A STUDY OF GLOW-DISCHARGE IONIZED NICKEL-CHROMIZING WITH AN ARC SOURCE AND THE CORROSION RESSISATNCE OF THE DIFFUSION LAYER OBTAINED BY THIS PROCESS
HE Qi; BIAN Jie; FAN Benhui; PAN Junde (Research Institute of Surface Engineering; Tai Yuan University of Technology)
Download:  PDF(2048KB) 
Export:  BibTeX | EndNote (RIS)      
Abstract  By using the technique of glow-discharge ionized surface alloying with an arc source, nickel-chromizing was conducted on the surface of carbon-steel samples with different carbon-content 0.1 wt%, 0.45 wt% and 0.8 wt%, designated as 10 steel, 45 steel and T8 steel, respectively. The microstructure, the elemental concentration distribution and the phases of the surface layer were studied. The corrosion resistance of the diffusion layer in 0.05 mol/L H2SO4 solution was evaluated. The results indicated that the ndcrostructure of Ni-Cr alloying layer on 10 steel was γ-phase only and on 45 and T8 steels were γ-phase based Cr23C6 and Cr7C3. The corrosion resistance of alloying layer on 10,45 steels was comparable with that of 18-8stainless steel. However, nickel-chromizing did not improve corrosion resistance for T8 steel.
Key words:  Cold cathode arc source      Nickel-chromizing      Corrosion resistance     
Received:  25 August 1996     
Service
E-mail this article
Add to citation manager
E-mail Alert
RSS
Articles by authors

Cite this article: 

HE Qi; BIAN Jie; FAN Benhui; PAN Junde (Research Institute of Surface Engineering; Tai Yuan University of Technology). A STUDY OF GLOW-DISCHARGE IONIZED NICKEL-CHROMIZING WITH AN ARC SOURCE AND THE CORROSION RESSISATNCE OF THE DIFFUSION LAYER OBTAINED BY THIS PROCESS. J Chin Soc Corr Pro, 1996, 16(4): 287-292.

URL: 

https://www.jcscp.org/EN/     OR     https://www.jcscp.org/EN/Y1996/V16/I4/287

1潘俊德等.CNPatent.90103841.51990.62郑维能等.热加工工艺,1992,(6):33李玉清,刘锦岩.高温合金晶界间隙相,北京:冶金工业出版社,1990.3
[1] HAN Yuetong, ZHANG Pengchao, SHI Jiefu, LI Ting, SUN Juncai. Surface Modification of TA1 Bipolar Plate for Proton Exchange Membrane Fuel Cell[J]. 中国腐蚀与防护学报, 2021, 41(1): 125-130.
[2] SHI Kunyu, WU Weijin, ZHANG Yi, WAN Yi, YU Chuanhao. Electrochemical Properties of Nb Coating on TC4 Substrate in Simulated Body Solution[J]. 中国腐蚀与防护学报, 2021, 41(1): 71-79.
[3] BAO Ren, ZHOU Genshu, LI Hongwei. Preparation of High-tin Bronze Corrosion-resistant Coating by Potentiostatic Pulse Electrodeposition[J]. 中国腐蚀与防护学报, 2020, 40(6): 585-591.
[4] LIU Haixia, HUANG Feng, YUAN Wei, HU Qian, LIU Jing. Corrosion Behavior of 690 MPa Grade High Strength Bainite Steel in a Simulated Rural Atmosphere[J]. 中国腐蚀与防护学报, 2020, 40(5): 416-424.
[5] LI Congwei, DU Shuangming, ZENG Zhilin, LIU Eryong, WANG Feihu, MA Fuliang. Effect of Current Density on Microstructure, Wear and Corrosion Resistance of Electrodeposited Ni-Co-B Coating[J]. 中国腐蚀与防护学报, 2020, 40(5): 439-447.
[6] CAO Jingyi, FANG Zhigang, CHEN Jinhui, CHEN Zhixiong, YIN Wenchang, YANG Yange, ZHANG Wei. Preparation and Properties of Micro-arc Oxide Film with Single Dense Layer on Surface of 5083 Aluminum Alloy[J]. 中国腐蚀与防护学报, 2020, 40(3): 251-258.
[7] WANG Le,YI Danqing,LIU Huiqun,JIANG Long,FENG Chun. Effect of Ru on Corrosion Behavior of Ti-6Al-4V Alloy and Its Mechanism[J]. 中国腐蚀与防护学报, 2020, 40(1): 25-30.
[8] SHI Chao,SHAO Yawei,XIONG Yi,LIU Guangming,YU Yuelong,YANG Zhiguang,XU Chuanqin. Influence of Silane Coupling Agent Modified Zinc Phosphate on Anticorrosion Property of Epoxy Coating[J]. 中国腐蚀与防护学报, 2020, 40(1): 38-44.
[9] WU Dongcai,HAN Peide. Effects of Moderate Temperature Aging Treatment on Corrosion Resistance of SAF2304 DuplexStainless Steel[J]. 中国腐蚀与防护学报, 2020, 40(1): 51-56.
[10] YANG Yinchu,FU Xiuqing,LIU Lin,MA Wenke,SHEN Moqi. Electrochemical Corrosion of Ni-P-BN(h)-Al2O3 Composite Coating Deposited by Spray Electrodeposition[J]. 中国腐蚀与防护学报, 2020, 40(1): 57-62.
[11] XIAO Jintao,CHEN Yan,XING Mingxiu,JU Pengfei,MENG Yingen,WANG Fang. Effect of Process Parameters on Corrosion Resistance of Anodizing Film on 2195 Al-Li Alloy[J]. 中国腐蚀与防护学报, 2019, 39(5): 431-438.
[12] SHI Kunyu,ZHANG Jinzhong,ZHANG Yi,WAN Yi. Preparation and Corrosion Resistance of Nb2N Coating on TC4 Ti-alloy[J]. 中国腐蚀与防护学报, 2019, 39(4): 313-318.
[13] SUN Xiaoguang,HAN Xiaohui,ZHANG Xingshuang,ZHANG Zhiyi,LI Gangqing,DONG Chaofang. Corrosion Resistance and Environmentally-friendly Chemical Passivation of Welded Joints for Ultra-low Carbon Austenitic Stainless Steel[J]. 中国腐蚀与防护学报, 2019, 39(4): 345-352.
[14] Duoyun CHENG,Jinbin ZHAO,Bo LIU,Cheng JIANG,Xiaoqian FU,Xuequn CHENG. Corrosion Behavior of High Nickel and Conventional Weathering Steels Exposed to a Harsh Marine Atmospheric Environment at Maldives[J]. 中国腐蚀与防护学报, 2019, 39(1): 29-35.
[15] Delin LAI,Gang KONG,Chunshan CHE. Effect of Sodium Silicate Sealing on Corrosion Resistance of TiO2Conversion Film on Hot-dip Galvanized[J]. 中国腐蚀与防护学报, 2018, 38(6): 607-614.
No Suggested Reading articles found!