国产镀锌钢在不同水环境中的腐蚀行为：I淡水和盐水

doi:10.11902/1005.4537.2021.003

中国腐蚀与防护学报

2021, Vol. 41

Issue (2): 169-177 DOI: 10.11902/1005.4537.2021.003

研究报告

本期目录 | 过刊浏览

国产镀锌钢在不同水环境中的腐蚀行为：I淡水和盐水

曹京宜¹, 方志刚¹, 李亮¹, 冯亚菲¹, 王兴奇², 寿海明³, 杨延格²(

), 褚广哲¹, 殷文昌¹

^1.中国人民解放军92228部队北京 100072
^2.中国科学院金属研究所师昌绪先进材料创新中心沈阳 110016
^3.中国人民解放军92942部队北京 100161

Corrosion Behavior of Domestic Galvanized Steel in Different Water Environment: Fresh Water and Salt Water

CAO Jingyi¹, FANG Zhigang¹, LI Liang¹, FENG Yafei¹, WANG Xingqi², SHOU Haiming³, YANG Yange²(

), CHU Guangzhe¹, YIN Wenchang¹

^1.Unit 92228, People's Liberation Army, Beijing 100072, China
^2.Shi -changxu Innovation Center for Advanced Materials, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016, China
^3.Unit 92942, People's Liberation Army, Beijing 100161, China

全文: PDF(11099 KB) HTML

摘要:

利用电化学阻抗谱和电化学噪声技术对比研究了国产镀锌钢板在盐水和淡水中的腐蚀行为。结果表明，镀锌钢在两种水溶液中的腐蚀均可分为3个阶段，不同阶段表现出完全不同的电化学特征，镀锌钢在盐水中的腐蚀速率明显高于其在淡水中的腐蚀速率，其在盐水中的腐蚀产物呈棒状或片层状，对基体不具有保护性，而在淡水中的腐蚀产物形态呈规则的球状，对基体具有明显的保护作用。

关键词 ：镀锌钢, 水环境, 电化学阻抗谱, 电化学噪声

Abstract：

Corrosion behavior of domestic galvanized steel in salt water and fresh water was investigated by means of electrochemical impedance spectroscopy and electrochemical noise. The results indicated that corrosion process of galvanized steel can be divided into three different stages both in salt water and fresh water, and distinguished electrochemical characteristic in each stage can be observed. Corrosion rate of the galvanized steel in salt water was obviously higher than that in fresh water. The formed corrosion products are rod-like or lamellar on the surface of galvanized steel after immersion in salt water, but less protectiveness for the substrate. Whereas, the formed corrosion products are compact film composed of sphere-like particulates on the surface of galvanized steel after immersion in fresh water, which can effectively protect the substrate from further corrosion.

Key words： galvanized steel water environment electrochemical impedance spectroscopy electrochemical noise

收稿日期: 2021-01-05

ZTFLH:

TG174

通讯作者: 杨延格 E-mail: ygyang@imr.ac.cn

Corresponding author: YANG Yange E-mail: ygyang@imr.ac.cn

作者简介: 曹京宜，女，1972年生，研究员

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	曹京宜
	方志刚
	李亮
	冯亚菲
	王兴奇
	寿海明
	杨延格
	褚广哲
	殷文昌
44.8K

引用本文:

曹京宜, 方志刚, 李亮, 冯亚菲, 王兴奇, 寿海明, 杨延格, 褚广哲, 殷文昌. 国产镀锌钢在不同水环境中的腐蚀行为：I淡水和盐水[J]. 中国腐蚀与防护学报, 2021, 41(2): 169-177.
Jingyi CAO, Zhigang FANG, Liang LI, Yafei FENG, Xingqi WANG, Haiming SHOU, Yange YANG, Guangzhe CHU, Wenchang YIN. Corrosion Behavior of Domestic Galvanized Steel in Different Water Environment: Fresh Water and Salt Water. Journal of Chinese Society for Corrosion and protection, 2021, 41(2): 169-177.

链接本文:

https://www.jcscp.org/CN/10.11902/1005.4537.2021.003 或 https://www.jcscp.org/CN/Y2021/V41/I2/169

图1 国产热浸镀锌钢板截面显微组织

图2 国产镀锌钢在盐水和淡水中开路电位随浸泡时间的变化

图3 国产镀锌钢在盐水中浸泡不同时间的电化学阻抗谱

图4 国产镀锌钢在淡水中浸泡不同时间的电化学阻抗谱

图5 国产镀锌钢在两种水溶液中浸泡720 h电化学阻抗谱低频模值随时间的变化

图6 国产镀锌钢在盐水中浸泡不同时间的电化学噪声信号

图7 国产镀锌钢在盐水中浸泡不同时间的电流噪声Hilbert-Huang谱

图8 国产镀锌钢在淡水中浸泡不同时间的电化学噪声信号

图9 国产镀锌钢在淡水中浸泡不同时间的电流噪声Hilbert-Huang谱图

图10 镀锌钢在盐水和淡水中浸泡720 h的微观形貌

1	Wang Y B. Investigation on interfacial microstructures and properties of hot-dip galvanizing coating [D]. Xi'an: Northwestern Polytechnical University, 2016
1	王友彬. 热浸镀锌镀层界面结构与性能研究 [D]. 西安: 西北工业大学, 2016
2	Cui Z Y, Li X G, Xiao K, et al. Corrosion behavior of field-exposed zinc in a tropical marine atmosphere [J]. Corrosion, 2014, 70: 731
3	De La Fuente D, Castaño J G, Morcillo M. Long-term atmospheric corrosion of zinc [J]. Corros. Sci., 2007, 49: 1420
4	Meng Y, Liu L J, Zhang D W, et al. Initial formation of corrosion products on pure zinc in saline solution [J]. Bioact. Mater., 2019, 4: 87
5	Chung S C, Lin A S, Chang J R, et al. EXAFS study of atmospheric corrosion products on zinc at the initial stage [J]. Corros. Sci., 2000, 42: 1599
6	Yang H Y, Ding G Q, Huang G Q, et al. Corrosion behavior of galvanized steels in different atmospheric environments [J]. Corros. Prot., 2017, 38: 369
6	杨海洋, 丁国清, 黄桂桥等. 镀锌钢在不同大气环境中的腐蚀行为 [J]. 腐蚀与防护, 2017, 38: 369
7	Zhong X Z, Wang Z Y, Liu Y J, et al. Corrosion behavior of galvanized steel in simulated ocean atmosphere [J]. J. Chin. Soc. Corros. Prot., 2015, 35: 151
7	钟西舟, 王振尧, 刘艳洁等. 镀锌钢在模拟海洋大气环境下的腐蚀行为 [J]. 中国腐蚀与防护学报, 2015, 35: 151
8	Yadav A P, Katayama H, Noda K, et al. Effect of Fe-Zn alloy layer on the corrosion resistance of galvanized steel in chloride containing environments [J]. Corros. Sci., 2007, 49: 3716
9	Wang X D, Gao L Y, Chen X P, et al. Corrosion resistance of domestic galvanized steel sheet [J]. Mater. Prot., 2002, 35(10): 12
9	王向东, 高令远, 陈小平等. 国产镀锌钢板的耐蚀性研究 [J]. 材料保护, 2002, 35(10): 12
10	Granese S L, Rosales B M, Fernandez A. Behavior of Zn in atmospheres containing sulfur dioxide and chloride ions [A]. 11th International Corroion Congress [C]. Florence: International Corrosion Council, 2009
11	Svensson J E, Johansson L G. A Laboratory study of the initial stages of the atmospheric corrosion of zinc in the presence of NaCl; influence of SO₂ and NO₂ [J]. Corros. Sci., 1993, 34: 721
12	Ning L J, Du A L, Xu L K, et al. Corrosion behavior of galvanized steel in NaCl solution [J]. Corros. Sci. Prot. Technol., 2012, 24: 291
12	宁丽君, 杜爱玲, 许立坤等. 镀锌层在NaCl溶液中的腐蚀行为研究 [J]. 腐蚀科学与防护技术, 2012, 24: 291
13	Liu S, Sun H Y, Fan H J, et al. Progress of research on corrosion behavior of galvanized steel [J]. Mater. Prot., 2012, 45(12): 42
13	刘栓, 孙虎元, 范汇吉等. 镀锌钢腐蚀行为的研究进展 [J]. 材料保护, 2012, 45(12): 42
14	Liu S, Sun H Y, Sun L J, et al. Effects of Zn(OH)₂ on corrosion behavior of galvanized steel in seawater [J]. Mater. Eng., 2013, (8): 60
14	刘栓, 孙虎元, 孙立娟等. 海水中Zn(OH)₂对镀锌钢腐蚀行为的影响 [J]. 材料工程, 2013, (8): 60
15	Marder A R. The metallurgy of zinc-coated steel [J]. Prog. Mater. Sci., 2000, 45: 191

[1]	苍雨, 黄毓晖, 翁硕, 轩福贞. 环境变量对核电汽轮机转子钢焊接接头电偶腐蚀性能的影响[J]. 中国腐蚀与防护学报, 2021, 41(3): 318-326.
[2]	曹京宜, 杨延格, 方志刚, 寿海明, 李亮, 冯亚菲, 王兴奇, 褚广哲, 赵伊. 淡水舱涂层在不同水环境中的失效行为研究[J]. 中国腐蚀与防护学报, 2021, 41(2): 209-218.
[3]	曹京宜, 方志刚, 冯亚菲, 李亮, 杨延格, 寿海明, 王兴奇, 臧勃林. 国产镀锌钢在不同水环境中的腐蚀行为：II反渗透水和调质水[J]. 中国腐蚀与防护学报, 2021, 41(2): 178-186.
[4]	胡露露, 赵旭阳, 刘盼, 吴芳芳, 张鉴清, 冷文华, 曹发和. 交流电场与液膜厚度对A6082-T6铝合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(4): 342-350.
[5]	张震, 吴欣强, 谭季波. 电化学噪声原位监测应力腐蚀开裂的研究现状与进展[J]. 中国腐蚀与防护学报, 2020, 40(3): 223-229.
[6]	王霞,任帅飞,张代雄,蒋欢,古月. 豆粕提取物在盐酸中对Q235钢的缓蚀性能[J]. 中国腐蚀与防护学报, 2019, 39(3): 267-273.
[7]	达波,余红发,麻海燕,吴彰钰. 等效电路拟合珊瑚混凝土中钢筋锈蚀行为的电化学阻抗谱研究[J]. 中国腐蚀与防护学报, 2019, 39(3): 260-266.
[8]	达波,余红发,麻海燕,吴彰钰. 阻锈剂的掺入方式对全珊瑚海水混凝土中钢筋锈蚀的影响[J]. 中国腐蚀与防护学报, 2019, 39(2): 152-159.
[9]	邓培昌, 刘泉兵, 李子运, 王贵, 胡杰珍, 王勰. X70管线钢在热带海水-海泥跃变区的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2018, 38(5): 415-423.
[10]	乔越, 朱志平, 杨磊, 刘志峰. 高温状态下锅炉给水氧化还原电位监测与模拟实验研究[J]. 中国腐蚀与防护学报, 2018, 38(5): 487-494.
[11]	邓三喜, 闫小宇, 柴柯, 吴进怡, 史洪微. 假单胞菌对聚硅氧烷树脂清漆涂层分解及防腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2018, 38(4): 326-332.
[12]	曹海娇, 魏英华, 赵洪涛, 吕晨曦, 毛耀宗, 李京. Q345钢预热时间对熔结环氧粉末涂层防护性能的影响II：涂层体系失效行为分析[J]. 中国腐蚀与防护学报, 2018, 38(3): 255-264.
[13]	张杰, 胡秀华, 郑传波, 段继周, 侯保荣. 海洋微藻环境中钙质层对Q235碳钢腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2018, 38(1): 18-25.
[14]	安朋亮, 梁平, 任建民, 史艳华, 刘峰, 陈思瑶. 高氮奥氏体不锈钢点蚀行为的电化学噪声特征[J]. 中国腐蚀与防护学报, 2018, 38(1): 26-32.
[15]	梅朦, 郑红艾, 陈惠达, 张鸣, 张大全. 硫酸盐还原菌对Cu在循环冷却水中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2017, 37(6): 533-539.

Viewed

Full text

Abstract

Cited

Shared

Discussed