湖北鄂州出土青铜器锈蚀状况分析

黄凰¹,秦颍¹,徐劲松²

1. 中国科学技术大学科技史与科技考古系合肥 230026
2. 湖北省鄂州市博物馆鄂州 436001

A RESEARCH ON THE RUSTED RESIDUES OF BRONZE VESSELS EXCAVATED IN EZHOU, HUBEI

HUANG Huang¹，QIN Ying¹，XU Jinsong²

1. Department of the History of Science and Technology and Archaeology, University of Science and Technology of China, Hefei 230026
2. Museum of Ezhou in Hubei Province, Ezhou 436001

全文: PDF(1911 KB)

摘要: 在X射线荧光（XRF）基体合金成分及金相分析的基础上，利用X射线衍射（XRD）对湖北鄂州出土的几件“水坑器”锈蚀产物进行分析。结果表明，
干湿交替的潜水面浮动带的大环境，与潮湿缺氧、透气性差以及SO₄^2-、 Cl^-等络阴离子含量较高的局部埋藏环境造成青铜器严重腐蚀，锈蚀产物成分虽简单但不稳定，未见孔雀石等表生氧化条件下的稳定腐蚀产物。

关键词 ：青铜器, 锈蚀产物, 水坑器, 埋藏环境

Abstract：The research of rusted residues of bronze vessels has been a vital task in archaeology research, and many scholars have already done lots of work on it, but there are seldom special research on rusted residues of southern “water bronze vessels”. This paper analyzed the rusted residues of some “water bronze vessels” from Ezhou, using XRD, XRF and metallographic examination, and their soil surroundings were discussed. The reason why these bronze vessels were seriously rusted while their rusted residues were still simple was revealed. The embedding surroundings of these bronze vessels are moist and anoxic and the soil have a high content of SO₄^2- and Cl^-.

Key words： bronze vessels rusted residues water bronze vessels soil surroundings

收稿日期: 2009-12-08

ZTFLH:

K854.2

基金资助:

中国科学院知识创新工程（KJCX3.SYW.N12）

通讯作者: 秦颍 E-mail: yingqin@ustc.edu.cn

Corresponding author: QIN Ying E-mail: yingqin@ustc.edu.cn

作者简介: 黄凰，女，1986年生，硕士生，研究方向为科技考古

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	黄凰
44.8K

引用本文:

黄凰,秦颍,徐劲松. 湖北鄂州出土青铜器锈蚀状况分析[J]. 中国腐蚀与防护学报, 2011, 31(1): 76-80.
HUANG Huang. A RESEARCH ON THE RUSTED RESIDUES OF BRONZE VESSELS EXCAVATED IN EZHOU, HUBEI. J Chin Soc Corr Pro, 2011, 31(1): 76-80.

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2011/V31/I1/76

[1] Sun S Y, Yao Z H, Wan F B. Metallographical study on ancient bronze drums and artifacts from Vietnam [J]. J. Guilin Inst. Technol., 2005, 25(4):498-505

    (孙淑云, 姚智辉, 万辅彬. 越南铜鼓及相关器物金相分析[J]. 桂林工学院学报, 2005, 25(4)：498-505)

[2] Zhang X M, Yuan S X, Liu Y, et al. Research on the corrosion of bronzes from Zhouyuan Site and Yu State Cemeteries [J]. Sci. Conserv. Archaeol., 1999, 11(2)：7-18(张晓梅，原思训, 刘煜等.周原遗址及渔国墓地出土青铜锈蚀研究 [J]. 文物保护与考古科学，1999, 11(2)：7-18)

[3] Huang W. The research of the soil environment and rusted residues of bronze artifacts at different areas of Shanxi [D]. Xi$^\prime$an: Northwest University, 2006

    (黄薇.陕西不同地区土壤埋藏环境与青铜器锈蚀特征的研究 [D]. 西安: 西北大学, 2006)

[4] Jin P J, Qin Y, Hu Y L, et al. Analysis of rusted residues of bronze artifacts from Jiuliandun tomb Nos. 1 & 2 [J]. Jianghan Archaeol., 2009, (1): 112-119

    (金普军，秦颍，胡雅丽等.九连墩墓地1、2号墓出土青铜器上锈蚀产物分析 [J]. 江汉考古, 2009,(1)：112-119）

[5] Tie F D. The relationship between the characteristic of rusted bronze and the corrosive property of soil [J]. Cult. Relics Cent.China, 1995, (2): 19

    (铁付德.青铜器腐蚀特征与土壤腐蚀性的关系 [J]. 中原文物, 1995, (2)：19)

[6] Fu L Y, Chen Z X, Cai L K, et al. Effect of pH and chloride on corrosion of bronze [J]. Corros. Prot.,2000, 21(7): 294-296

     (傅丽英，陈中兴，蔡兰坤等.溶液pH值与氯离子对青铜腐蚀的影响 [J]. 腐蚀与防护，2000,21(7)：294-296)

[7] Zhu H F, Zhou H. A study of the corrosion on bronze [J]. Electrochemistry, 1999, 5(3): 314-318

    (祝鸿范, 周浩. 青铜器文物腐蚀受损原因的研究 [J]. 电化学，1999，5(3)：314-318)

[8] Lv Q, Cheng D R. Relationship between bronze corrosion and relative humidity in the existence of SO₄^2- [J].Sci. Conserv. Archaeol., 1997, 9(2): 20-23

    (吕庆, 程德润. 在SO₄^2-存在下青铜腐蚀与相对湿度的关系 [J]，文物保护与考古科学, 1997, 9(2)：20-23)

[9] Zhong J R. Study on the conservation of bronzes and influential of powder rust [J]. J. Shanxi Univ. (Nat. Sci. Ed.), 2004, 27(1): 44-47

    (钟家让. 出土青铜器的锈蚀因素及其防护研究 [J].山西大学学报(自然科学版), 2004, 27(1)：44-47)

[10] Zhou H, Zhu H F, Cai L K. Morphology and composition of the rust on bronze artifacts [J]. Sci. Conserv. Archaeol., 2005, 17(3): 22-27

     (周浩，祝鸿范，蔡兰坤.青铜器锈蚀结构组成及形态的比较研究 [J]. 文物保护与考古科学,2005, 17(3)：22-27)

[11] Wang Z W, Yuan S F. Relation between corrosion rate of brass and concentration of chloride ion [J].Mater. Prot., 2004, 37(10): 50-51

     (王志武, 原素芳.黄铜腐蚀速度与Cl^-浓度的关系 [J]. 材料保护, 2004, 37(10):50-51)

[1]	程旭东,孙连方,曹志烽,朱兴吉. 钢筋非均匀锈蚀导致的混凝土保护层锈胀开裂过程分析[J]. 中国腐蚀与防护学报, 2015, 35(3): 257-264.
[2]	吴涛涛, 孟威威, 鲍志荣, 李洋, 潘春旭. 过量CO₂气氛环境下青铜表面生成孔雀石锈蚀产物的模拟研究[J]. 中国腐蚀与防护学报, 2014, 34(1): 82-88.
[3]	晏德付,秦颍,陈茜,黄凰. 青铜器氯化物腐蚀产物的热分析[J]. 中国腐蚀与防护学报, 2012, 32(1): 64-66.
[4]	赵羽习,任海洋. 基于固结试验和接触理论分析的铁锈力学性能[J]. 中国腐蚀与防护学报, 2010, 30(5): 383-390.
[5]	冯丽婷; 刘清; 包祥; 冯绍彬 . 青铜器加速腐蚀的多孔氧电极研究[J]. 中国腐蚀与防护学报, 2006, 26(3): 184-187 .
[6]	张展适; 陈少华; 陈障茹; 刘月妙 . 青铜文物腐蚀过程的模拟研究[J]. 中国腐蚀与防护学报, 2006, 26(2): 94-99 .

Viewed

Full text

Abstract

Cited

Shared

Discussed