HIGH TEMPERATURE CORROSION BEHAVIOR OF A3 STEELIN V2O5+Na2SO4 SALTS AT 700 ℃

J Chin Soc Corr Pro

2002, Vol. 22

Issue (2): 92-94 DOI:

Research Report

Current Issue | Archive | Adv Search

HIGH TEMPERATURE CORROSION BEHAVIOR OF A3 STEELIN V2O5+Na2SO4 SALTS AT 700 ℃

Xin Ren;Huaiyu Yang;Fuhui Wang;Zhu Zhao;Yawei Shao

中国科学院金属研究所金属腐蚀与防护国家重点实验室

Cite this article:

Xin Ren; Huaiyu Yang; Fuhui Wang; Zhu Zhao; Yawei Shao. HIGH TEMPERATURE CORROSION BEHAVIOR OF A3 STEELIN V2O5+Na2SO4 SALTS AT 700 ℃. J Chin Soc Corr Pro, 2002, 22(2): 92-94 .

Download:

PDF(119KB)
Export: BibTeX | EndNote (RIS)

Abstract High temperature corrosion behavior of A3 ste el was studied in V2O5+Na2SO4 at 700℃.The results indicated that severe corrosion of A3 steel occurred in V2O5+Na2SO4 at 700℃～850℃ and max imal corrosion rate was found in 85 mass% V2O5+15 mass%Na2SO4.The corros ion mechanisms were discussed.

Key words: vanadium corrosion high temperature corrosion mild steel

Received: 03 December 2001

ZTFLH:

TG172.82

	Service

	E-mail this article
	Add to citation manager
	E-mail Alert
	RSS
	（）
	Articles by authors
	Xin Ren
	Huaiyu Yang
	Fuhui Wang
	Zhu Zhao
	Yawei Shao

URL:

https://www.jcscp.org/EN/ OR https://www.jcscp.org/EN/Y2002/V22/I2/92

[1]PaulLD ,SeeleyRR .Oilashcorrosion-areviewofutilityboilerexperience[J].Corrosion,1991,47(2):152
[2]SlunderCJ.Theresidualoilashcorrosionproblem[J].Corrosion,1959,15(11):61
[3]FrederickSH ,EdenTF .Corrosionaspectsofthevanadiumproblemingasturbines[J].Corrosion,1955,11(1):35
[4]SwisherJH ,ShankarnarayanS .Inhibitingvanadium-inducedcor rosion[J].MaterialsPerformance,1994,9:49
[5]CunninghamGW ,BrasunasADeS .Theeffectsofcontaminationbyvanadiumandsodiumcompoundsontheair-corrosionofstainlesssteel[J].Corrosion,1956,12(8):389
[6]TiwariSN ,PrakashS .Magnesiumoxideasinhibitorofhotoilashcorrosion[J].Mater.Sci.Technol.,1998,14:467
[7]FosterWR ,LeipoldMH .Asimplephaseequilibriumapproachtotheproblemofoil-ashcorrosion[J].Corrosion,1956,12(11):23
[8]SidkyPS ,HockingMG .ThehotcorrosionofNi-basedternaryal loysandsuperalloysforapplicationingasturbinesemployingresidualfuels[J].Corros.Sci.,1987,27(5):499
[9]OteroE ,PardoA ,HernaezJ ,etal.ThehotcorrosionofIn-657su peralloyinNa2SO4-V2O5melteutectic[J].Corros.Sci.,1991,32(7):677
[10]ZhaoGT ,ZhaoKQ .AnIntroductiontotheHighTemperatureOxidationofMetals[M ].Beijing:MetallurgyIndustryPress,1989:143(赵公台,赵克清译.金属高温氧化导论[M ].北京:冶金工业出版社,1989:143)
[11]ZhuRZ ,QiHB ,HuangZZ ,etal.Someproblemsinhightemper aturesulfurcorrosionofmetals[J].PetrochemicalCorrosionandProtection,1995,3:48(朱日彰,齐慧滨,黄震中等.金属材料的高温硫腐蚀中的若干问题[J].石油化工腐蚀与防护,1995,3:48)

[1]	LI Rui, YU Lixin, CUI Yu, LIU Rui, MENG Fandi, LIU Li, WANG Fuhui. Corrosion Behavior of Ti60 Alloy in Mixed Salt Spray Environment at 600 ℃[J]. 中国腐蚀与防护学报, 2026, 46(3): 798-806.
[2]	LI Yanyan, LI Shuai, DONG Chao, LI Dongqiang, BAO Zebin, ZHU Shenglong. Corrosion Behavior of Atmospheric Plasma Spray Thermal Barrier Coatings at 900 °C Beneath NaCl Deposits in Oxygen Flow Carrying Water Vapor[J]. 中国腐蚀与防护学报, 2025, 45(5): 1233-1243.
[3]	SHEN Chen, HUANG Jinyang, ZHANG Xingxing, HU Xinyuan, ZHU Ming, LU Jintao. Research Progress of Carbonization-corrosion and Protection of Alloy Steels[J]. 中国腐蚀与防护学报, 2025, 45(3): 589-601.
[4]	ZHAN Fuyuan, LIU Xuanyi, HAUNG Shifu, LIU Shuaiqi, XU Yuanyuan, PAN Xigui, HE Hualin, LIU Guangming. Corrosion Behavior of SA210C Steel Beneath Deposit Film of Mixed Salts Na₂SO₄-NaCl in Air at 600^oC[J]. 中国腐蚀与防护学报, 2024, 44(6): 1656-1662.
[5]	LI Jiancheng, ZHAO Jing, XIE Xin, WANG Jinlong, CHEN Minghui, WANG Fuhui. Preparation of Phosphate Coatings on Ti-alloy and Their Corrosion Behavior Beneath Salt-mixture in Water Vapor Flow at 650^oC[J]. 中国腐蚀与防护学报, 2024, 44(1): 159-166.
[6]	LIU Zhihao, LIU Guangming, HE Sifan, DONG Meng, LI Yu, LI Futian, ZHU Ting. High Temperature Corrosion Behavior of F22 Base Metal and Weld in Simulated Coastal Atmosphere[J]. 中国腐蚀与防护学报, 2023, 43(3): 594-600.
[7]	GUAN Yu, LIU Guangming, ZHANG Minqiang, LIU Huanhuan, LIU Zhihao, GONG Bingbing. High Temperature Corrosion Behavior of Sanicro 25 Steel in High-sulfur Coal Ash/simulated Flue Gas[J]. 中国腐蚀与防护学报, 2022, 42(4): 681-686.
[8]	WANG Minghao, WANG Huan, LIU Rui, MENG Fandi, LIU Li, WANG Fuhui. Research on Image Recognition for NiCrAlY Coating/N5 High-temperature Alloy System Based on Deep Learning Method[J]. 中国腐蚀与防护学报, 2022, 42(4): 583-589.
[9]	LI Rui, CUI Yu, LIU Li, FAN Lei, MENG Fandi, WANG Fuhui. Corrosion Behavior of Ti60 Alloy in Fog of NaCl Solution at 600 ℃[J]. 中国腐蚀与防护学报, 2021, 41(5): 595-601.
[10]	CHEN Tuchun, XIANG Junhuai, JIANG Longfa, XIONG Jian, BAI Lingyun, XU Xunhu, XU Xincheng. High-temperature Corrosion Behavior of Q235 Steel in Oxidizing Atmosphere Containing Chlorine[J]. 中国腐蚀与防护学报, 2021, 41(4): 560-564.
[11]	Mingming ZHANG,Li XIN,Xueyong DING,Shujiang GENG,Shenglong ZHU,Fuhui WANG. Corrosion Resistance of Alternately Multilayered Coating Ti/TiAlN on Ti-alloy Ti-6Al-4V Beneath a Solid NaCl Film in Atmosphere of Water Vapor and Oxygen at 600 ℃[J]. 中国腐蚀与防护学报, 2017, 37(1): 29-35.
[12]	Yan LI,Jintao LU,Zhen YANG,Ming ZHU,Yuefeng GU. Effect of Sulfur Content on Corrosion Behavior of Candidate Alloys Used for 700 ℃ Level A-USC Boiler in Simulated Coal Ash and Flue Gas Environments[J]. 中国腐蚀与防护学报, 2016, 36(5): 505-512.
[13]	HUANG Bensheng,YIN Wenfeng,WANG Xiaohong,SHI Yijun. Corrosion Behavior of Steels Used in Making Crude Oil Distillation Unit in High Temperature Crude Oil Fractions[J]. 中国腐蚀与防护学报, 2013, 33(5): 377-382.
[14]	PAN Taijun, CHEN Degui, ZHANG Ke, HU Jing. HIGH TEMPERATURE CORROSION OF NF616 AND 12CrMoV IN SIMULATED WASTE-GASIFICATION ENVIROMENTS[J]. 中国腐蚀与防护学报, 2011, 31(6): 457-461.
[15]	DONG Zehua, HE Jinbei, GUO Xingpeng,ZHANG Yaoxiang, HAN Jicheng. HIGH TEMPERATURE INTERACTIVE CORROSION OF NAPHTHENIC ACID AND ORGANIC SULPHIDE ON Cr5Mo STEEL IN SYNTHETIC REFINING MIXTURE[J]. 中国腐蚀与防护学报, 2011, 31(3): 219-224.

No Suggested Reading articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed