常温腐蚀对Al-Si涂层循环氧化行为的影响

中国腐蚀与防护学报

2003, Vol. 23

Issue (3): 183-186

研究报告

本期目录 | 过刊浏览

常温腐蚀对Al-Si涂层循环氧化行为的影响

宋复斌;张琦

北京航空航天大学材料科学与工程学院

INFLUENCE OF THE ROOM-TEMPERATURE CORROSION ONTHE CYCLIC OXIDATION BEHAVIOR OF Al-Si COATINGS

Fubin Song;Qi Zhang

北京航空航天大学材料科学与工程学院

全文: PDF(142 KB)

摘要: 研究常温腐蚀对镍基高温合金表面Al-Si防护涂层循环氧化行为的影响.结果表明涂层在常温腐蚀后，涂层表面粗糙化，表层Al含量明显下降.在循环氧化过程中不仅涂层内出现γ′Ni3Al相的时间明显提前，而且涂层表面Al2O3膜更易剥落，从而降低了涂层的抗循环氧化能力，缩短了涂层的寿命.

关键词 ： Al-Si涂层, 常温腐蚀, 循环氧化

Abstract：The cyclic oxidation behavior of Al-Si coatings on the Ni-base superalloy DZ125 has been investigated,which has been corroded by ro om temperature corrosion.The results indicated that the room temperature corrosi on decreased the Al content,and increased the surface roughness of the coating.D uring the subsequent cyclic oxidation,the phase transformation of βNiAl t oγ′Ni3Al and the spallation of Al2O3 scale are accelerated.As a re sult,the oxidation resistance and lifetime of the coating are decreased.

Key words： Al-Si coatings room-temperature corrosion cyclic oxi dation

收稿日期: 2001-11-20

ZTFLH:

TG174

通讯作者: 宋复斌

Corresponding author: Fubin Song

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	宋复斌
	张琦
44.8K

引用本文:

宋复斌; 张琦 . 常温腐蚀对Al-Si涂层循环氧化行为的影响[J]. 中国腐蚀与防护学报, 2003, 23(3): 183-186 .
Fubin Song, Qi Zhang. INFLUENCE OF THE ROOM-TEMPERATURE CORROSION ONTHE CYCLIC OXIDATION BEHAVIOR OF Al-Si COATINGS. J Chin Soc Corr Pro, 2003, 23(3): 183-186 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2003/V23/I3/183

[1]　YangZhonglin,MoLongsheng,CaiYulin,ZhengYunrong.StudyonprotectiveperformanceofAl-Sicoatings[J].J .Chin.Soc.Corros.Prot.,1981,1(4):28-36(杨忠林,莫龙生,蔡玉林,郑运荣.铝—硅涂层防护性能的研究[J].中国腐蚀与防护学报,1981,1(4):28-36)
[2]　CaiYulin,ZhengYunrong,MoLongsheng,YangZhonglin.TheeffectanddistributionofsilioninAl-Sicoatings—studyontheSi-richcarbidebarrier[J].Aer.Mater.,1981,1(1):39-44(蔡玉林,郑运荣,莫龙生,杨忠林.Al-Si涂层中硅的分布及作用—含Si隔层的研究[J].航空材料,1981,1(1):39-44)
[3]　YangZhonglin,YuXiafei.TheinfluenceofsiliondistributiononthehightemperaturecorrosionbehaviorofAl-Sicoatings[J].J .Aer.Mater.,1994,14(2):36-40(杨忠林,余霞飞.硅的分布对铝-硅涂层抗热腐蚀性能的影响[J].航空材料学报,1994,14(2):36-40)
[4]　NesbittJA ,BarrettCA .Predictingtheoxidation-limitedofβ-NiAl[A].ProceedingsoftheFirstInternationalSymposiumonStructuralIntermetallics[C].Pennsylvania.1993,Sep26-30,601-609
[5]　MooreVS ,BrentnallWD ,StetsonAR .Evaluationofcoatingsforcobalt-andnickel-basesuperalloys[J].NASACR -72714.N72-18579,1970
[6]　ZhengYunrong,ZhangDetang.ColorMetallographicInvestigationofSuperalloysandSteels[M ].Beijing:NationalDefenceIndustryPress,1999(郑运荣,张德堂.高温合金与钢的彩色金相研究[M ].北京:国防工业出版社,1999)
[7]　LiuGang,NiuYan,WangWen,WuWeitao.OxidationbehaviorofPt-modifiedaluminidecoatingsonIN738at1100℃[J].J .Chin.Soc.Corros.Prot.,2001,21(1):54-58(刘刚,牛焱,王文,吴维.IN738合金上铂铝涂层的高温氧化[J].中国腐蚀与防护学报,2001,21(1):54-58)
[8]　ChenGuofeng,LouHanyi.Effectofγ′precipitationonoxidefor mationontheNi-3Cr-20AlandNi-10Cr-11Al-8Tinanocrystallinecoatings[J].Corros.Sci.,2000,42:1185-1195

[1]	杨世伟; 刘海涛; 朱玲斌; 娄瑾 . K4104合金渗Al-Si涂层抗高温氧化性能研究[J]. 中国腐蚀与防护学报, 2006, 26(6): 371-375 .
[2]	张重远; 李美恒; 孙晓峰 . 单晶高温合金热障涂层的循环氧化行为[J]. 中国腐蚀与防护学报, 2002, 22(2): 111-114 .
[3]	袁福河; 孙晓峰; 管恒荣 . 钴基高温合金的循环氧化行为研究[J]. 中国腐蚀与防护学报, 2002, 22(2): 115-117 .
[4]	耿树江; 王福会; 朱圣龙 . 溅射纳米晶IN738合金涂层的抗循环氧化行为[J]. 中国腐蚀与防护学报, 2001, 21(6): 334-339 .

Viewed

Full text

Abstract

Cited

Shared

Discussed