AZ91D镁合金化学镀镍

霍宏伟;李瑛;王福会

中科院金属所

ELECTROLESS NICKEL PLATING ON AZ91D MAGNESIUM ALLOY

Hongwei Huo;Ying Li;Fuhui Wang

中科院金属所

全文: PDF(135 KB)

摘要: 利用化学镀镍的方法，在AZ91D镁合金表面得到了均匀、致密，无明显表面缺陷的Ni-P涂层.X-ray衍射分析表明，镀层组织为单一的Ni；热震实验表明涂层与基体合金结合良好；动电位极化测试表明涂层的自腐蚀电位接近-0.4 V(SCE)，有明显的钝化区，耐腐蚀性能优异，可对基体合金起到理想的防护作用.

关键词 ： AZ91D, 镁合金, 化学镀镍, 腐蚀

Abstract：A nickel-phosphor coating was prepared on the surfa ce of AZ91D magnesium alloy by electroless plating.The coating was so uniform an d dense that it had no obvious surface defects.The structure o f the coating was single phase (Ni) by X-ray diffraction and the adhesion was go od by quenching.By dynamic potential polarization,it was shown that the free cor rosion potential of the coating approached -0.4 V(SCE) and it had evident passiv ation.The coating had better corrosion resistance than the substrate,and had ext ensive application prospect.

Key words： AZ91D magnesium electroless nickel plating corrosion

收稿日期: 2001-11-08

ZTFLH:

TG174.4

通讯作者: 霍宏伟

Corresponding author: Hongwei Huo

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	霍宏伟
	李瑛
	王福会
44.8K

引用本文:

霍宏伟; 李瑛; 王福会 . AZ91D镁合金化学镀镍[J]. 中国腐蚀与防护学报, 2002, 22(1): 14-17 .
Hongwei Huo, Ying Li, Fuhui Wang. ELECTROLESS NICKEL PLATING ON AZ91D MAGNESIUM ALLOY. J Chin Soc Corr Pro, 2002, 22(1): 14-17 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2002/V22/I1/14

[1]ZengXiaoqin,WangQudong,L櫣Ｙｉｚｈｅｎ,etal.Newdevelopmentofmagnesiumalloyapplication[J].Foundry,1998,(11):39
(曾小琴,王渠东,吕宜振等.镁合金应用新进展[J].铸造,1998,(11):39)
[2]HuoHongwei,LiYing,WangFuhui,etal.Corrosionandprotectionofmagnesiumalloy[J].MaterialsReview,2001,16(7):25
(霍宏伟,李瑛,王福会等.镁合金的腐蚀与防护[J].材料导报,2001,16(7):25)
[3]ZengAiping,XueYing,QianYufeng,etal.Chemicalsurfacetreat mentformagnesiumalloy[J].CorrosionandProtection,2000,21(2):55
(曾爱平,薛影,钱宇峰等.镁合金的化学表面处理[J].腐蚀与防护,2000,21(2):55)
[4]FairweatherWA .Electrolessnickelplatingofmagnesium[J].TransIMF ,1997,75(3):113
[5]SakataY .Electrolessnickelplatingdirectlyonmagnesiumalloydiecastings[A].In:TheProceedingsofthe74thAESFAnnualTechni calConference[C].Orlando:AESF ,1987.6
[6]JiangXiaoxia,ShenWei.TheFundamentalsandPracticeofElectro lessPlating[M ].Beijing:NationalDefenseIndustryPress,2000.26
(姜晓霞,沈伟.化学镀理论及实践[M ].北京:国防工业出版社,2000.26)
[7]GB/T 13913-92Autocatalyticnickel-phosphoruscoating-Spec ificationandtestmethods

[1]	郑黎, 王美婷, 于宝义. 镁合金表面冷喷涂技术研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 22-28.
[2]	魏征, 马保吉, 李龙, 刘潇枫, 李慧. 镁合金表面超声滚压预处理对微弧氧化膜耐蚀性能的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 117-124.
[3]	于浩冉, 张文丽, 崔中雨. 4种镁合金在Cl^--NH₄⁺-NO₃^-溶液体系中的腐蚀行为差异研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 553-559.
[4]	岳亮亮, 马保吉. 超声表面滚压对AZ31B镁合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 560-568.
[5]	郏义征, 王保杰, 赵明君, 许道奎. 固溶处理制度对挤压态Mg-Zn-Y-Nd镁合金在模拟体液中腐蚀和析氢行为的影响规律研究[J]. 中国腐蚀与防护学报, 2020, 40(4): 351-357.
[6]	张尧, 郭晨, 刘妍慧, 郝美娟, 成世明, 程伟丽. 挤压态Mg-2Sn-1Al-1Zn合金在模拟体液中的电化学腐蚀行为[J]. 中国腐蚀与防护学报, 2020, 40(2): 146-150.
[7]	郏义征, 赵明君, 程世婧, 王保杰, 王硕, 盛立远, 许道奎. 模拟人体体液中镁合金的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2019, 39(6): 463-468.
[8]	欧阳跃军,胡婷,王佳音,谢治辉. 镁合金表面层状双氢氧化物的电化学沉积和表征[J]. 中国腐蚀与防护学报, 2019, 39(5): 453-457.
[9]	王保杰,栾吉瑜,王士栋,许道奎. 镁合金应力腐蚀开裂行为研究进展[J]. 中国腐蚀与防护学报, 2019, 39(2): 89-95.
[10]	刘丽,于思荣. 添加Gd对AM60镁合金耐腐蚀性能的影响[J]. 中国腐蚀与防护学报, 2019, 39(2): 185-191.
[11]	樊志民, 于锦, 宋影伟, 单大勇, 韩恩厚. 镁合金点蚀的研究进展[J]. 中国腐蚀与防护学报, 2018, 38(4): 317-325.
[12]	王志虎, 张菊梅, 白力静, 张国君. AZ91镁合金表面微弧氧化与化学镀铜复合处理层的微观组织与性能[J]. 中国腐蚀与防护学报, 2018, 38(4): 391-396.
[13]	陈琳, 钟福荣, 昝金龙. 复合电解液中AZ31B镁合金的放电特性及电压滞后[J]. 中国腐蚀与防护学报, 2018, 38(2): 197-202.
[14]	崔学军, 平静. 微弧氧化及其在镁合金腐蚀防护领域的研究进展[J]. 中国腐蚀与防护学报, 2018, 38(2): 87-104.
[15]	王海媛, 卫英慧, 杜华云, 刘宝胜, 郭春丽, 侯利锋. 绿色缓蚀剂SDDTC对AZ31B镁合金的缓蚀作用及吸附行为[J]. 中国腐蚀与防护学报, 2018, 38(1): 62-67.

Viewed

Full text

Abstract

Cited

Shared

Discussed