聚苯胺在水中的抗菌作用

石南林,刘宝蕴,张彦英,宫骏,孙超

中国科学院金属研究所沈阳 110016

ANTIBACTERIAL ACTIVITY OF POLYANILINE IN WATER

SHI Nanlin, LIU Baoyun, ZHANG Yanying, GONG Jun, SUN Chao

Institute of Metal Reserch, Chinese Academy of Sciences, Shenyang 110016

全文: PDF(757 KB)

摘要: 研究了聚苯胺在水中的抗菌作用及其相应机制。对用掺杂聚苯胺处理后污水的水质分析和研究结果表明，其微生物指标可达到中水水质，但由于掺杂态聚苯胺在水中发生酸溶出效应，造成水体的化学需氧量COD（Chemical oxygen demand）值升高，形成对水的二次污染。当水中菌液浓度为3.0~10² CFU•mL^-1时本征态聚苯胺的抗菌效果达99%，微生物指标达到生活饮用水标准值，同时并不二次污染水体。碘蓝分光光度法分析结果表明，聚苯胺将水中的氧气氧化为活性氧而杀死细菌是聚苯胺在水中抗菌的另一个可能机制。

关键词 ：聚苯胺, 抗菌, 掺杂, 活性氧

Abstract：Antibacterial activity of polyaniline and the mechanism in water was studied in this paper. The results indicated that the microorganism index of treated sewage water for urban by doped polyaniline could reach to the level of reclaimed water. Due to the dissolving out of doping acid the doped polyaniline could raise the COD (chemical oxygen demand) of wate and result in secondary pollution. In comparison, the antibacterial rate of emeraldine base polyaniline could reach up to 99% without contamination. The result of analysis by KI iodine-blue spectrophotometry reveals that the activity of active oxygen created by oxidation of polyaniline may be another antibacterial mechanism during treament of water.

Key words： polyaniline antibacterial doping active oxygen

收稿日期: 2011-01-11

ZTFLH:

TV213.6

基金资助:

国家高技术发展计划项目（2008AA03Z409）资助}

通讯作者: 石南林 E-mail: nlshi@imr.ac.cn.

Corresponding author: SHI Nanlin E-mail: nlshi@imr.ac.cn.

作者简介: 石南林，男，1946年生，研究员，研究方向为导电高分子材料

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	石南林
44.8K

引用本文:

石南林,刘宝蕴,张彦英,宫骏,孙超. 聚苯胺在水中的抗菌作用[J]. 中国腐蚀与防护学报, 2011, 31(5): 385-388.
DAN Na-Lin. ANTIBACTERIAL ACTIVITY OF POLYANILINE IN WATER. J Chin Soc Corr Pro, 2011, 31(5): 385-388.

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2011/V31/I5/385

[1] Heeger A J. Nobel lecture: Semiconducting and metallic polymers: The fourth generation of polymeric materials[J]. Rev. Modern Phys.,2001, 73(3): 681-700

[2] Shimano J Y, MacDiarmid A G. Polyaniline, a dynamic block copolymer: key to attaining its intrinsic conductivity [J]. Synth. Met., 2001, 123(2): 251-262

[3] Janata J, Josowicz M. Conducting polymers in electronic chemical sensors[J]. Nat. Mater., 2003, 2: 19-24

[4] Guo X M, Shi N L. Research progress of micro/nanostructural polyaniline in its preparations and application [J]. J. Funct. Polym., 2004,17(3): 521-526

    (郭雪梅,石南林. 微/纳米结构聚苯胺的制备及应用的新进展 [J]. 功能高分子学报，2004, 17(3): 521 -526)

[5] Li X W, Ju M, Li X X. Application of conducting polyaniline in corrosion protection [J]. Mater.Rev., 2001, 15(3): 42-43

    (李星纬, 居明, 李晓宣. 用于腐蚀与防护的导电聚苯胺研究新进展 [J]. 材料导报, 15(3)，2001: 42-43)

[6] Guo X M. Synthesis,characterization and properties of polyaniline micro/nanofibers and its composite materials [D]. Beijing: Graduate School of Chinese Academy of Sciences, 2005

    (郭雪梅. 聚苯胺微/纳米纤维及其复合材料的制备、表征与性能研究 [D]. 中国科学院研究生院博士学位论文，2005)

[7] Shi N L, Guo X M, Jing H M, et al. An antibacterial material [P]. Chinese Pat., 200510046183.1，2005

    (石南林, 郭雪梅, 敬和民等. 一种抗菌材料 [P]. 中国：200510046183.1，2005)

[8] Shi N L, Guo X M, Jing H M, et al. Antibacterial effect of the conducting polyaniline [J]. J. Mater.Sci. Technol., 2006, 22(3): 289-290

[9] Seshadri D T, Bhat N V. Use of polyaniline as an antimicrobial agent in textiles [J]. Indian J. Fibre Textile Res., 2005, 30(2): 204-206

[10] Liu B Y, Investigation on the preparation and antibacterial property of polyaniline [D]. Beijing:Graduate School of Chinese Academy of Sciences, 2009

     (刘宝蕴.聚苯胺的制备及其抗菌性的研究 [D]. 中国科学院研究生院博士学位论文，2009

[11] Watanabe M, Kohnosu M. Method and device for producing water having sterilizing activity [P]. Japan Pat: 2000210666A, 2000

[12] Zhang Y Y, Lin L, Su B J. Determination of trace H₂O₂ by KI iodine-blue spectrophotometry [J]. Chin. J. Anal. Lab.,2001, 20(4): 41-42

     (章亚彦, 林荔, 苏必桔. 碘化钾碘蓝分光光度法测定微量过氧化氢 [J]. 分析试验室, 2001, 20(4): 41-42)

[1]	陈超,梁艳芬,梁天权,满泉言,罗毅东,张修海,曾建民. 稀土复合掺杂ZrO₂陶瓷涂层抗Na₂SO₄+NaVO₃热腐蚀性能的研究进展[J]. 中国腐蚀与防护学报, 2019, 39(4): 291-298.
[2]	刘东,向红亮,刘春育. 含Ag抗菌双相不锈钢表面腐蚀产物的XPS分析[J]. 中国腐蚀与防护学报, 2018, 38(6): 533-542.
[3]	万起展,陈宁宁,杨培培,钟莲,王燕华,王佳. 聚苯胺/改性石墨复合材料的电化学制备及其防腐蚀性能研究[J]. 中国腐蚀与防护学报, 2017, 37(5): 428-434.
[4]	李小宝,徐利,刘怡宏,廖婷,李明田,崔学军. 酞菁铜二磺酸改性聚苯胺的制备及耐蚀性能[J]. 中国腐蚀与防护学报, 2016, 36(4): 306-312.
[5]	钱超,云虹,张志国,徐群杰. 纳米ZnS增强聚苯胺复合涂层的性能研究[J]. 中国腐蚀与防护学报, 2016, 36(3): 273-280.
[6]	张山,周丽娜,简璐,王煦. 聚苯胺/TiO₂/环氧涂层的制备及耐蚀性研究[J]. 中国腐蚀与防护学报, 2016, 36(1): 59-66.
[7]	吕文静,张颖君,师超,邵亚薇,王艳秋,孟国哲. 水溶性掺杂聚苯胺的制备及其性能研究[J]. 中国腐蚀与防护学报, 2015, 35(6): 519-524.
[8]	潘太军, 汪涛. AZ91镁合金表面合成聚苯胺涂层及其腐蚀性能研究[J]. 中国腐蚀与防护学报, 2014, 34(6): 489-494.
[9]	康先进，范文玉，张彦英，钱余海，严川伟，孙超，宫骏. 聚苯胺长效防腐水性环保涂料的研制及性能研究[J]. 中国腐蚀与防护学报, 2012, 32(5): 393-396.
[10]	张颖君,冯涛,邵亚薇,孟国哲,张涛,王福会. 聚苯胺/环氧涂层对AZ91D镁合金耐蚀性能的影响[J]. 中国腐蚀与防护学报, 2010, 30(4): 283-287.
[11]	刘宏芳黄玲刘涛胡裕龙. 硫酸盐还原菌杀菌剂应用现状及研究进展[J]. 中国腐蚀与防护学报, 2009, 29(2): 154-160.
[12]	李春福王戎牛艳花朱泽华李天雷. 纳米掺杂对Al₂O₃+13%TiO₂等离子喷涂涂层耐蚀性能的影响[J]. 中国腐蚀与防护学报, 2008, 28(6期): 331-336.
[13]	徐国荣; 周光喜; 易清风; 任凤莲 . 铝基体上电沉积聚苯胺膜及其耐蚀性[J]. 中国腐蚀与防护学报, 2008, 28(1): 11-15 .
[14]	井利新 . 本征态聚苯胺的防腐蚀性能[J]. 中国腐蚀与防护学报, 2004, 24(5): 301-305 .

Viewed

Full text

Abstract

Cited

Shared

Discussed