微液滴现象与大气腐蚀——Ⅱ. 微液滴现象的电化学表征

张际标;王燕华;姜应律

广东海洋大学海洋资源与环境监测中心

MICRO-DROPLETS PHENOMENON AND ATMOSPHERIC CORROSION——Ⅱ.Electrochemical characteristics of the micro-droplets phenomenon

;;;

广东海洋大学海洋资源与环境监测中心

全文: PDF(250 KB)

摘要: 用扫描Kelvin探头和电化学极化等手段，研究了微液滴现象与大气腐蚀的电化学过程之间的相关性.扫描Kelvin探头测定主液滴周围的电位分布显示，微液滴只在表面的正电性区域出现；当有微液滴形成时，火山形电位分布的峰高且宽、谷深且窄；同时，峰变宽的速率与微液滴的扩展速率近似相等.电化学极化结果显示，微液滴的成核速率随极化电流的增加而线性加速，促使大气腐蚀过程发生的电位差和相应的腐蚀电流是微液滴形成和发展的推动力.

关键词 ：微液滴现象, 电位分布, 腐蚀电流, 电化学极化

Abstract：Micro-droplets phenomenon has a close relation with the electrochemical process of atmospheric corrosion.A volcano pattern of poten tial distribution with a potential valley in the center of main-droplet and a po tential annular peak in the area covered with micro-droplets was observed by sca nning Kelvin probe.The electrochemical polarization results proved that the spre ading rate of micro-droplets increased linearly with the polarization current,an d the corrosion current established by the potential difference between the cent ral and peripheral area of main-droplet was the true driving force for the forma tion and spreading of micro-droplets.

Key words： micro-droplets phenomenon potential distribution corrosion current electrochemical polarization

收稿日期: 2005-05-18

ZTFLH:

TG172.3

通讯作者: 张际标 E-mail: zhangjb@gdou.edu.cn

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	张际标
	王燕华
	姜应律
44.8K

引用本文:

张际标; 王燕华; 姜应律 . 微液滴现象与大气腐蚀——Ⅱ. 微液滴现象的电化学表征[J]. 中国腐蚀与防护学报, 2006, 26(5): 282-285 .
. MICRO-DROPLETS PHENOMENON AND ATMOSPHERIC CORROSION——Ⅱ.Electrochemical characteristics of the micro-droplets phenomenon. J Chin Soc Corr Pro, 2006, 26(5): 282-285 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2006/V26/I5/282

[1]Evens U R.Trans.by Hua B D.Corrosion and Oxidation of Metals[M].Beijing:Mechanical Industry Press,1976:401-430(Evens U R.华保定译.金属的腐蚀与氧化[M].北京:机械工业出版社,1976:401-430)
[2]Skerry B S,Johnson J B,Wood G C.Corrosion in smoke,hydrocar-bon and SO2polluted atmospheres—Ⅰ.General behavior of iron[J].Corros.Sci.,1988,28(7):657-695
[3]Stratmann M,Streeckel H.On the atmospheric corrosion of metalswhich are covered with thin electrolyte layers[J].Corros.Sci.,1990,30:681-714
[4]Zakipour S,Leygraf C.Quartz crystal microbalance applied to studiesof atmospheric corrosion of metals[J].Br.Corros.J.,1992,27(4):295-298
[5]Neufeld A K,Cole I S,Bond A M,Furman S A.The initiation mech-anism of corrosion of zinc by sodium chloride particle deposition[J].Corros.Sci.,2002,44:555-572
[6]Wang J,Tsuru T.Electrochemical measurements under thin elec-trolyte layer using Kelvin probe reference electrode[J].J.Chin.Soc.Corros.Prot.,1995,15(3):173-179(王佳,水流彻.使用Kelvin探头参比电极技术进行薄液下电化学测量[J].中国腐蚀与防护学报,1995,15(3):173-179)
[7]Wang J.Role of salt particle deposition in the initiation and propaga-tion of atmospheric corrosion[J].J.Chin.Soc.Corros.Prot.,2004,24(3):155-158(王佳.无机盐微粒沉积和大气腐蚀的发生与发展[J].中国腐蚀与防护学报,2004,24(3):155-158)

[1]	秦越强, 左勇, 申淼. FLiNaK-CrF₃/CrF₂氧化还原缓冲熔盐体系对316L不锈钢耐蚀性能的影响[J]. 中国腐蚀与防护学报, 2020, 40(2): 182-190.
[2]	汤雪颖,卢国华,朱志平,柳森,毛大厦. 炉前材料20G在高温水溶液中的电化学行为[J]. 中国腐蚀与防护学报, 2015, 35(4): 365-371.
[3]	许晨岳增国金伟良. 电化学频率调制技术在混凝土钢筋锈蚀中的应用[J]. 中国腐蚀与防护学报, 2013, 33(2): 136-140.
[4]	陈旭;李晓刚;杜翠薇; 梁平. 溶液环境对模拟剥离涂层下X70钢腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2010, 30(1): 35-40.
[5]	冯兴国唐聿明赵旭辉左禹. 混凝土结构中钢筋腐蚀电位与腐蚀电流在液面附近的分布[J]. 中国腐蚀与防护学报, 2009, 29(6): 459-464.
[6]	张际标; 王佳; 王燕华; 姜应律 . 微液滴现象与大气腐蚀—— Ⅲ. 干湿交替下微液滴的扩展行为[J]. 中国腐蚀与防护学报, 2008, 28(3): 151-154 .
[7]	曹圣山; 孙吉星 . 阴极保护设计问题的优化模型[J]. 中国腐蚀与防护学报, 2007, 27(2): 114-118 .
[8]	杜艳霞; 张国忠 . 储罐底板外侧阴极保护电位分布的数值模拟[J]. 中国腐蚀与防护学报, 2006, 26(6): 346-350 .
[9]	王燕华; 王佳; 张际标 . AZ91D镁合金微弧氧化过程中的火花放电现象研究[J]. 中国腐蚀与防护学报, 2006, 26(5): 267-271 .
[10]	张际标; 王燕华; 姜应律; 王佳 . 微液滴现象与大气腐蚀—— Ⅰ. 微液滴的形成与扩展[J]. 中国腐蚀与防护学报, 2006, 26(4): 207-210 .
[11]	王佳 . 气相环境中无机盐微粒沉积金属表面的电位分布[J]. 中国腐蚀与防护学报, 2004, 24(1): 1-5 .
[12]	李正奉; 毛旭辉; 甘复兴 . 阴极保护下缝隙内的电位分布[J]. 中国腐蚀与防护学报, 2000, 20(3): 129-134 .
[13]	郭海丁;高德平;田锡唐. 含纵向焊缝管内部电偶腐蚀电流分布的复变函数解[J]. 中国腐蚀与防护学报, 1998, 18(1): 72-76.
[14]	邱枫;徐乃欣. 用带状牺牲阳极对埋地钢管实施阴极保护时的电位和电流分布[J]. 中国腐蚀与防护学报, 1997, 17(2): 106-110.
[15]	邱枫;徐乃欣. 码头钢管桩阴极保护时的电位分布[J]. 中国腐蚀与防护学报, 1997, 17(1): 12-18.

Viewed

Full text

Abstract

Cited

Shared

Discussed