FACTORS INFLUENCING PROTECTIVE BEHAVIOR OF RUST-PREVENTING OIL AND THE CORROSION UNDER OIL FILM

Guigang Hang;;

湖南大学材料测试中心

Download:

PDF(148KB)
Export: BibTeX | EndNote (RIS)

Abstract The resistance distribution of oil film was measured using wire beam electrode and its effect on protective or the oil film was examined.Metal corrosion under oil film was also investigated on the basis of the surface composition analysis and its depth distribution obtained by AES.The results showed that the protective behavior of oil film was inhomogeneous,and the corrosion under oil film occured locally.The inhomogeneity and propective behavior of rust-preventing oil could be improved by introducing inhibitors.The thickness of oil film and immersion duration affected the protective behavior of rust-preventing oil.The resistance was consistent with the results of AES.

Key words: rust-preventing oil protective behavior wire beam electrode localized corrosion

Received: 25 July 2005

Corresponding Authors: Guigang Hang

	Service

	E-mail this article
	Add to citation manager
	E-mail Alert
	RSS
	（）
	Articles by authors
	Guigang Hang

Cite this article:

Guigang Hang. FACTORS INFLUENCING PROTECTIVE BEHAVIOR OF RUST-PREVENTING OIL AND THE CORROSION UNDER OIL FILM. J Chin Soc Corr Pro, 1999, 19(3): 179-184 .

URL:

https://www.jcscp.org/EN/ OR https://www.jcscp.org/EN/Y1999/V19/I3/179

1Szauer T, Klenowicz Z, Szklarska-smialowska Z.Corrosion, 1980, 36(7): 400
2张承典,徐乃欣,丁翠红,王志杰.中国腐蚀与防护学报,1991,11(3): 263
3李国希,胡茵,吴翠兰.材料保护,1989,22(4):29
4黄桂芳,吴翠兰,靳九成.材料保护,1996,29(4):9
5蒋汉瀛,钟庆东,舒余德,吴翠兰.中国腐蚀与防护学报,1996,16(4):298
6钟庆东,舒余德,蒋汉瀛.中国腐蚀与防护学报,1997,17(4):281

[1]	JIA Yizheng, ZHAO Mingjun, CHENG Shijing, WANG Baojie, WANG Shuo, SHENG Liyuan, XU Daokui. Corrosion Behavior of Mg-Zn-Y-Nd Alloy in Simulated Body Fluid[J]. 中国腐蚀与防护学报, 2019, 39(6): 463-468.
[2]	Baojie WANG,Jiyu LUAN,Shidong WANG,Daokui XU. Research Progress on Stress Corrosion Cracking Behavior of Magnesium Alloys[J]. 中国腐蚀与防护学报, 2019, 39(2): 89-95.
[3]	Peichang DENG, Quanbing LIU, Ziyun LI, Gui WANG, Jiezhen HU, Xie WANG. Corrosion Behavior of X70 Pipeline Steel in the Tropical Juncture Area of Seawater-Sea Mud[J]. 中国腐蚀与防护学报, 2018, 38(5): 415-423.
[4]	Chao FENG, Bicao PENG, Yi XIE, Jun WANG, Minghuan LI, Tangqing WU, Fucheng YIN. Corrosion Behavior of T91 Steel by Salt Spray with 0.1%NaHSO₃ Solution[J]. 中国腐蚀与防护学报, 2017, 37(6): 583-589.
[5]	Penghui ZHANG, Kun PANG, Kangkang DING, Xiangfeng KONG, Xin PENG. Research Progress of Scanning Vibrating Electrode Technique in Field of Corrosion[J]. 中国腐蚀与防护学报, 2017, 37(4): 315-321.
[6]	Yalin CHEN, Wei ZHANG, Qi WANG, Jia WANG. Debonding Mechanism of Organic Coating with Artificial Defect in Areas Nearby Water-line in 3.5%NaCl Solution by WBE Technique-II[J]. 中国腐蚀与防护学报, 2017, 37(4): 322-328.
[7]	Jiejing CHEN,Hong JU,Can SUN,Xia LI,Yunfei LIU. Application of Electrochemical Testing Technology for Corrosion Under-deposits[J]. 中国腐蚀与防护学报, 2017, 37(3): 207-215.
[8]	Qingli CHENG,Bin TAO,Shuan LIU,Quanzhen LIU,Weihua ZHANG,Songbai TIAN,Liping WANG. Corrosion Behaviour of Q235B Carbon Steel in Sediment Water From Crude Oil[J]. 中国腐蚀与防护学报, 2017, 37(2): 126-134.
[9]	Jian DING,Wei ZHANG,Jia WANG,Yalin CHEN,Pengfei YIN,Bo ZHANG. Evaluation of Water-line Zone Corrosion of an Electrode with Coating in NaCl Solution by WBE Technique-I[J]. 中国腐蚀与防护学报, 2016, 36(5): 463-470.
[10]	Xiao TANG,Chuntao SHI,Guang CAO,Yan LI. Effect of Coastal Soil Environment on Localized Corrosion for Oil and Gas Pipelines[J]. 中国腐蚀与防护学报, 2016, 36(3): 191-196.
[11]	Shuzhen ZHAO,Lining XU,Juanjuan DOU,Wei CHANG,Minxu LU. Influence of Acetic Acid on Top Localized Corrosion of X70 Steel Pipeline in CO₂ Containing Wet Gas[J]. 中国腐蚀与防护学报, 2016, 36(3): 231-237.
[12]	Yalin CHEN,Wei ZHANG,Kuiying DING,Jia WANG,Pengfei YIN,Caichang DONG,Wanguo YANG. Debonding Mechanism of Organic Coating with Man-made Defect in the Area nearby Water-line by WBE Technique[J]. 中国腐蚀与防护学报, 2016, 36(1): 67-72.
[13]	CHEN Yalin, ZHANG Wei, WANG Wei, WANG Jia, WANG Qi, CAI Guangxu. Evaluation of Water-line Area Corrosion for Q235 Steel by WBE Technique[J]. 中国腐蚀与防护学报, 2014, 34(5): 451-458.
[14]	ZHANG Penghui, WANG Yanhua, PENG Xin, LIU Zaijian, ZHOU Yuanyuan, WANG Jia. Study of Corrosion Behavior of Copper Beneath a Droplet by Means of Wire Beam Electrode Technology[J]. 中国腐蚀与防护学报, 2014, 34(5): 459-464.
[15]	LIU Yu,LI Yan. Research Progress of CO₂ Corrosion of Internal Gas Pipeline Steel[J]. 中国腐蚀与防护学报, 2013, 33(1): 1-9.

No Suggested Reading articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed