中国腐蚀与防护学报  2002, Vol. 22 Issue (4): 233-236     
  研究报告 本期目录 | 过刊浏览 |
镁合金化学镀镍层的结合机理
刘新宽;向阳辉;胡文彬
上海交通大学材料科学与工程学院
ADHESION MECHANISM OF DIRECT ELECTROLESSNICKEL COATING ON MAGNESIUM ALLOYS〖ST〗〖HT〗〖WT〗〖KH1D〗
Xinkuan Liu;Yanghui Xiang;Wenbin Hu
上海交通大学材料科学与工程学院
全文: PDF(132 KB)  
摘要: 镁合金在直接化学镀前的活化处理时,表面生成一层氟化物 保护膜.溶解度计算及XPS分析表明,氟化物膜在镀液中可稳定存在.用SEM、XPS、SAM考察 了初始沉积Ni、镀层横截面以及开裂后的断面形貌与成分,发现在镀层与基体之间存在着 氟化物、镀液成分与Ni的混杂层.这一混杂层是镀层与基体结合的最薄弱环节,镀层开裂通 常首先发生在此混杂层内.
关键词 镁合金化学镀结合机制氟化物    
Abstract:The theoretical calculation and XPS analysis show t hat the fluoride layer formed during activation in hydrogen fluoride acid dissol ves little in electroless plating bath.The adhesive characteristics of nickel co ating with the magnesium alloys matrix were studied by means of the analysis of the initially deposited nickel and the cross section of the coating as well as t he fracture surface by using TEM,XPS,SAM.It is shown that there exists a mixture co mpound layer above the matrix surface between the magnesium and the nickel coati ng,which consists of fluoride,nickel and the composition of plating bath.Fractur e usually occurs in the mixture layer which is the weakest link for the adhesion of nickel coating on the magnesium alloys.
Key wordsmagnesium alloy    direct electroless nickel plating    adh esion mechanism    fluoride
收稿日期: 2001-01-13     
ZTFLH:  TQ153.1  
通讯作者: 刘新宽   
Corresponding author: Xinkuan Liu   

引用本文:

刘新宽; 向阳辉; 胡文彬 . 镁合金化学镀镍层的结合机理[J]. 中国腐蚀与防护学报, 2002, 22(4): 233-236 .
Xinkuan Liu, Yanghui Xiang, Wenbin Hu. ADHESION MECHANISM OF DIRECT ELECTROLESSNICKEL COATING ON MAGNESIUM ALLOYS〖ST〗〖HT〗〖WT〗〖KH1D〗. J Chin Soc Corr Pro, 2002, 22(4): 233-236 .

链接本文:

https://www.jcscp.org/CN/      或      https://www.jcscp.org/CN/Y2002/V22/I4/233

[1]MakarGL ,KrugerJ .Corrosionofmagnesium[J].Inter.Mater.Rew.,1993,38(3):138-153
[2]LiuXikuan,XiangYanghui,HuWenbin,etal.Reviewofelectrolessnickelcoatingonmagnesiumalloys[J].AerospaceMaterials&Technology,2001,4:21-25(刘新宽,向阳辉,胡文彬,等.镁合金化学镀镍研究状况[J].宇航材料工艺,2001,4:21-25)
[3]BrownL .UKcompanyleadsthewayinmagnesiumplating[J].Fin ishing,1994,18(11):22-23
[4]Standardguideforpreparationofmagnesiumandmagnesiumalloysforelectroplating[S].ASTMDesignation:B480-88
[5]FairweatherWA .Electrolessnickelplatingofmagnesium[J].TransIMF ,1997,75(3):113-117
[6]ZhangXianglin.CompoundChemistry[M].Changsha:PressofCen tralSouthPolytechnicUniversity,1988(张祥麟.配合物化学[M].长沙:中南工业大学出版社,1988)
[7]XiangYH .Astudyonsurfacestateduringthepretreatmentofelec trolessnickelplatingonmagnesiumalloys[J].TransIMF ,tobepublished.
[8]WangJianqi,WuWenhui,FengDaming.IntroductionofElectronicSpectroscopy(XPS/XAES/UPS)[M ].Beijing:DefensiveIndustryPress,1992(王建琪,吴文辉,冯大明.电子能谱学(XPS/XAES/UPS)引论[M].北京:国防工业出版社,1992)
[9]XiangYanghui.Initialdepositionmechanismofelectrolessnickelcoatingonmagnesiumalloys[J].JournalofShanghaiJiaotongUni versity,2000,34(12):1638-1640(向阳辉.镁合金直接化学镀镍的初始沉积机制[J].上海交通大学学报,2000,34(12):1638-1640)
[1] 郑黎, 王美婷, 于宝义. 镁合金表面冷喷涂技术研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 22-28.
[2] 魏征, 马保吉, 李龙, 刘潇枫, 李慧. 镁合金表面超声滚压预处理对微弧氧化膜耐蚀性能的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 117-124.
[3] 于浩冉, 张文丽, 崔中雨. 4种镁合金在Cl--NH4+-NO3-溶液体系中的腐蚀行为差异研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 553-559.
[4] 岳亮亮, 马保吉. 超声表面滚压对AZ31B镁合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 560-568.
[5] 郏义征, 王保杰, 赵明君, 许道奎. 固溶处理制度对挤压态Mg-Zn-Y-Nd镁合金在模拟体液中腐蚀和析氢行为的影响规律研究[J]. 中国腐蚀与防护学报, 2020, 40(4): 351-357.
[6] 孙硕, 杨杰, 钱薪竹, 常人丽. Ni-Cr-P化学镀层的制备与电化学腐蚀行为[J]. 中国腐蚀与防护学报, 2020, 40(3): 273-280.
[7] 张尧, 郭晨, 刘妍慧, 郝美娟, 成世明, 程伟丽. 挤压态Mg-2Sn-1Al-1Zn合金在模拟体液中的电化学腐蚀行为[J]. 中国腐蚀与防护学报, 2020, 40(2): 146-150.
[8] 郏义征, 赵明君, 程世婧, 王保杰, 王硕, 盛立远, 许道奎. 模拟人体体液中镁合金的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2019, 39(6): 463-468.
[9] 欧阳跃军,胡婷,王佳音,谢治辉. 镁合金表面层状双氢氧化物的电化学沉积和表征[J]. 中国腐蚀与防护学报, 2019, 39(5): 453-457.
[10] 王保杰,栾吉瑜,王士栋,许道奎. 镁合金应力腐蚀开裂行为研究进展[J]. 中国腐蚀与防护学报, 2019, 39(2): 89-95.
[11] 刘丽,于思荣. 添加Gd对AM60镁合金耐腐蚀性能的影响[J]. 中国腐蚀与防护学报, 2019, 39(2): 185-191.
[12] 刘辉,邱玮,冷滨,俞国军. 304和316H不锈钢在LiF-NaF-KF熔盐中的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2019, 39(1): 51-58.
[13] 樊志民, 于锦, 宋影伟, 单大勇, 韩恩厚. 镁合金点蚀的研究进展[J]. 中国腐蚀与防护学报, 2018, 38(4): 317-325.
[14] 王志虎, 张菊梅, 白力静, 张国君. AZ91镁合金表面微弧氧化与化学镀铜复合处理层的微观组织与性能[J]. 中国腐蚀与防护学报, 2018, 38(4): 391-396.
[15] 陈琳, 钟福荣, 昝金龙. 复合电解液中AZ31B镁合金的放电特性及电压滞后[J]. 中国腐蚀与防护学报, 2018, 38(2): 197-202.