THE EFFECT OF IMPLANTATION Ce+ ON THE OXIDATIONBEHAVIOR OF PRE-OXIDIZED Ni20Cr ALLOY AT 1050℃

Yuhai Qian;Meishuan Li;Yaming Zhang

宝山钢铁股份有限公司技术中心汽研所

Download:

PDF(125KB)
Export: BibTeX | EndNote (RIS)

Abstract The oxidation behavior of Ni20Cr(mass%) and some pr e-oxidized Ni20Cr with the Ce+ implantation is studied.The results indicate th at the effect of the Ce+ implantation after 0.5 and 1 hour pre-oxidation treat ment on the oxidation behavior is similar to the effect of direct implantation,w hich can decrease the oxidation rate and improve the adherence of surface oxide film,but the degree of effect is different.The results are explained accord ing to the current REE mechanism.

Key words: Ni20Cr alloy ion implantation oxidation kinetic high t emperature oxidation

Received: 30 November 2000

ZTFLH:

TG172.82

Corresponding Authors: Yuhai Qian E-mail: yhqian@imr.ac.cn

	Service

	E-mail this article
	Add to citation manager
	E-mail Alert
	RSS
	（）
	Articles by authors
	Yuhai Qian
	Meishuan Li
	Yaming Zhang

Cite this article:

Yuhai Qian; Meishuan Li; Yaming Zhang. THE EFFECT OF IMPLANTATION Ce+ ON THE OXIDATIONBEHAVIOR OF PRE-OXIDIZED Ni20Cr ALLOY AT 1050℃. J Chin Soc Corr Pro, 2002, 22(4): 225-228 .

URL:

https://www.jcscp.org/EN/ OR https://www.jcscp.org/EN/Y2002/V22/I4/225

[1]HouPY ,BrownIG ,StringerJ.Studyoftheeffectofreactive-el ementadditionbyimplantingmetalionsinapreformedoxidelayer[J].NuclearInstrumentsandMethods,1991,B59/60:1345-1349
[2]HorstBeske,WillemQuadakkersJ,HorstHolzbrecher,HansSchus ter,HubertusNickel.SIMSinvestigationsonthegrowthmehanismsofprotectivechromiaandaluminasurfacescales,[J].MikrochimicaActa,1990,11:109-119
[3]PrzybylskiK .TheinfluenceofimplantedyttriumontheoxidationpropertiesofaCo-25Cr-1Alalloy[J].MaterialsScienceandEn gineering,1989,A121:509-517
[4]PrzybylskiK ,Garratt-ReedAJ ,YurekGJ .Grainboundarysegre gationofyttriuminchromiascales[J].J.Electrochem.Soc.,1988,135(2):509-517
[5]CotellCM ,YurekGJ,HusseyRJ ,MitchellDJ ,GrahamMJ .Theinfluenceofimplanted yttriumonthemechanismofgrowthofCr2O3 onCr[J].J.Electrochem.Soc.,1987,134:1871-1872
[6]PrzybylskiK ,YurekGJ .TheinfluenceofimplantedyttriumonthemicrostructureofchromiascalesformedonaCo-45weightpercentCralloy[J].J.Electrochem.Soc.,1988,135(2):517=

[1]	Mengjin Meng; Xiaofeng Sun; Hengrong Guan; Xiaoxia Jiang. HIGH TEMERATURE OXIDATION BEHAVIOR OF (Ni,Pd) Al COATION[J]. 中国腐蚀与防护学报, 2003, 23(1): 13-16 .
[2]	Mingkai Lei; Fujun Yang; Peng Luo; Xiaopeng Zhu. MODELING OF CYCLIC OXIDATION KINETIC FOR HIGH-TEMPERATURE ALLOYS BASED ON BUCKLING SPALLATION OF OXIDE SCALE[J]. 中国腐蚀与防护学报, 2002, 22(2): 65-68 .
[3]	Huiming Jin. IMPROVEMENT OF ADHESION OF THE SCALE FORMED ON Co-40Cr(wt%) ALLOY BY YTTRIUM IMPLANTATION[J]. 中国腐蚀与防护学报, 1999, 19(1): 50-54 .
[4]	Huiming Jin. INFLUENCE OF YTTRIUM IMPLANTATION ON OXIDATION BEHAVIOR OF cO-40cR(WT%)ALLOY[J]. 中国腐蚀与防护学报, 1999, 19(1): 45-49 .
[5]	XIN Li ZHOU Longjiang LI Meishuan LI Tiefan(Corrosion Science Laboratory; Institute of Corrosion and Protection of Metals; Chinese Academy of Sciences). THE INFLUENCE OF Y~+-IMPLANTATION ON OXIDATION OF DIRECTIONALLY SOLIDIFIED ALLOY Ni30Cr[J]. 中国腐蚀与防护学报, 1997, 17(4): 269-275.
[6]	LI Tiefan; YE Changjiang (Cormsion Science Lab.; Institute of Corrosion and Protection of Metals; Chinese Academy of Sciences)(Physics Dept. of Jinan University). AN INVESTIGATION ON INITIAL OXIDATION RATE OF Ni_3Al ALLOY[J]. 中国腐蚀与防护学报, 1996, 16(3): 201-205.

No Suggested Reading articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed