环境诱导氢致断裂的过载效应

高桦;杨晓雷;曹卫杰

上海工程技术大学能源与环境工程研究所

EFFECT OF OVERLOADING ON ENVIRONMENTAL HYDROGEN INDUCED FRACTURE

Gao Hua;Yang Xiaolei;Cao Weijie(Shanghai University of Engineering Science)

全文: PDF(1586 KB)

摘要: 在连续充氢条件下，就４２ＣｒＭｏ／０．５ｍｏｌ／ＬＨ２ＳＯ４体系短时过载对氢致断裂寿命的影响进行了研究。实验结果表明：（１）在材料服役的早期加入短时过载将使氢致断裂寿命延长，（２）在材料服役的后期加入短时过载则会缩短氢致断裂寿命。文中从过载引起残余压应力、位错屏蔽效应和过载损伤等方面进行了分析与讨论。

关键词 ：氢致断裂, 过载效应, 氢浓度

Abstract：The effect of short period overloading on the lifetime of environmental hydrogen induced fracture (HIF) for 0.42%C, 0.87%Cr, 0.21%Mo steel in 0.5mol/L H2SO4 solution was studied under continuous hydrogen charging. Experimental results showed that when overloading was applied at the early or intermediate stage of the service period, the HIF life become longer; however, if overloading was applied rather late, the HIF life was shortened. It was noticed that hydrogen absorption, hydrogen transportation and accumulation,crack initiation and propagation were at only dependent on the electro-chemistry condition, but also on the stress-strain state and history. These observations were explained in terms of residual compression stress, dislocation shielding and damage caused by overloading.

Key words： Hydrogen induced fracture Overloading effect Hydrogen concentration

收稿日期: 1995-08-25

基金资助:国家自然科学基金;;上海市高教科技发展基金

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	高桦
	杨晓雷
	曹卫杰
44.8K

引用本文:

高桦;杨晓雷;曹卫杰. 环境诱导氢致断裂的过载效应[J]. 中国腐蚀与防护学报, 1995, 15(4): 254-260.
. EFFECT OF OVERLOADING ON ENVIRONMENTAL HYDROGEN INDUCED FRACTURE. J Chin Soc Corr Pro, 1995, 15(4): 254-260.

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y1995/V15/I4/254

1HydrogenEmbrittlementTed．ASTM．STP543,19742高桦,曹卫杰．中国腐蚀与防护学报,1991,11(2):1633王克仁,徐纪林,高桦．SCIENTIASINICA,1979,XXII:579-5834PookLP．Eng．Fract．Mech,1971,3:205-2125吴世丁,陈廉,刘民治．金属学报,1990,26(2):A86-A916高桦,曹卫杰,方昌鹏,刘树望,陈廉．中国腐蚀与防护学报,1993.13(3):237-2447PageRA,GerberichWW．Metall．Thans．1982,13A(2):305-311

[1]	黄长河;李金许;王燕斌;褚武扬;梅冬生;俞梦文;籍可镔. 重轨钢氢脆的表现形式及规律[J]. 中国腐蚀与防护学报, 1997, 17(2): 129-134.
[2]	曹卫杰;杨晓雷;高桦. 环境诱导氢致断裂的非比例过载效应[J]. 中国腐蚀与防护学报, 1996, 16(3): 181-186.

Viewed

Full text

Abstract

Cited

Shared

Discussed