亚温淬火对30CrMnSiA 钢氢致延迟断裂的影响

吴忍畊;李仁顺

哈尔滨工业大学;哈尔滨工业大学

EFFECT OF QUENCHING FROM INTERCRITICAL TEMPERATURE ON HYDROGEN-INDUCED CRACKING IN 30CrMnSiA STEEL

Wu Rengeng Li Renshun (Harbin Institute of Technology)

全文: PDF(1786 KB)

摘要: 本文研究了亚温(α+γ)区域淬火对高强钢30CrMnSiA 氢致延迟断裂的影响。结果表明,在900℃油淬和250℃回火之间增加一次自860℃(α+γ)区的亚温淬火能显著提高该钢的抗氢脆能力。可提高回火马氏体的氢致延迟断裂的下临界应力,降低裂纹扩展速率,而对回火索氏体组织影响不大。离子探针和 X-射线能谱分析发现亚温淬火在不同程度上消除了合金元素和杂质元素在奥氏体晶界上的偏聚;微量铁素体的存在,以及奥氏体晶粒细化都对改善钢的氢致延迟断裂抗力起着有益的作用。

Abstract：The effect of quenching from intercritical temperature in(α+γ)region on hydrogen-induced cracking of a high strength steel 30CrMnSiA was studied. The results showed that an additional intereritical quenching from 860℃,per- formed between the oil quenching from 900℃ and tempering at 250℃,markedly improved the hydrogen embrittlement resistance of this steel.The minimum stress to hydrogen-induced cracking was increased by several times in steels with tempered martensltebut there was no effect on steel with sorbitic struc- ture having hardness below HRc36.The crack propagation rate of the steels with tempered martensite also decreased due to the intercritical quenching. The microanalyses of fractures with IMA and XPS showed that the segregation of impurities and the elements producing brittle failure at austenite grain boundaries was attenuated to a certain extent by this quenching.It would be bene- ficial for the superior hydrogen embrittlement resistance of the steel.In addition,the presence of minor ferrite and austenite grains refined could could also be helpful.

收稿日期: 1984-02-25

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	吴忍畊
	李仁顺
44.8K

引用本文:

吴忍畊;李仁顺. 亚温淬火对30CrMnSiA 钢氢致延迟断裂的影响[J]. 中国腐蚀与防护学报, 1984, 4(1): 22-28.
. EFFECT OF QUENCHING FROM INTERCRITICAL TEMPERATURE ON HYDROGEN-INDUCED CRACKING IN 30CrMnSiA STEEL. J Chin Soc Corr Pro, 1984, 4(1): 22-28.

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y1984/V4/I1/22

[1] Peterson M.H.,Brown B.F.,Newbegin R.L.,Groover R.E.,Corrosion 23,14(1967)
[2] Sandoz G.,Met.Trans.,3,1169(1972)
[3] 中里福和寺奇富久长《铁と钢》,61,6,856～868(1975)
[4] #12
[5]#12
[6] Hrirnak L.,Welding in the world,7,3,176(1969)
[7] #12
[8] #12
[9] #12
[10] 李仁顺吴忍(田井),航天工艺金属材料的氢脆与应力腐蚀开裂(专辑),30～40(1983)
[11] Cappak B.N.,8,C.17(1977)
[12] Cappak B.H.,5,C.11(1982) ,

No related articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed