Al60Mn13Ti25V2金属间化合物的高温氧化行为研究

中国腐蚀与防护学报

2004, Vol. 24

Issue (3): 129-134

研究报告

本期目录 | 过刊浏览

Al60Mn13Ti25V2金属间化合物的高温氧化行为研究

金光熙;乔利杰;高克玮;桥本健纪;褚武扬

北京科技大学材料物理系

Study on High Temperature Oxidation of Al60Mn13Ti25V2 Intermetallic

;;;;

北京科技大学材料物理系

全文: PDF(351 KB)

摘要: 研究了不同热处理后的Al60Mn13Ti25V2合金的高温氧化行为.结果表明：在1000℃下，单纯均匀化热处理合金和热等静压+均匀化热处理的合金均具有良好的恒温氧化性能；而在900℃和1000℃条件下，热等静压+均匀化热处理合金的循环氧化性能明显优于单纯均匀化热处理合金的循环氧化性能.其原因为热等静压处理有助于消除合金内部微孔等缺陷，使合金组织的均匀化得到改善，降低氧化膜的热应力对循环氧化的影响.

关键词 ： Al60Mn13Ti25V2合金, 恒温氧化, 循环氧化

Abstract：Al60Mn13Ti25V2 intermetallic was heat treated by two ways.One was complex treatment of hot isostatic pressing (HIP)at 1200℃ and 173 MPa for 4 hours following homogenization treatment in vacuum furnace (4×10-4Pa)at 1100℃ for 48 hours.The other way was just homogenization treatment with the samecondition.Static and cycle oxidation behavior of the alloys treated by the two ways were studied at 900℃ and 1000℃ respectively.The results showed that oxidation resistance was high for the both treated alloys under the condition of static oxidation.Under the condition of cycle oxidation,ho wever,the oxidation resistance of the HIP treated alloy was much better than that of the single homogenized treatment.The reason was that the HIP decreased porosity and Mn-rich region.

Key words： Al60Mn13Ti25V2 intermetallic isothermal cyclic oxidation

收稿日期: 2003-06-30

ZTFLH:

TG146.2

通讯作者: 金光熙 E-mail: jgx1964@163.com

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	金光熙
	乔利杰
	高克玮
	桥本健纪
	褚武扬
44.8K

引用本文:

金光熙; 乔利杰; 高克玮; 桥本健纪 ; 褚武扬 . Al60Mn13Ti25V2金属间化合物的高温氧化行为研究[J]. 中国腐蚀与防护学报, 2004, 24(3): 129-134 .

链接本文:

https://www.jcscp.org/CN/Y2004/V24/I3/129

[1]MabuchiH .MicrostructureandmechanicalpropertiesofternaryL12intermetalliccompoundinAl-Ti-Crsystem[J].Mater.Trans.JIM ,1997,38(6):560
[2]ChenSP .OxidationbehaviorofAl3Ti-basedL12 typeintermetallicalloys[J].Scr.Metall.Mater.,1992,27:455
[3]ParfittLJ .OxidationbehaviorofcubicphasesformedbyalloyingAl3TiwithCrandMn[J].Scr.Metall.Mater.,1991,25:727
[4]YoshiokaT .BehaviorofhightemperatureoxidationofTi(Al,X)3(X =Mn,Cr,Ag,Cu)anddiffusionofTiAl/Ti(Al,X)3joints[J].J .JapanInst.Metals,2000,64:1317
[5]HashimotoK .ImprovementofthermalandmechanicalpropertiesofL12 typetitaniumtrialuminide[A].NRIMResearchActivities[C].Japan:NationalResearchInstituteforMetals,2000,30
[6]YamamotoY .L12 singlephaseregioninAl-Tibaseternaryandquaternarysystemsat1450K [J].J.JapanInst.Metals,1999,63:1317
[7]DeadmoreDL .LowellCE .Theeffect△T(oxidizingtemperatureminuscoolingtemperature)onoxidespallation[J].Oxid.Met.,1977,11:91

[1]	徐勋虎,何翠群,向军淮,王玲,张洪华,郑晓冬. Co-20Re-25Cr-1Si合金在0.1 MPa纯O₂中的高温氧化行为[J]. 中国腐蚀与防护学报, 2020, 40(1): 75-80.
[2]	王玲,向军淮,张洪华,覃宋林. 3种不同Cr含量Co-20Re-Cr合金在1000和1100 ℃的高温氧化行为[J]. 中国腐蚀与防护学报, 2019, 39(1): 83-88.
[3]	陈浩,陈庆,辛丽,时龙,朱圣龙,王福会. DD98M纳米晶AlSi渗层制备及抗高温腐蚀性能研究[J]. 中国腐蚀与防护学报, 2019, 39(1): 59-67.
[4]	肖斌,向军淮,张洪华. 四元Fe-Cu-Ni-Al合金900 ℃下的恒温及循环氧化行为[J]. 中国腐蚀与防护学报, 2017, 37(1): 69-73.
[5]	陈倩,辛丽,滕英元,朱圣龙,王福会. 氮化物涂层对钛合金抗循环氧化性能的影响[J]. 中国腐蚀与防护学报, 2012, 32(1): 7-12.
[6]	张泽海,孟杰. 一种镍基单晶高温合金的恒温氧化行为[J]. 中国腐蚀与防护学报, 2010, 30(4): 337-340.
[7]	宋复斌; 张琦 . 常温腐蚀对Al-Si涂层循环氧化行为的影响[J]. 中国腐蚀与防护学报, 2003, 23(3): 183-186 .
[8]	张重远; 李美恒; 孙晓峰 . 单晶高温合金热障涂层的循环氧化行为[J]. 中国腐蚀与防护学报, 2002, 22(2): 111-114 .
[9]	袁福河; 孙晓峰; 管恒荣 . 钴基高温合金的循环氧化行为研究[J]. 中国腐蚀与防护学报, 2002, 22(2): 115-117 .
[10]	耿树江; 王福会; 朱圣龙 . 溅射纳米晶IN738合金涂层的抗循环氧化行为[J]. 中国腐蚀与防护学报, 2001, 21(6): 334-339 .
[11]	胡武生;李铁藩;沈嘉年. 几种Ni-Cr-Al墓低偏析高温合金的抗氧化性能研究[J]. 中国腐蚀与防护学报, 1996, 16(4): 293-297.

Viewed

Full text

Abstract

Cited

Shared

Discussed