and 1100 ℃[J]. 中国腐蚀与防护学报, 2019, 39(1): 83-88.
[15] Hao CHEN,Qing CHEN,Li XIN,Long SHI,Shenglong ZHU,Fuhui WANG. Preparation and High Temperature Corrosion Behavior of Aluminized Nanocrystalline Coating on DD98M Alloy[J]. 中国腐蚀与防护学报, 2019, 39(1): 59-67.
No Suggested Reading articles found!