CAUSES OF SUPERIOR CORROSION RESISTANCE OF Ni-Fe ELECTRODEPOSITS PRODUCED AT AMBIENT TEMPERATURE

Huang Shukun; Zou Zhenhua; Kuang Shanlin; Xiao Juemin; Wu Lijun(Hunan University)

Download:

PDF(1155KB)
Export: BibTeX | EndNote (RIS)

Abstract Ni-Fe electrodeposits obtained at ambient temperature possess superior corrosion resistance. Its cause was experimentally investigated by means of electronmicroscopy and X-ray distraction analysis. The results showed that both low-iron (5～7Wt%) and high-iron (20～25wt%) alloy deposits were homogeneous nickel-base solid solutiolls. In these deposits lower internal stress, smaller grain size and (100) texture me those obtained in the Watts nickel electrodeposit were obserVed. Besides, a lamellar structure composed of iron-rich and iron-depleted zones alternately made up a galvanic corrosion system which may prevent the underneath steel substrate from corrosion.

Received: 25 February 1995

	Service

	E-mail this article
	Add to citation manager
	E-mail Alert
	RSS
	（）
	Articles by authors

Cite this article:

Huang Shukun; Zou Zhenhua; Kuang Shanlin; Xiao Juemin; Wu Lijun(Hunan University). CAUSES OF SUPERIOR CORROSION RESISTANCE OF Ni-Fe ELECTRODEPOSITS PRODUCED AT AMBIENT TEMPERATURE. J Chin Soc Corr Pro, 1995, 15(1): 64-68.

URL:

https://www.jcscp.org/EN/ OR https://www.jcscp.org/EN/Y1995/V15/I1/64

1邝少林,黄树坤,邹震华．中国技术成果大全,94-99,中国技术成果大全编辑部编,北京:科学技术文献出版社,1992．p392邝少林等．湖南大学学报,1987,14(2):13531975,11:16894AmblardJ,etal．J．AppLElectrochem,1979,9:23351981,17:7196HadleyJ,O'GradyJ．Thans．Inst．Met．Finish,1981,part37屠振密．电镀合金原理与工艺,北京:国防工业出版社,1993,p．92-93

No related articles found!

No Suggested Reading articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed