黄铜冷凝管的点蚀

单义斌;常玉勤;林海潮;班明昭

中国科学院长春应用化学研究所;中国科学院长春应用化学研究所;中国科学院长春应用化学研究所;中国科学院长春应用化学研究所

ON THE PITTING CORROSION OF BRASS CONDENSER TUBE

Shan Yibin;Chang Yugin;Lin Haichao;Ban Mingzhao Changchun Institute of Applied Chemistry; Academia Sinica

全文: PDF(865 KB)

摘要: 研究了 H68 A 黄铜在含 Cl~-溶液中的闭塞阳极行为。结果表明,黄铜的闭塞阳极不存在加速腐蚀的自催化效应,而是使闭塞区表面保持活性状态。其电位随阳极液 Cu~+浓度升高而变正。闭塞区Cu~+和 H~+不能向外扩散时,EE_(Cu/CuCl/Cl~-)进行生成 CuCl[s]的溶解反应。Cu~+和 H~+能向外扩散时,E>E_(Cu/Cu_2O/h 即能发生溶解。此时闭塞室内生成 Cu_2O。闭塞区外有扩散出来的 Cu~+经二次反应后生成的沉积物。黄铜冷凝管点蚀的腐蚀产物分布情况符合后者,这种点蚀在 E>E_(Cu/Cu_2O)时即能形成。黄铜管表面有碳膜时容易形成闭塞区并使电位升高,起到促进点蚀发生和加速点蚀作用,而不是产生点蚀的必要条件。为防止点蚀必须促使黄铜表面生成完整的保护膜。

Abstract：The anodic behaviour of H68A brass in occluded condition was investigated. It is shown that in the occluded area the surface of brass remains in active state,butno autocatalytic dissolution effect can be detected.The potential of brass in occluded area becomes more noble as the concentration of Cu~+ in anolyte increases.If H~+ and Cu~+ can not diffuse outwardly from occluded area, the anodic dissolution of brass in occluded area can not take place when EE_(Cu/CuCl/Cl~-).On the other hand,if H~+ and Cu~+ can diffuse outwardly from occluded area,the anodic dissolution occurs at potential above E_(Cu/Cu_2O/H~+.The product of anodic dissolution in cavity is Cu_2O.At the same time,there are deposits formed at the mouth of the cavity by secondary reactions of Cu~+ diffused outwardly from cavity. The distribution of the corrosion products within and over the pits on brass conpenser tubes seems the latter case as mentioned above,so Cu~+ and H~+ ions must diffuse from pits toward outside in the pitting corrosion process of brass tube and hence these pits can be formed when E

收稿日期: 1985-08-25

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	单义斌
	常玉勤
	林海潮
	班明昭
44.8K

引用本文:

单义斌;常玉勤;林海潮;班明昭. 黄铜冷凝管的点蚀[J]. 中国腐蚀与防护学报, 1985, 5(4): 241-249.
. ON THE PITTING CORROSION OF BRASS CONDENSER TUBE. J Chin Soc Corr Pro, 1985, 5(4): 241-249.

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y1985/V5/I4/241

[1] Breckon,C.,Baines,J.R.T.,Trans Inst.Mar.Engrs.,6 7,1(1955)
[2] Retief,R.,Br.Corros.J.,8,264(1973)
[3] 中国科学院上海冶金研究所六室,金属腐蚀与防护,(1) ,13(1977)
[4] Evans,U.R.,金属的腐蚀与氧化,华保定译,机械工业出版社,393(1976)
[5] Müller,R.O.,Metallice Corrosion,8 th ICMC,Frankfurt Main,1470(1981)
[6] Campall,H.S.,Localized Corrosion(Proceeding on U.R.,Evens Conference on Loalized Corrosion),NACE-3,Williamsburg,Virglnia,6～10,Dec.,625(1971) ,Editors:Staehle,R.W.,et al.
[7] 何辉纯,火力发电厂金属的水汽腐蚀问题及其防腐研究,中国腐蚀与防护学会第二分组第一次学术报告会(1979)
[8] 中国科学院应用化学研究所金属腐蚀组,金属腐蚀与防护,(1) ,9(1976)
[9] 山东工学院,黄铜管表面残碳对其耐蚀性能影响的初步探讨
[10] Faia,G.,Fiori,G.,Salvadore,D.,Corrosion,Science,15,382(1975)
[11] Pourbaix,M.Corrosion,25,267(1969)
[12] Mattsson,E.,Fredriksson,A.M.,Br Corros J.,3,246(1968)

No related articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed