AZ91D镁合金的化学镀镍

谷长栋;连建设;李光玉;牛丽媛;江中浩

吉林大学南岭校区汽车材料教育部重点实验室

Electroless Ni-P Plating on the AZ91D Magnesium Alloy

谷长栋 Changdong Gu;;;;

吉林大学南岭校区汽车材料教育部重点实验室

全文: PDF(133 KB)

摘要: 使用硫酸镍作为化学镀镍磷镀液的主盐，直接在AZ91D镁合金基体上化学镀镍.使用扫描电镜和X射线衍射技术分析镀层的表面形貌和组织.化学镀镍磷镀层是致密的，无明显缺陷，其磷含量约为372 mass%.化学镀镍磷镀层的显微硬度值约为660 VHN，化学镀镍的沉积速度为23 μm/h.前处理过程中的酸洗步骤使镁合金基体产生粗糙的表面，从而使镀层和基体之间起到了互锁的作用，增加了镀层的结合力.

关键词 ：化学镀, 镁合金, AZ91D, Ni-P合金

Abstract：Direct electroless Ni-P plating on the AZ91D magnesium alloy from a plating bath containing sulfate nickel was investigated.The morphology and microstructure of the electroless Ni-P coating was studied by using SEM and XRD.The electroless Ni-P coating was compact and no obvious defects.The hardness values of the Ni-P coatings were about 660 VHN and the phosphorus content of this coating was about 3.72 mass%.The deposition rate of the electroless Ni-P alloy was about 23 μm/h.The acid pickle pretreatment on the AZ91D magnesium alloy substrate provides surface pits to act as sites for mechanical interlocki ng to improve adhesion of the coating and the substrate.

Key words： electroless deposition magnesium alloy AZ91D Ni-P alloy

收稿日期: 2004-05-21

ZTFLH:

TQ174.4

通讯作者: 谷长栋 E-mail: changdong_gu@163.com

Corresponding author: 谷长栋 Changdong Gu E-mail: changdong_gu@163.com

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	谷长栋
	连建设
	李光玉
	牛丽媛
	江中浩
44.8K

引用本文:

谷长栋; 连建设; 李光玉; 牛丽媛; 江中浩 . AZ91D镁合金的化学镀镍[J]. 中国腐蚀与防护学报, 2005, 25(5): 271-274 .
谷长栋 Changdong Gu. Electroless Ni-P Plating on the AZ91D Magnesium Alloy. J Chin Soc Corr Pro, 2005, 25(5): 271-274 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2005/V25/I5/271

[1]Froes F H,Ward-Close C M.Processing of light metals for en-hanced performance[J].J.Mater.Process.Technol.,1995,(48):667
[2]Song G L,Atrens A.Corrosion mechanisms of magnesium alloys[J].Adv.Eng.Mater.,1999,(1):11
[3]Gray J E,Luan B.Protective coatings on magnesium and its alloys-a critical review[J].J.Alloy.Compd.,2002,(336):88
[4]Miller R E.Trends in the electroless nickel industry[J].Plat.Surf.Finish.,1987,(74):52
[5]Keen R H.Application and control of electroless nickel processes atNorthwest Airlines[J].Plat.Surf.Finish.,1988,(75):22
[6]Ambat R,Zhou W.Electroless nickel-plating on AZ91D magne-sium alloy:effect of substrate microstructure and plating parameters[J].Surf.Coat.Technol.,2004,(179):124
[7]Shahin G E.Electroless nickel on magnesium alloy automotive parts[J].Automotive Finishing,2001,(Winter):12
[8]Sharma A K,Suresh M R,Bhojraj H,et al.Electroless nickel platingon magnesium alloy[J].Met.Finish.,1998,(96):10
[9]Huo H W,Li Y,Wang F H.Electroless nickel plating AZ91D mag-nesium alloy[J].J.Chin.Soc.Corros.Prot.,2002,22(1):14(霍宏伟,李瑛,王福会.AZ91D镁合金化学镀镍[J].中国腐蚀与防护学报,2002,22(1):14)
[10]Xing Y H,Hu W B,Shen B,Zhao C Z,Ding W J.Initial depositionmechanism of direct electroless nickel plating on magnesium alloy[J].J.Shanghai Jiaotong University,2000,34(12):1638(向阳辉,胡文彬,沈彬,赵昌正,丁文江.镁合金直接化学镀镍的初始沉积机制[J].上海交通大学学报,2000,34(12):1638)
[11]ASTM Standards B733-97.Standard Specification for Auto-catalytic(Electroless)Nickel-Phosphorus Coatings on Metal[S].
[12]Chen B H,Hong L,Ma Y,Ko T M.Effects of surfactants in anelectroless nickel-plating bath on the properties of Ni-P alloy de-posits[J].Ind.Eng.Chem.Res.,2002,(41):2668
[13]Liu X K,Xiang Y H,Hu W B,Ding W J.Adhesion mechanism ofdirect electroless nickel coating magnesium alloys[J].J.Chin.Soc.Corros.Prot.,2002,22(4):235(刘新宽,向阳辉,胡文彬,丁文江.镁合金化学镀镍层的结合机理[J].中国腐蚀与防护学报,2002,22(4):235)

[1]	郑黎, 王美婷, 于宝义. 镁合金表面冷喷涂技术研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 22-28.
[2]	魏征, 马保吉, 李龙, 刘潇枫, 李慧. 镁合金表面超声滚压预处理对微弧氧化膜耐蚀性能的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 117-124.
[3]	于浩冉, 张文丽, 崔中雨. 4种镁合金在Cl^--NH₄⁺-NO₃^-溶液体系中的腐蚀行为差异研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 553-559.
[4]	岳亮亮, 马保吉. 超声表面滚压对AZ31B镁合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 560-568.
[5]	郏义征, 王保杰, 赵明君, 许道奎. 固溶处理制度对挤压态Mg-Zn-Y-Nd镁合金在模拟体液中腐蚀和析氢行为的影响规律研究[J]. 中国腐蚀与防护学报, 2020, 40(4): 351-357.
[6]	孙硕, 杨杰, 钱薪竹, 常人丽. Ni-Cr-P化学镀层的制备与电化学腐蚀行为[J]. 中国腐蚀与防护学报, 2020, 40(3): 273-280.
[7]	张尧, 郭晨, 刘妍慧, 郝美娟, 成世明, 程伟丽. 挤压态Mg-2Sn-1Al-1Zn合金在模拟体液中的电化学腐蚀行为[J]. 中国腐蚀与防护学报, 2020, 40(2): 146-150.
[8]	郏义征, 赵明君, 程世婧, 王保杰, 王硕, 盛立远, 许道奎. 模拟人体体液中镁合金的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2019, 39(6): 463-468.
[9]	欧阳跃军,胡婷,王佳音,谢治辉. 镁合金表面层状双氢氧化物的电化学沉积和表征[J]. 中国腐蚀与防护学报, 2019, 39(5): 453-457.
[10]	王保杰,栾吉瑜,王士栋,许道奎. 镁合金应力腐蚀开裂行为研究进展[J]. 中国腐蚀与防护学报, 2019, 39(2): 89-95.
[11]	刘丽,于思荣. 添加Gd对AM60镁合金耐腐蚀性能的影响[J]. 中国腐蚀与防护学报, 2019, 39(2): 185-191.
[12]	樊志民, 于锦, 宋影伟, 单大勇, 韩恩厚. 镁合金点蚀的研究进展[J]. 中国腐蚀与防护学报, 2018, 38(4): 317-325.
[13]	王志虎, 张菊梅, 白力静, 张国君. AZ91镁合金表面微弧氧化与化学镀铜复合处理层的微观组织与性能[J]. 中国腐蚀与防护学报, 2018, 38(4): 391-396.
[14]	陈琳, 钟福荣, 昝金龙. 复合电解液中AZ31B镁合金的放电特性及电压滞后[J]. 中国腐蚀与防护学报, 2018, 38(2): 197-202.
[15]	崔学军, 平静. 微弧氧化及其在镁合金腐蚀防护领域的研究进展[J]. 中国腐蚀与防护学报, 2018, 38(2): 87-104.

Viewed

Full text

Abstract

Cited

Shared

Discussed