纳米阻燃母液提高APP/PER/MEL防火涂料耐水性研究

王震宇;韩恩厚;柯伟

中科院金属腐蚀与防护研究所

STUDY OF NANO-CONCENTRATES IMPROVEMENT IN WATER RESISTANCE OF APP/PER/EN COATING

;;

中科院金属腐蚀与防护研究所

全文: PDF(247 KB)

摘要: 用Solsperse17000超分散剂对纳米二氧化硅和纳米氢氧化镁表面进行包覆改性，再加入树脂、助剂等，经球磨和超声波分散制成纳米阻燃母液，并配制出不同纳米母液含量的纳米改性防火涂料.用透射电子显微镜分析(TEM)和红外光谱分析(FT-IR)研究纳米粒子分散状态和稳定机制.用红外光谱分析(FT-IR)、扫描电子显微镜分析(SEM)、浸水失重曲线分析、差热分析(DTA)研究在水介质中纳米改性防火涂料形貌变化、分子结构变化、水介质传输行为和浸水前后防火涂层的热降解行为.结果表明：4%纳米阻燃母液能有效提高APP/PER/MEL防火涂料的耐水性，且不损害它的热降解行为和防火性能.

关键词 ： APP/PER/EN防火涂料, 纳米阻燃母液, 纳米改性

Abstract：Surface of nanometer silicon dioxide and magnesium hydroxide was modified by Sol sperse17000 dispersing agent.Nano-concentrates were gotten by mixing modified na noparticles with resin through ball milling and supersonic wave,then flame retar dant nano-coatings with different content of nano-concentrates were prepared.Dis persion morphology and stability principle of nanoparticles were analyzed by the use of transmittance electron microscopy (TEM) and Fourier transform infrared s pectroscopy(FT-IR).Morphology,molecule structure,water transport behavior and th ermal degradation of the flame retardant coatings were studied by use of SEM,FT- IR,curve of weight loss,DTA.It is indicated that 4% nano-concentrates can enhanc e water resistance and do not harm thermal degradation and flame retardant prope rty.

Key words： APP/PER/EN flame-retardant coating Nano-concentrates Modified flame-retardant nano-coatin water resi

收稿日期: 2004-12-30

ZTFLH:

TG174.46

通讯作者: 王震宇 E-mail: zzyywang@imr.ac.cn

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	王震宇
	韩恩厚
	柯伟
44.8K

引用本文:

王震宇; 韩恩厚; 柯伟 . 纳米阻燃母液提高APP/PER/MEL防火涂料耐水性研究[J]. 中国腐蚀与防护学报, 2006, 26(2): 103-108 .

链接本文:

https://www.jcscp.org/CN/Y2006/V26/I2/103

[1]Wang Y Q.Flame Retardant Material and Application[M].Bejing:Chemical Industry Press,2003:44-91(王永强.阻燃材料及应用技术[M].北京:化学工业出版社,2003:44-91)
[2]Tan W Q.Study of anti-corrosion property of ultra-thin flameretardant coating for steel structure[J].Paint and Coating Indus-try,2004,34:5-8(覃文清.超薄膨胀型钢结构防火涂料防腐性能的研究[J].涂料工业,2004,34:5-8)
[3]Cheng H L,Liu X D,Yang X Y.Problem study of flame retardantcoating for steel structure[J].New Building Materials,2002,8:47-49(程海丽,刘向东,杨秀云.钢结构防火涂料存在问题探讨[J].新型建筑材料,2002,8:47-49)
[4]Li X Y.New development of flame retardants[J].Hebei ChemicalEngineering,1998,4:30-32(李秀瑜.阻燃剂的最新进展[J].河北化工,1998,4:30-32)
[5]Zheng Y P,Wang B.Study of the properties of TiO2/epoxynanocomposite[J].Acta Materiae Compositae Sinica,2002,19(4):11-13(郑亚萍,王波.TiO2/环氧树脂纳米复合材料的研究[J].复合材料学报,2002,19(4):11-13)
[6]Wang H B,Li C Z,Jiang H B.Surface modification of sub-micronantibacterial agent in organic solvent[J].Journal of East China Uni-versity of Science and Technology,2002,28(6):614-617(王焕冰,李春忠,姜海波.亚微米级无机抗菌剂的有机湿法改性[J].华东理工大学学报,2002,28(6):614-617)
[7]Lin J,Siddiiqui Junaid A.Surface modification of inorganic oxideparticles with silane coupling agent and organic dyes[J].Polym.Adv.Technol.,2001,12(5):285-292
[8]Gu F C,Wang L,Zhao Z X,et al.Study of poly(vinyl butyral)/sili-ca nanocomposite materials[J].Acta Materiae Compositae Sinica,2003,20(5):77-81(古凤才,王莉,赵竹暄等.聚乙烯醇缩丁醛/SiO2纳米复合材料的研究[J].复合材料学报,2003,20(5):77-81)
[9]Donald R B,Paul E Burrows,Anter A EI-Azab.Enhancing coat-ing functionality using nanoscience and nanotechnology[J].Progressin Organic Coating,2003,(47):342-356
[10]Hu J M,Zhang J Q,Xie D M,et al.Water transport in organiccoatings-ⅠFickian diffusion[J].J.Chin.Soc.Corros.Prot.,2002,22(5):311-315(胡吉明,张鉴清,谢德明等.水在有机涂层中的传输-ⅠFick扩散过程[J].中国腐蚀与防护学报,2002,22(5):311-315)
[11]Hu J M,Zhang J Q,Xie D M,et al.Water transport in organiccoatings.Ⅱ.A complicated actual trend[J].J.Chin.Soc.Corros.Prot.,2002,22(6):371-374(胡吉明,张鉴清,谢德明等.水在有机涂层中的传输-Ⅱ复杂的实际传输过程[J].中国腐蚀与防护学报,2002,22(6):371-374)
[12]Perez C,Collazo A,Lzquierdo M.Characterization of the barrierproperties of different paint system.PartⅡ.Non-ideal diffusionand water uptake kinetics[J].Progress in Organic Coatings,1999,37:169-174
[13]Parslow G I,Stephenson D J,Strutt J E,et al.Paint layer erosionresistance behavior for use in a multilayer paint erosion indicationtechnique[J].Wear,1997,212:103-109
[14]Duquesne S,Magnet S,Jama C.Intumescent paint:fire protectivecoatings for metallic substrates[J].Surf.Coat.Technol.,2004,108-181:302-307
[15]Ge L M,Dai A P,Li T L.Application of thermal analysis in re-search of anti-fire coatings[J].Journal of Xi′an University of Sci-ence&Technology,2002,22(1):12-14(葛岭梅,代爱萍,李天良.热分析技术在防火涂料中的应用[J].西安科技大学学报,2002,22(1):12-14)
[16]Xiao X Y,Tu W P,Yang Z R.Study on fire resistant mechanismsof intumescent coatings[J].J.South China University of Technol-ogy(Natural Science),1998,26(12):77-81(肖新颜,涂伟萍,杨卓如.膨胀型防火涂料的阻燃机理研究[J].华南理工大学学报(自然科学版),1998,26(12):77-81)

[1]	张尧, 郭晨, 刘妍慧, 郝美娟, 成世明, 程伟丽. 挤压态Mg-2Sn-1Al-1Zn合金在模拟体液中的电化学腐蚀行为[J]. 中国腐蚀与防护学报, 2020, 40(2): 146-150.
[2]	师超,邵亚薇,熊义,刘光明,俞跃龙,杨志广,许传钦. 硅烷偶联剂改性磷酸锌对环氧涂层防腐性能的影响[J]. 中国腐蚀与防护学报, 2020, 40(1): 38-44.
[3]	王贵容,郑宏鹏,蔡华洋,邵亚薇,王艳秋,孟国哲,刘斌. 环氧防腐涂料在模拟海水干湿交替条件下的失效过程[J]. 中国腐蚀与防护学报, 2019, 39(6): 571-580.
[4]	王贵容,邵亚薇,王艳秋,孟国哲,刘斌. 阴极保护电位对破损环氧涂层阴极剥离的影响[J]. 中国腐蚀与防护学报, 2019, 39(3): 235-244.
[5]	王振华, 白杨, 马晓, 邢少华. 钛合金和铜合金管路电偶腐蚀数值仿真[J]. 中国腐蚀与防护学报, 2018, 38(4): 403-408.
[6]	常亮, 师超, 邵亚薇, 王艳秋, 刘斌, 孟国哲. 植酸转化膜对环氧清漆防腐性能的影响[J]. 中国腐蚀与防护学报, 2018, 38(3): 265-273.
[7]	桂琪, 郑大江, 宋光铃. 醇酸清漆保护性的电化学加速评价[J]. 中国腐蚀与防护学报, 2018, 38(3): 274-282.
[8]	刘丽红，闫杰. 氨基磁漆涂层工艺在海洋大气环境下老化行为研究[J]. 中国腐蚀与防护学报, 2012, 32(1): 75-79.
[9]	张伟,王佳,赵增元,刘学庆. 电化学阻抗谱对比研究连续浸泡和干湿循环条件下有机涂层的劣化过程[J]. 中国腐蚀与防护学报, 2011, 31(5): 329-335.
[10]	刘浩宇,梁小峰,邵亚薇,孟国哲,张涛,王福会. 静水压力下Q235钢环氧涂层在3.5%NaCl溶液中的失效过程[J]. 中国腐蚀与防护学报, 2010, 30(5): 374-378.
[11]	田惠文李伟华宗成中侯保荣. 纳米SiO₂改性环氧涂层的防腐性能[J]. 中国腐蚀与防护学报, 2009, 29(5): 365-370.
[12]	陈中华唐英余飞. 一种环保水性抗静电防腐蚀涂料的性能研究[J]. 中国腐蚀与防护学报, 2009, 29(2): 113-118.
[13]	王石青何德良丁庆云徐以兵高娟区永康. 模数对水性硅酸钾富锌涂层电化学行为的影响[J]. 中国腐蚀与防护学报, 2008, 28(6期): 359-362.
[14]	邵亚薇; 李瑛; 王福会; 杜元龙 . Ti纳米粒子对环氧涂层防护性能的影响[J]. 中国腐蚀与防护学报, 2006, 26(2): 115-120 .
[15]	谢德明 . 富锌漆研究进展[J]. 中国腐蚀与防护学报, 2004, 24(5): 314-320 .

Viewed

Full text

Abstract

Cited

Shared

Discussed