NaCl在A3钢大气腐蚀中的作用

屈庆;严川伟;白玮

云南大学

ROLE OF NaCl IN THE ATMOSPHERIC CORROSION OF A3 STEEL

Qing Qv;Chuanwei Yan;Wei Bai

云南大学

全文: PDF(147 KB)

摘要: 研究了温度为25℃、相对湿度为80%时NaCl对A3钢大气腐蚀的影响.结果表明，A3钢腐蚀失重随NaCl沉积量的增加而增加，同时随暴露时间的延长也呈增加趋势；但暴露一定时间后，腐蚀失重增加趋缓.采用扫描电镜(SEM/EDAX)及光电子能谱( XPS)对腐蚀形貌及产物成分进行了分析，腐蚀表面呈现不均匀的凹凸形貌，腐蚀产物上有细微裂缝.探讨了该条件下A3钢的大气腐蚀过程.

关键词 ： A3钢, NaCl沉积, 大气腐蚀

Abstract：The effect of NaCl deposition on the atmospheric co rrosion of A3 steel at 25℃ and 80%RH was investigated.The results showed that w eight loss increased with the amount of NaCl deposition,but it did not change ob viously in the presence of more amount of NaCl deposition after exposure for cer tain time.Scanning electron microscopy(SEM),electron dispersion X-ray analysis(E DAX)and X-ray photoelectron spectroscopy(XPS)were used to study the morphology,e lement composition and valence on the corrosion surface.The surfaces were obviou sly uneven,and some tiny crevices appeared in corrosion products that can help O 2 transmit to inner layer.A brief corrosion mechanism was presented to explain t he experimental observations under this condition.

Key words： A3 steel NaCl deposition atmospheric corrosion

收稿日期: 2001-10-08

ZTFLH:

TG172.3

通讯作者: 屈庆 E-mail: quqing58hotmail.com

Corresponding author: Qing Qv E-mail: quqing58hotmail.com

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	屈庆
	严川伟
	白玮
44.8K

引用本文:

屈庆; 严川伟; 白玮 . NaCl在A3钢大气腐蚀中的作用[J]. 中国腐蚀与防护学报, 2003, 23(3): 160-163 .
Qing Qv, Chuanwei Yan, Wei Bai. ROLE OF NaCl IN THE ATMOSPHERIC CORROSION OF A3 STEEL. J Chin Soc Corr Pro, 2003, 23(3): 160-163 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2003/V23/I3/160

[1]　BiestekT .AtmosphericCorrosion[M ].NewYork:JohnWiley,1982:631
[2]　FrielJJ .AtmosphericcorrosionproductsonAl,ZnandAlZnmetalliccoatings[J].Corrosion,1986,42:422-426
[3]　AlmeidaM ,MorcilloM ,RosalesB .Atmosphericcorrosionofzinc[J].Br.Corros.J.,2000,35:289-296
[4]　HouW ,LiangC .Eight-yearatmosphericcorrosionexposureofsteelinChina[J].Corrosion,1999,55:65-73
[5]　GullmanJ.Effectsofseasaltoncorrosionattacksat8years’ex posureofmetalsinasmallgeographicalareaoftheSwedishwestcoast[A].CorrosionControlforLow-Costreliability,12 thInter nationalCorrosionCongress[C].1993:642-648
[6]　MorcilloM ,ChicoB ,MariacaL ,OteroE .Effectofmarineaerosolonatmosphericcorrosion[J].Mater.Perform.,1999,38:72-77
[7]　BengtssonBl櫣ｃｈｅｒＤ,Lindstr mR .TheeffectofCO2 ontheNaCl-inducedatmosphericcorrosionofaluminum[J].J .Electrochem.Soc.,2001,148:B127-B131
[8]　LinCY ,HsiehMJ .InfluenceofNaClcontentinatmosphericaironthecorrosioncharacteristicofboilers[J].Corros.Prev.Con trol,1995,42:107-118
[9]　WangGY ,WangHJ ,LiXL ,YinYD .CorrosionandProtectioninNaturalEnvironment[M ].Beijing:ChemicalIndustryPress,1997:18(王光雍,王海江,李兴濂,银耀德.自然环境的腐蚀与防护[M ].北京:化学工业出版社,1997:18)
[10]　FeliuS ,MorcilloM ,ChicoB .Effectofdistancefromseaonat mosphericcorrosionrate[J].Corrosion,1999,55:883-891
[11]　SvenssonJE ,JohanssonLG .AlaboratorystudyoftheinitialstagesoftheatmosphericcorrosionofzincinthepresenceofNaCl,InfluenceofSO2 andNO2[J].Corros.Sci.,1993,34:721-740
[12]　Lindstr mR ,SvenssonJE ,JohanssonLG .TheatmosphericcorrosionofzincinthepresenceofNaCl[J].J .Electrochem.Soc.,2000,147:1751-1757
[13]　QuQ ,YanCW ,BaiW ,CaoCN .InfluenceofNaCldepositiononatmosphericcorrosionofzincinthepresenceofSO2[J].ActaMetall.Sin.,2001,37:72-76(屈庆,严川伟,白玮,曹楚南.SO2存在下NaCl沉积量对Zn大气腐蚀的影响[J].金属学报,2001,37:72-76)
[14]　QuQ ,YanCW ,CaoCN ,EffectofNaCloninitialatmosphericcorrosionofzincbyusingquartzcrystalmicrobalance[J].Corros.Sci.Prote.Technol.,2002,22(3):139(屈庆,严川伟,曹楚南.用石英晶体微天平研究NaCl对Zn初期大气腐蚀的影响[J].腐蚀科学与防护技术.2002,22(3):139)
[15]　DawsonJL ,FerreiraMG .Electrochemicalstudiesofthepittingofausteniticstainlesssteel[J].Corros.Sci.,1986,26:1009-1026

[1]	曹敏, 刘莉, 余钟芬, 李瑛, 王福会. 2A02铝合金在模拟海洋大气环境中的剥蚀行为研究[J]. 中国腐蚀与防护学报, 2018, 38(5): 502-510.
[2]	朱丽琴 . 席夫碱基咪唑啉化合物对A3钢在盐酸介质中缓蚀性能研究[J]. 中国腐蚀与防护学报, 2006, 26(6): 336-341 .
[3]	韩薇; 贾薇; 汪俊 . 凝露状态下SO2对A3钢腐蚀机理的影响[J]. 中国腐蚀与防护学报, 2002, 22(6): 355-358 .
[4]	徐永祥; 严川伟 . 大气环境中涂层下金属的腐蚀和涂层的失效[J]. 中国腐蚀与防护学报, 2002, 22(4): 249-256 .
[5]	刘仲娥; 毕玉玲; 李忆莲 . 低压电器用铆钉触头在潮湿大气中的腐蚀[J]. 中国腐蚀与防护学报, 2001, 21(4): 230-233 .
[6]	严川伟; 曹楚南; 林海潮 . 石英晶体微天平(QCM)在大气腐蚀研究中的应用[J]. 中国腐蚀与防护学报, 2001, 21(2): 0-127 .

Viewed

Full text

Abstract

Cited

Shared

Discussed