Abstract Thermal barrier coatings （TBCs） have been increasingly used to extend the durability of aircraft gas turbine engine.This not only increases components lifetime，but also allows higher engine temperatures and there－fore better efficiency.The performance valuation and analysis was reviewed to the mechanics property，oxidation resistance， hot corrosion resistance， erosion resistance， and thermal property of thermal barrier coatings.
|
|
Received: 20 February 2006
|
|
|
[1]Padture N P,Gell M,Jordan E H.Thermal barrier coatings forgas-turbine engine applications[J].Science,2002,296:280-284
[2]Xu H B,Gong S K,Liu F S.Recent development in materialsdesign of thermal barrier coatings for gas turbine[J].Acta Aero-nautica et Astronautica Sinica,2000,21(1):7-12(徐惠彬,宫声凯,刘福顺.航空发动机热障涂层材料体系的研究[J].航空学报,2000,21(1):7-12)
[3]Liu F S,Gong S K,Xu H B.Recent development in thermal bar-rier coatings prepared by EB-PVD[J].Acta Aeronautica et As-tronautica Sinica,2000,21(Supl.):30-34(刘福顺,宫声凯,徐惠彬.大功率EB-PVD陶瓷热障涂层的研究与应用[J].航空学报,2000,21(增刊):30-34)
[4]Li M F,Zhu J C,Xiang X H.et al.Progress in study on ceram-ic/metal high-temperature thermal barrier coatings[J].Mater.Rev.,2000,14(8):19-21(李明伟,朱景川,向兴华等.陶瓷/金属高温热障涂层研究进展[J].材料导报.2000,14(8):19-21)
[5]Zeng Z H,Guo Z,Wu S J.Functionally gradient material and itsdevelopment status and trend[J].Missiles and Space Vehicles,1996,220:60-67(曾昭焕,郭正,巫世杰.梯度功能材料及其研究现状与发展趋势[J].导弹与航天运载技术,1996,220:60-67)
[6]Hu C S,Wang F H,Wu W T.Review of progress in thermal bar-rier coatings[J].Corro.Sci.Prot.Technol.,2000,12(3):160-163(胡传顺,王福会,吴维.热障涂层研究进展[J].腐蚀科学与山文防护技术,2000,12(3):160-163)
[7]Dapkunas S J.Measurement methods and standards for processingand application of thermal barrier coatings[J].J.Thermal SprayTechnol.,1997,6(1):67-76
[8]BerndtCC.Tensileadhesiontestingmethodologyforthermallysprayedcoatings[J].J.Mater.Eng.,1990,12:151-158
[9]Berndt C C,Lin C K.Measurement of adhesion for thermally sprayedmaterials[J].J.Adhes.Sci.Technol.,1993,7:1235-1264
[10]Lhermitte-Sebire I,Colmet R,Naslain R.The adhesion betweenphysically vapour-deposited or chemically vapour-deposited alumi-na and TiC-coated cemented carbides as characterized by Augerelectron spectroscopy and scratch testing[J].Thin Solid Films,1986,138:221-233
[11]Steinmann P A,Tardy Y,Hintermann H E.Adhesion testing bythe scratch test method:The influence of intrinsic and extrinsic pa-rameters on the critical load[J].Thin Solid Films,1987,154:333-349
[12]Burnett P J,Rickerby D S.The relationship between hardnessand scratch adhesion[J].Thin Solid Films,1987,154:403-416
[13]Bull S J.Failure modes in scratch adhesion testing[J].Surf.Coat.Technol.,1991,50:25-32
[14]Jindal P C,Quinto D T,Wolfe G J.Adhesion measurements ofchemically vapor deposited and physically vapor deposited hardcoatings on WC-Co substrates[J].Thin Solid Films.1987,154:361-375
[15]Loubet J L.Boron-carbide coatings-correlation between mechan-ical-properties and LPCVD parameters values[A].In:Proc.16thLeeds-Lyon Symp.[C].On Tribo.,Dowson D,Taylor C M,GodetM,eds.,held at the Inst.Nation.Des Sci.Appl.,Lyon,France,1989,429
[16]Oliver W C,Pharr G M.An improved technique for determininghardness and elastic-modulus using load and displacement sensingindentation experiments[J].J.Mater.Res.,1992,7:1564-1583
[17]Marshall D B,Noma T,Evans A G.A simple method for deter-mining elastic-modulus to hardness ratios using Knoop indentationmeasurements[J].J.Am.Ceram.Soc.,1982,65:C175-176
[18]Fawcett N.A novel method for the measurement of Young's mod-ulus for thick-film resistor material by flexural testing of coatedbeams[J].Mater.Sci.Technol.,1998,9:2023-2026
[19]Chantikul P,Anstis G R,Lawn B R,et al.A critical evaluationof indentation techniques for measuring fracture toughness 2.Strength method[J].J.Am.Ceram.Soc.,1981,64:539-543
[20]Anstis G R,Chantikul P,Lawn B R,et al.A critical evaluationof indentation techniques for measuring fracture toughness 1.Directcrack measurements[J].J.Am.Ceram.Soc.,1981,64:533-538
[21]Shih T T.An evaluation of the chevron V-notched bend bar frac-ture toughness specimen[J].Engingeering Fracture Mechanics,1981,14(4):821-828
[22]Williams D P,Evans A G.A simple method for studying slow crackgrowth[J].J.Test.Eval.,1973,1(4):264-270
[23]Reece M J,Guiu F,Sammur M F R.Cyclic fatigue crack propa-gation in alumina under direct tension compression loading[J].J.Am.Ceram.Soc.,1989,72(2):348-352
[24]Suresh S.Mechanics and micromechanisms of fatigue crack-growthin brittle solids[J].Int.J.Fracture,1990,42(1):41-56
[25]ASTMStandard E399-74:Standard Method ofTest for Plane-StrainFracture Toughness of Metallic Materials[S].American Society ofTesting Materials,1974
[26]Simpson L A.Use of the notched-beam test for evaluation of frac-ture energies of ceramics[J].J.Am.Ceram.Soc.,1974,57:151-154
[27]GB4161-84:Chinese National Standard.Test Method forPlane-strain Fracture Toughness[S].Beijing:Standards Press ofChina,1985(GB4161-84.金属材料平面应变断裂韧度试验方法[S].北京:中国标准出版社,1985)
[28]Li M H,Sun X F,Gong S K,et al.Studies of microstructure andphase of EB-PVD TBCs exposed to elevated temperatures[J].J.Chin.Soc.Corros.Prot.,2002,22(2):105-110(李美女亘,孙晓峰,宫声凯.EB-PVD热障涂层高温氧化过程中的显微结构和相分析[J].中国腐蚀与防护学报,2002,22(2):105-110)
[29]Li M H,Zhang Z Y,Sun X F,et al.Oxidation behavior of sput-tered NiCrAlY coating[J].Surf.Coat.Technol.,2003,165:241-247
[30]Li M H,Zhang Z Y,Sun X F,et al.Oxidation and degradation ofEB-PVD thermal-barrier coatings[J].Oxidation of Metals,2002,58(5/6):499-512
[31]Li M H,Sun X F,Gong S K,et al.Phase transformation andbond coat oxidation behavior of EB-PVD thermal barrier coating[J].Surf.Coat.Technol.,2004,176:209-214
[32]Wu Y N,Wang F H,Huang W,et al.Oxidation behavior ofthermal barrier coatings obtained by detonation spraying[J].Surf.Coat.Technol.,2003,166:189-194
[33]Tolpygo V K,Clarke D R.Morphological evolution of thermal bar-rier coatings induced by cyclic oxidation[J].Surf.Coat.Technol.,2003,163-164:81-86
[34]Zhang D B,Gong S K,Xu H B,et al.Thermal cycling behaviorsof TBC on intermetallic Ni3Al based superalloy[J].Surf.Coat.Technol.,2003,168:78-83
[35]Miller R A,Lissler G W,Jobe J M.A hot dynamic seal rig formeasuring hypersonic engine seal durability and flow performancetechnical[J].NASA Lewis Research Center,1993,3295
[36]Jones R L.Experiences in seeking stabilizers for zirconia havinghot corrosion-resistance and high temperature tetragonal(t')sta-bility[P].NRL/MR/6170-96-7841,1996
[37]Roark R J,Young W C.Formulas for Stress and Strain[M].NewYork:McGraw-Hill Book Company,1982:516
[38]Rhys-Jones T,Toriz F C.Thermal barrier coatings for turbine ap-plications in aero engines[J].High Temperature Technology,1989,7(2):73-81
[39]Tabakoff W.Investigation of coatings at high temperature for usein turbomachinery[J].Surf.Coat.Technol.,1989,39/40:97-115
[40]Hanschuh R F.High temperature erosion of plasma sprayed par-tially stabilized zirconia in a simulated turbine environment[J].NASA,TP2406,Dec.1984
[41]Toriz F C,Thakker A B,Gupta S K.Thermal barrier coatings forjet engines[J].ASME,88-GT-279
[42]Davis A G,Boone D H,Levy AV.Erosion of ceramic thermalbarrier coatings[J].Wear,1986,110(2):101-116
[43]Eaton H E,Novak R C.Particulate erosion of plasma sprayed porousceramic[J].Surf.Coat.Technol.,1987,30:41-50
[44]Nicholls J R,Jaslier Y,Rickerby D S.Erosion and foreign objectdamage of thermal barrier coatings[J].Mater.Sci.Forum,1997,251-254:935-948
[45]Andersson C A,Lau S K,et al.Advanced ceramic coating devel-opment for industrialatility gas turbine applications[A].NASACR-165619,Final Report[C].1982:12
[46]Zhu D,Miller R A,Nagaraj B A,et al.Thermal conductivity ofEB-PVD thermal barrier coatings evaluated by a steady-state laserheat flux technique[J].Surf.Coat.Technol.,2001,138:1-8 |
| No Suggested Reading articles found! |
|
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|
Cited |
|
|
|
|
| |
Shared |
|
|
|
|
| |
Discussed |
|
|
|