埋置沸腾床中管件耗损与HCl影响的实验室模拟

牛焱;候嫣

中和院金属所;金属腐蚀与防护国家重点实验室

SIMULATED STUDY OF TUBE WASTAGE IN BUBBLING FLUIDIZED BED WITH DENSE PARTICLE IMPACT AND HCI EFFECT

Yan Niu;Yan Hou

中和院金属所;金属腐蚀与防护国家重点实验室

全文: PDF(209 KB)

摘要: 采用实验室流态床燃烧器模拟装置评定氯化物对埋管耗损的影响.该模拟装置能重现埋管底部遭受密集颗粒的冲刷,其运行参数可控,以接近沸腾流态床所遇工况.HCI被选为Cl源加入流态化空气中,其含量在50-400μg/g间可调.试验温度范围由室温至400℃.以1018低碳钢棒代表埋管,床体为平均粒度800μm的工业用SiO2砂.结果表明,HCl明显地加剧材料的耗损，且其随HCl浓度的增加而加剧。本研究所获HCl加剧耗损程度的数量级与报道的现场结果相当。

关键词 ： HCl, 耗损, 热交换管, 流态床燃烧

Abstract：Heat-exchanger tubes in fluidized bed combustors (FBCs) often suffer material loss due to combined effect of corrosion and erosion. Some field studies have indicated a possible chlorine effect,where coals containing higher chlorine contents cause higher wastage rates.Theeffect,however,is neither understood nor certain due to inconclusuve field and laboratory data. The purpose of this paper is to report the results of experiments using a wastage simulator to evaluate the effect of chlorine on in-bed tube wastage.The rig was designed to simulate dense particle impacts in tube bottoms with well-controlled parameters, and has been proven to closely reflect situations found in operating bubbling FBCs.In this study ,HCl gas wwas chosen to be the chloring source and was introduced into the fluidized bed at 40-50μg/g concentrations. Tests were performed at temperatures ranging from ambient to 400℃ using 1018low carbon steel rods in abed of commercial SiO2 sand that had an average size of 800μm .The wear profile after each test was measured using profilometer.Results showed a significant increase in material wastage rates in the presence of HCl, and that the rate was greater with higher HCl concentrations. The magnitude of the effect observed appears to be of the same order as that reported in practice.

Key words： HCl wastage heat exchanger tube fluidized bed combustion

收稿日期: 1999-07-20

ZTFLH:

TG172.82

Corresponding author: Yan Niu

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	牛焱
	候嫣
44.8K

引用本文:

牛焱; 候嫣 . 埋置沸腾床中管件耗损与HCl影响的实验室模拟[J]. 中国腐蚀与防护学报, 2000, 20(4): 217-223 .
Yan Niu, Yan Hou. SIMULATED STUDY OF TUBE WASTAGE IN BUBBLING FLUIDIZED BED WITH DENSE PARTICLE IMPACT AND HCI EFFECT. J Chin Soc Corr Pro, 2000, 20(4): 217-223 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2000/V20/I4/217

[1] Stringer J, Stallings J W, Wheeldon J M. Wastage in bubbling fluidized-bed combustors: an updated [A]. Manaker AM. Proc. 10thInt. Conf. on Fluidized Bed Combustion [C]. New York: ASME Press, 1989.857-862.
[2] Stringer J, Wright I G. Erosion/Corrosion in FBC Boilers [A]. Proc. of a Workshop Held at Argonne National Laboratory[C].Argonne: 1987, (1):1 - 38.
[3] Oakey J E, Minchener AJ, Hodges N J. The use of high chlorine coal in industrial boilers[A]. Stringer J, Banerjee DD. Chlorine inCoals[C]. New York: Elseviar Press, 1991.251 - 273.
[4] Wheeldon J W, Stallings J W, Sethi VK, Wright I G. Preliminary results from a programmer to identify bed materials properties whichmay have promoted metals loss from evaporator tubing in TVA's 20-Mwe bubbling AFBC pilot plant [A]. Levy A V. Proc. Corrosionerosion-wear. at Elev. Temp. [C]. Houston: NACE, 1991.22-31.
[5] Macadam SS. Stringer J. Temperature dependence of steel wastage in a bubbling fluidized bed simulator [J]. Corrosion. 1993, (49):156 - 169.
[6] Macadam S, Stringer J. The nature of bubble-induced wear of in-bed tubes. in FBCs [A]. Levy A. Proc. 4th Berkeley Conf. onCorrosion-erosion-wear of Mater. at Elev. Temp. [C]. Berkeley: 1990. 17-21.
[7] Hou PY. MacAdam J J, Zhang H, Stringer J. Summary of results from the Berkeley in-bed tube erosion simulator [J]. Mater. at HighTemp., 1997, (14): 325 - 335.
[8] Zhang H, Hou P Y, Stringer J. The effect of temperature gradient on steel tube wastage in a bubbling fluidized bed simulator[J]. Wear,1997, (197): 286-294.D

[1]	黄勇, 王善林, 王帅星, 龚玉兵, 柯黎明. 含硫化物夹杂铁基块体非晶合金在HCl溶液中的腐蚀行为[J]. 中国腐蚀与防护学报, 2018, 38(2): 203-209.
[2]	偶国富, 赵露露, 王凯, 王宽心, 金浩哲. 10^#碳钢在HCl-H₂O环境中的露点腐蚀行为[J]. 中国腐蚀与防护学报, 2018, 38(1): 33-38.
[3]	唐俊文,邵亚薇,陈阵，张涛，孟国哲，王福会. 碳钢在90℃、H₂S-HCl-H₂O环境下的腐蚀行为 Ⅱ-H₂S溶液中HCl浓度对碳钢腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2011, 31(1): 34-39.
[4]	骆素珍 . 1Cr18Mn14N不锈钢在HCl溶液中的空蚀行为[J]. 中国腐蚀与防护学报, 2004, 24(6): 350-355 .
[5]	陈俊明;吕战鹏. 有、无磁场下缓蚀剂对Fe/0.05mol· L~(-1)HCl极化行为的影响[J]. 中国腐蚀与防护学报, 1997, 17(2): 135-141.
[6]	沈嘉年;王戈. Ni-20Cr合金的高温氯化[J]. 中国腐蚀与防护学报, 1995, 15(3): 189-195.

Viewed

Full text

Abstract

Cited

Shared

Discussed