阳极极化状态下铝的瞬时阻抗

朱应扬;王旷;朱日彰;张文奇

北京钢铁学院;北京钢铁学院;北京钢铁学院;北京钢铁学院

INSTATNEOUS IMPEDANCE OF ALUMINIUM IN ANODIC POLARIZATION STATUS

Zhu Yingyang;Wang Kuang;Zhu Rizhang;Zhang Wanqi Beijing University of Iron and Steel Technology

全文: PDF(627 KB)

摘要: 采用拉普拉斯变换交流阻抗测量方法,测量了铝在 NaCl 溶液中阳极极化后的瞬时阻抗。极化刚开始的瞬间,表面膜尚未受破坏,此时界面电阻(R_界)与极化电流密度(i_P)的关系为:logR_界=K-logi_P 界面电容(C_界)则与 i_P 无关,主要取决于膜厚。极化开始以后,R_界随时间变化不大,C_界则变化很大。这是由于溶解区电阻与有膜区电阻相差不大,而溶解区电容与有膜区电容相差较大。将铝在空气中形成的钝化膜看作半导体膜,所导出的结论与试验结果符合很好。

Abstract：The instantaneous impedance of Al in 1N NaCl at various polarization times has been measured using Laplace transformation method.In the instan of beginning of polarization,the dependence of interfacial resistance R,on polarization current densitg i_p,is as follows: logR_f=K-logi_p Interfacial capacitance Cf,which is independent of i,depends only on film's thickness.In the course of polarization,R_f hardly changes with time, but C_f changes greatly This is due to the fact that the difference between electric resistance on corroded region and that on film region is very small while there is a large difference in capacitance of both regions.

收稿日期: 1985-08-25

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	朱应扬
	王旷
	朱日彰
	张文奇
44.8K

引用本文:

朱应扬;王旷;朱日彰;张文奇. 阳极极化状态下铝的瞬时阻抗[J]. 中国腐蚀与防护学报, 1985, 5(4): 250-257.
. INSTATNEOUS IMPEDANCE OF ALUMINIUM IN ANODIC POLARIZATION STATUS. J Chin Soc Corr Pro, 1985, 5(4): 250-257.

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y1985/V5/I4/250

[1] Pryor,M.J.,Localized Corrosion,Ed.Staehle,R.W.et al.,NACE,Houson TX.,2(1974)
[2] Wood,G.,C.,Sutton,W.H.,Richardson,J.A.,Riley,T.N.K.,Malherbe,A.G.,Ibid.P526
[3] 徐乃欣,Thompson,G.E.,DaWson,J.L.,Wood,G.C.,中国腐蚀与防护学报,2(4) ,27(1982)
[4] Heine,M.A.,Pryor,M.J.,J.Electrohem.Soc.,110,1205(1963)
[5] Brock,A.J.,Wood,G.C.,Electrochim.Acta,12,395(1967)
[6] 沈行素,常玉勤,高效岳,中国腐蚀与防护学报,3(1) ,16(1983)
[7] 朱应扬,朱日彰,王旷,张文奇,实验技术与管理,2(2) ,38(1985)
[8] Kaesche,H.,Passivity in Metal,The Electrochemical Soc.,Princeton,N.J.,935(1978)
[9] Norio Sato.Ibid,P29
[10] Libsch,T.A.;Devereux,O.F.,J,Electrochem.Soc.,123,864(1976)
[11] McMullen,J.J.;Pryor,M.J.,First Iit.Cong.Metall.Corroosion,Butterworths,London.,52(1962)
[12] Antropov,L.I.,Theoretical Electrochemistry,中文译本284,78 (1977)

No related articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed