含铬高硅铁基合金组织和性能的研究

汪淑英;李具仓;赵爱民

北京科技大学材料学院材料加工工程

Study On The Microstructure And Properties Of Cr-Containing High-Silicon Iron-Based Alloy

;;

北京科技大学材料学院材料加工工程

全文: PDF(331 KB)

摘要: 用中频感应电炉熔炼获得不同Cr含量高Si铁基合金试样。借助光学显微镜、扫描电镜和力学性能检测设备及腐蚀性能检测仪器等手段，分析和研究了含Cr高Si铁基合金的组织、力学性能和耐腐蚀性能。结果表明：含Cr高Si铁基合金的共晶石墨数量少，分散度高，组织细小；当Cr含量>5.2%时，大量的富Cr相在晶界处析出；当Cr加入量为4.5％~6.5%时，其力学性能和耐硝酸腐蚀性能最好，冲击韧性达1.66 J/cm2，腐蚀速率仅为6.3119 g/h·m2；含Cr高Si铁基合金在H2SO4中的腐蚀速率随着Cr含量增加而增加。

关键词 ：含铬高硅铁基合金, 显微组织, 力学性能, 耐蚀

Abstract：The different compositions of Cr-containing high-silicon iron-based alloys are designed which in order to study the mechanical property and the corrosive property of the alloy.the alloys are melted in mediu-frequency induction furnace.Test and research is conducted by using metalloygraphic microscope ,stereoscan and other methods.The results shows that, the mechanical property of the alloy is good when added 4%~5% Cr, at the same time the corrosion rate of the alloy in nitric acid is the lowwest.But the corrosion rate of alloy in the sulfuric acid increasing with the increasing of the percentage composition of Cr.

Key words： Cr-containing high-silicon iron-based alloy microscopic strctrure mechanical property corrosive pro

收稿日期: 2006-04-17

ZTFLH:

TG174.2+2

通讯作者: 李具仓 E-mail: lijucang@163.com

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	汪淑英
	李具仓
	赵爱民
44.8K

引用本文:

汪淑英; 李具仓; 赵爱民 . 含铬高硅铁基合金组织和性能的研究[J]. 中国腐蚀与防护学报, 2007, 27(5): 292-295 .

链接本文:

https://www.jcscp.org/CN/Y2007/V27/I5/292

[1]Tao L H.Casting Manual Cast-iron Division Manual[M].Beijing:Mechanical Industry Press,2000,35-38(陶令恒.铸造手册(铸铁分册)[M].北京:机械工业出版社,2000:35-38)
[2]Qin Z R,Li L S,Guo N.Effect of Cr on microstructure and propertiesof high silicon cast-iron[J].China Petroleum Machinery,1997,25(9):13-14(秦紫瑞,李隆盛,郭宁.铬对高硅铸铁组织与性能的影响[J].石油机械,1997,25(9):13-14)
[3]Qin Z R,Yu J H.Research on the microstructure and propertiesof Cr-containing cast iron with high silicon[J].Shanghai Metals,1995,17(6):23-27(秦紫瑞,余建宏.含铬高硅铸铁的组织与性能的研究[J].上海金属,1995,17(6):23-27)
[4]Qin Z R,Yu J H.Microstructure and properties of high-siliconcast iron STSi15Cu7[J].Sulphuric Acid Ind.,1995,(6):41-44(秦紫瑞,余建宏.STSi15Cu7高硅铸铁的组织与性能研究[J].硫酸工业,1995,(6):41-44)
[5]Li J C,Li Z S,Zhao A M,et al.Study of high silicon cost iron[J].Foundry,2004,53(12):1028-1030(李具仓,李志思,赵爱民等.高硅铸铁的研究[J].铸造,2004,53(12):1028-1030)
[6]Liu DX.Corrosion and Protection ofMaterial[M].Xi′an:NorthwesterwPolytechnical Industry University Press,2006(刘道新.材料的腐蚀与防护[M].西安:西北工业大学出版社,2006)
[7]Cai S Q,Li W S,Luo J L.Structure and properties of passive filmsformed on iron in aqueous environments[J].J.Chin.Soc.Corros.Prot.,2003,23(3):187-192(蔡松崎,李伟善,Luo J L.Fe在水溶液中形成钝化膜的结构和性质[J].中国腐蚀与防护学报,2003,23(3):187￣192)
[8]Faraday M.Experimental Researches in Electricity[M].New York:Dover,1965
[9]Qing J G,Li D,Wang X L,et al.Effects of concentration of sodiumborate on anodizing for magnesium alloy[J].J.Chin.Soc.Corros.Prot.,2005,25(5):275-278(钱建刚,李荻,王学力等.硼酸钠浓度对镁合金阳极化的影响[J].中国腐蚀与防护学报,2005,25(5):275￣278)
[10]Qian Y C.Steel Material Chemical Pickling[M].Beijing:SciencePress,1993(钱映初.钢铁材料化学酸洗[M].北京:科学出版社,1993)WANG Shuying1,LI Jucang1,ZHAO Aimin1,MAO Shuangliang2,WANG Guiqing2,WANG Xiusheng2(1.School of Materials Science and Technology,University of Science and Technology Beijing,Beijing 100083;2.Taiyuan Ganglian Stainless Steel Co.Ld,Taiyuan 030003)

[1]	黄鹏, 高荣杰, 刘文斌, 尹续保. 盐溶液刻蚀-氟化处理制备X65管线钢镀镍超双疏表面及其耐蚀性研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 96-100.
[2]	魏征, 马保吉, 李龙, 刘潇枫, 李慧. 镁合金表面超声滚压预处理对微弧氧化膜耐蚀性能的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 117-124.
[3]	包任, 周根树, 李宏伟. 恒电位脉冲电沉积高锡青铜耐蚀镀层工艺研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 585-591.
[4]	刘海霞, 黄峰, 袁玮, 胡骞, 刘静. 690 MPa级高强贝氏体钢在模拟乡村大气中的腐蚀行为[J]. 中国腐蚀与防护学报, 2020, 40(5): 416-424.
[5]	李聪玮, 杜双明, 曾志琳, 刘二勇, 王飞虎, 马付良. 电流密度对Ni-Co-B镀层微观结构及磨蚀性能的影响[J]. 中国腐蚀与防护学报, 2020, 40(5): 439-447.
[6]	曹京宜, 方志刚, 陈晋辉, 陈志雄, 殷文昌, 杨延格, 张伟. 5083铝合金表面单致密微弧氧化膜的制备及其性能研究[J]. 中国腐蚀与防护学报, 2020, 40(3): 251-258.
[7]	王英君, 刘洪雷, 王国军, 董凯辉, 宋影伟, 倪丁瑞. 新型高强稀土Al-Zn-Mg-Cu-Sc铝合金的阳极氧化及其抗腐蚀性能研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 131-138.
[8]	王乐,易丹青,刘会群,蒋龙,冯春. Ru对Ti-6Al-4V合金腐蚀行为的影响及机理研究[J]. 中国腐蚀与防护学报, 2020, 40(1): 25-30.
[9]	武栋才,韩培德. 中温时效处理对SAF2304双相不锈钢耐蚀性的影响[J]. 中国腐蚀与防护学报, 2020, 40(1): 51-56.
[10]	张天翼,柳伟,范玥铭,李世民,董宝军,BANTHUKUL Wongpat,CHOWWANONTHAPUNYA Thee. 海洋大气环境Cu/Ni协同作用对低合金钢耐蚀性影响[J]. 中国腐蚀与防护学报, 2019, 39(6): 511-518.
[11]	孙晓光,韩晓辉,张星爽,张志毅,李刚卿,董超芳. 超低碳奥氏体不锈钢焊接接头耐腐蚀性及环保型化学钝化工艺研究[J]. 中国腐蚀与防护学报, 2019, 39(4): 345-352.
[12]	程多云,赵晋斌,刘波,姜城,付小倩,程学群. 高镍钢和传统耐候钢在马尔代夫严酷海洋大气环境中的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2019, 39(1): 29-35.
[13]	刘明,程学群,李晓刚,卢天健. 低合金钢筋在水泥萃取液中钝化膜的耐蚀机理研究[J]. 中国腐蚀与防护学报, 2018, 38(6): 558-564.
[14]	蓝秀玲,刘光明,周街胜,刘志雷,彭叔森,李茂东. 有机硅/SiO₂杂化溶胶改性丙烯酸树脂及性能研究[J]. 中国腐蚀与防护学报, 2018, 38(6): 601-606.
[15]	王凯, 易耀勇, 卢清华, 易江龙, 江泽新, 马金军, 张宇. 基于窄间隙焊接的热模拟峰值温度对Q690高强钢腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2018, 38(5): 447-454.

Viewed

Full text

Abstract

Cited

Shared

Discussed