铁器文物在含氯离子水溶液中局部腐蚀闭塞区化学状态的变化

欧阳维真

北京化工大学材料科学与工程学院

Chemical Changes Within Occluded Cell for Localized Corrosion of Iron Artifacts in Chloride Solution

北京化工大学材料科学与工程学院

全文: PDF(124 KB)

摘要: 用模拟闭塞电池恒电流实验研究了铁器文物在3.5%NaCl水溶液中局部腐蚀闭塞区内化学状态的变化。对内试件通入阳极电流后，闭塞区内溶液pH值随通电时间延长和电流密度的增加而下降，pH值与电量的对数成正比。Cl-向闭塞区内电迁移，迁移量和浓集倍数随时间和电流密度的增加而上升，迁移量与电极上通过的电量呈线性关系。

关键词 ：铁器文物, 闭塞电池, 局部腐蚀

Abstract：The changes of chemical state for localized corrosion of iron artifacts in 3.5% NaCl solution were studied within a simulated occluded cell. As anodic currents passed the cell a series of changes took place, the most important ones were pH fall and Cl- migration within the occluded cell. It was found that as anodic currents passing the cell, the pH value fell quickly at the beginning while slowly after it about 5, which was proportional to the logarithm of quantity of passing electricity. Meanwhile the Cl- migrated into occluded cell. The quantity of Cl- migration and enrichment multiples increased with the time of current flowing. As a rule, a linear relationship existed between the amount of Cl- migration and quantity of electricity passing. Consequently, Cl- concentration was a function of pH in occluded cell.

Key words： iron artifacts occluded cell localized corrosion

收稿日期: 2003-06-30

ZTFLH:

TG172.5

通讯作者: 欧阳维真

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	欧阳维真
44.8K

引用本文:

欧阳维真 . 铁器文物在含氯离子水溶液中局部腐蚀闭塞区化学状态的变化[J]. 中国腐蚀与防护学报, 2004, 24(6): 364-367 .

链接本文:

https://www.jcscp.org/CN/Y2004/V24/I6/364

[1]WalkerR .Thecorrosionandpreservationofironantiques[J].J .ChemicalEducation,1982,59(11):943
[2]WangGY ,WangHJ,LiXL ,etal.CorrosionandProtectionofNaturalEnvironmentAtmosphere,SeawaterandSoil[M ].Beijing:ChemicalIndustryPress,1997:130(王光雍,王海江,李兴濂.自然环境的腐蚀与防护大气、海水、土壤[M ].北京:化学工业出版社,1997:130)
[3]TaoH .Astudyofthemechanismofironrelicsofsaltindustry[J].HistoryofSaltIndustry,2000,3:31-37(陶宏.盐业铁质文物锈蚀机理探讨[J].盐业史研究,2000,3:31-37)
[4]TanW ,XuBS ,HanWZ ,etal.Analysisonrustsofcarbonsteelsubjectedto20-30 yearsexposureinsouth-eastcoastalatmo sphere[J].Corros.Sci.Prot.Technol.,2003,15(2):113-116(谭伟,徐滨士,韩文政等.水陆装甲车车体锈层分析[J].腐蚀科学与防护技术,2003,15(2):113-116)
[5]ZuoJinyi,JinZhiqiang,SunR ,etal.AcceleratingeffectandcriticalpHvalueofoccludedcellcorrosionwithinpits,crevices,orstrescorrosioncracks[J].Corros.Sci.,1988,44(8):539-543
[6]WeiBM ,QingYB ,LinK ,etal.TheTheoryandApplicationofMetalCorrosion[M ].Beijing:ChemicalIndustryPress,1984:150(魏宝明,秦有冰,林可等.金属腐蚀理论及应用[M ].北京:化学工业出版社,1984:150)
[7]XuCC ,FuXP ,LiuYP .Chemicalchangeswithinoccludedcorro sioncellofmildsteelinNaClsolution[J].J .Chem.Indust.andEng.,1999,50(4):258-262(许淳淳,傅晓萍,刘幼平.低碳钢在NaCl水溶液中闭塞区化学状态的变化[J].化工学报,1999,50(4):258-262)

[1]	郏义征, 赵明君, 程世婧, 王保杰, 王硕, 盛立远, 许道奎. 模拟人体体液中镁合金的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2019, 39(6): 463-468.
[2]	史伟宁,杨树峰,李京社. 不锈钢中诱发局部腐蚀的贫Cr区研究进展[J]. 中国腐蚀与防护学报, 2019, 39(4): 281-290.
[3]	王保杰,栾吉瑜,王士栋,许道奎. 镁合金应力腐蚀开裂行为研究进展[J]. 中国腐蚀与防护学报, 2019, 39(2): 89-95.
[4]	冯超, 彭碧草, 谢亿, 王军, 李明欢, 吴堂清, 尹付成. 0.1%NaHSO₃盐雾条件下T91钢的腐蚀行为[J]. 中国腐蚀与防护学报, 2017, 37(6): 583-589.
[5]	张彭辉, 逄昆, 丁康康, 孔祥峰, 彭欣. 扫描振动电极技术在腐蚀领域的应用进展[J]. 中国腐蚀与防护学报, 2017, 37(4): 315-321.
[6]	唐晓,时春涛,曹光,李焰. 海岸土壤环境对油气管道局部腐蚀的影响[J]. 中国腐蚀与防护学报, 2016, 36(3): 191-196.
[7]	赵书振,许立宁,窦娟娟,常炜,路民旭. 醋酸对X70管线钢CO₂湿气顶部腐蚀行为影响[J]. 中国腐蚀与防护学报, 2016, 36(3): 231-237.
[8]	刘士强, 王立达, 宗秋凤, 张成, 刘贵昌. 纯Al表面局部孔蚀的电化学噪声特征分析[J]. 中国腐蚀与防护学报, 2014, 34(2): 160-164.
[9]	刘玉,李焰. 天然气管线钢CO₂腐蚀研究进展[J]. 中国腐蚀与防护学报, 2013, 33(1): 1-9.
[10]	朱元良; 郭兴蓬 . 中性介质中碳钢腐蚀沉积膜下局部腐蚀行为[J]. 中国腐蚀与防护学报, 2008, 28(5): 271-276 .
[11]	叶威; 李瑛; 王福会 . 单相和双相不锈钢纳米涂层的电化学腐蚀行为[J]. 中国腐蚀与防护学报, 2008, 28(3): 129-134 .
[12]	许淳淳; 岳丽杰; 欧阳维真 . 碱性溶液中阴极极化对模拟铸铁文物局部腐蚀闭塞区化学和电化学状态的影响[J]. 中国腐蚀与防护学报, 2005, 25(5): 295-298 .
[13]	刘大扬; 魏开金; 李文军 . 南海榆林海域环境因素对钢局部腐蚀的影响[J]. 中国腐蚀与防护学报, 2003, 23(4): 211-216 .
[14]	董泽华; 郭兴蓬; 郑家shen . 16Mn钢局部腐蚀中的电化学噪声特征[J]. 中国腐蚀与防护学报, 2002, 22(5): 290-294 .
[15]	胡钢; 许淳淳; 张新生 . 冷加工对304不锈钢孔蚀敏感性的影响[J]. 中国腐蚀与防护学报, 2002, 22(4): 198-201 .

Viewed

Full text

Abstract

Cited

Shared

Discussed