THE EFFECT OF HYDROGEN ON STRESS CORROSION CRACKING OF α-BRASS

Qiao Line; Xu Rongjie; Liu Hui; Chu Wuyang; Xiao Jimei(University of Science and Technology; Beijing)

Download:

PDF(234KB)
Export: BibTeX | EndNote (RIS)

Abstract Hydrogen could promote stress corrosion cracking (SCC) of a-brass in ammonia solution. For a notched specimen under constant loading, hydrogen shortened the time to SCC fracture particularly upon lower loading. Slow strain rate tensile tests showed that hydrogen reduced both the fracture stress and the time to freture.

Received: 25 February 1995

	Service

	E-mail this article
	Add to citation manager
	E-mail Alert
	RSS
	（）
	Articles by authors

Cite this article:

Qiao Line; Xu Rongjie; Liu Hui; Chu Wuyang; Xiao Jimei(University of Science and Technology; Beijing). THE EFFECT OF HYDROGEN ON STRESS CORROSION CRACKING OF α-BRASS. J Chin Soc Corr Pro, 1995, 15(1): 61-63.

URL:

https://www.jcscp.org/EN/ OR https://www.jcscp.org/EN/Y1995/V15/I1/61

1乔利杰,缨辉俊,褚武扬,肖纪美,郭培新．中国科学A辑,1991,11:12182乔利杰,褚武扬,肖纪美,黄华．中国腐蚀与防护学报,1988,8:1483NohH,FlanaganTB,RansickMHScriptaMetall,1992．26:353

No related articles found!

No Suggested Reading articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed