Comprehensive Evaluating for Anticorrosive Properties of Heavy-duty Coating SEBF/SLF Applied Typical Aircraft Structures

Qunzhi Chen;Zuodong Sun;Weizhong Lu;;Tiejun Chang;Jing Li

北京航空工程技术研究中心

Download:

PDF(175KB)
Export: BibTeX | EndNote (RIS)

Abstract The accelerated corrosive environment spectrum and the accelerated corrosion test methods were studied for evaluation the local environment corrosion in the typical aircraft structures. The comparative tests for the heavy-duty coating SEBF/SLF and the ordinary coating on the active service aircraft structures were carried out. The results indicated that the anticorrosive properties of the heavy-duty coating SEBF/SLF are much better than the ordinary coating on the active service aircraft structures.

Key words: aircraft structures SEBF/SLF heavy-duty coat corrosion environment spectrum accelerated corrosion te

Received: 31 May 2004

ZTFLH:

TG174.2

Corresponding Authors: Qunzhi Chen E-mail: cqzyang850@sohu.com

	Service

	E-mail this article
	Add to citation manager
	E-mail Alert
	RSS
	（）
	Articles by authors
	Qunzhi Chen
	Zuodong Sun
	Weizhong Lu
	Tiejun Chang
	Jing Li

Cite this article:

Qunzhi Chen; Zuodong Sun; Weizhong Lu; Tiejun Chang; Jing Li. Comprehensive Evaluating for Anticorrosive Properties of Heavy-duty Coating SEBF/SLF Applied Typical Aircraft Structures. J Chin Soc Corr Pro, 2005, 25(6): 365-368 .

URL:

https://www.jcscp.org/EN/ OR https://www.jcscp.org/EN/Y2005/V25/I6/365

[1]Chen Q Z.A technique system research on the calendar life of air-craft structure under corrosive environments[D].Beijing:Beijing U-niv.Aeron.Astron.,1999:10-25(陈群志.腐蚀环境下飞机结构日历寿命技术体系研究[D].北京:北京航空航天大学,1999:10-25)
[2]LI X H.Studies of nano-composite coatings system to be appliedon typical military aircraft structures for corrosion protection[J].Haerbin:Haerbin University of Engineering,2003:11-35(李祥海.纳米复合涂层在军用飞机结构防腐中的应用研究[J].哈尔滨:哈尔滨工程大学,2003:11-35)
[3]Hu F Y,Wang M C,Wen J L.Corrosion and protection of alumini-um alloy applied on aircraft structure serving along the coast[J].Corros.Sci.Prot.Technol.,2003,15(2):97-100(胡芳友,王茂才,温景林.沿海飞机铝合金结构件腐蚀与防腐[J].腐蚀科学与防腐技术,2003,15(2):97-100)
[4]Cao C N.Statistics Analysis on Corrosion Testing Data[M].Bei-jing:Chemical Industry Press,1988:75-88(曹楚南.腐蚀试验数据的统计分析[M].北京:化学工业出版社,1988:75-88)
[5]Chen Q Z,Liu W T,Chen Z W,et al.Current status and key tech-niques of calendar life of aircraft structure under corrosive environ-ment[J].China Safety Science Journal,2000,10(3):43-47(陈群志,陈志伟,刘文王廷等.腐蚀环境下飞机结构日历寿命研究现状与关键技术问题[J].中国安全科学学报,2000,10(3):43-47)

[1]	ZHU Yichen,LIU Guangming,LIU Xin,PEI Feng,TIAN Xu,SHI Chao. Investigation on Interrelation of Field Corrosion Test and Accelerated Corrosion Test of Grounding Materials in Red Soil Environment[J]. 中国腐蚀与防护学报, 2019, 39(6): 550-556.
[2]	WANG Zhenyao,YU Quancheng,CHEN Junjun,WANG Jun,XU Song,HU Botao. Atmospheric Corrosion Behavior of P265GH Steel and Q235 Steel under Dry/Humid/Immersion Alternative Condition[J]. 中国腐蚀与防护学报, 2014, 34(1): 53-58.
[3]	;. Study on Corrosion Behavior on Joint Section of Aircraft Aluminium Alloy Structure[J]. 中国腐蚀与防护学报, 2007, 27(6): 334-337 .
[4]	Zhenyao Wang; Teng Ma; Wei Han; Guocai Yu. Corrosion behaviors of Al alloy LC4 in simulated polluted atmospheric environments[J]. 中国腐蚀与防护学报, 2005, 25(6): 321-326 .
[5]	Zhenyao Wang. INVESTIGATION ON INTERRELATION OF ACCELERATED CORROSION TESTING AND ATMOSPHERIC EXPOSURE OF ZINC[J]. 中国腐蚀与防护学报, 1999, 19(4): 239-244 .

No Suggested Reading articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed