PROGRESS OF WATER VAPOUR EFFECT ON GROWTH OF ALUMINA FORMING ALLOYS

J Chin Soc Corr Pro

2011, Vol. 31

Issue (6): 409-413 DOI:

Review

Current Issue | Archive | Adv Search

PROGRESS OF WATER VAPOUR EFFECT ON GROWTH OF ALUMINA FORMING ALLOYS

XING Linlin, ZHENG Yanjun, CUI Lishan, SUN Maohu, SHAO Mingzeng, LU Guiwu

Departments of Materials Science and Engineering, China University of Petroleum, Beijing 102249

Download:

PDF(369KB)
Export: BibTeX | EndNote (RIS)

Abstract Alumina coating has excellent thermal stability at elevated temperatures, this can provide a good diffusion barrier to withstand high temperature oxidation and therefore, increase their life time in aggressive atmospheres. With the industrial development, water vapour is present in nearly all atmospheres where alumina forming alloys are used at high temperatures for industrial process. The most important problem is that how to maintain excellent performance of alloy in humid atmospheres. This paper summarizes the effect of water or water vapour on the stability of alumina scales, growth kinetics, film adherence and alumina film surface morphology.

Key words: alumina scale water vapour stability oxidation rate

Received: 01 September 2010

ZTFLH:

TG178

Corresponding Authors: ZHENG Yanjun E-mail: yanjun_zheng@hotmail.com

	Service

	E-mail this article
	Add to citation manager
	E-mail Alert
	RSS
	（）
	Articles by authors
	GENG Lin-Lin
	ZHENG Yan-Jun
	CUI Li-Shan
	XUN Mao-Hu
	SHAO Meng-Ceng

Cite this article:

XING Linlin, ZHENG Yanjun, CUI Lishan, SUN Maohu, SHAO Mingzeng, LU Guiwu. PROGRESS OF WATER VAPOUR EFFECT ON GROWTH OF ALUMINA FORMING ALLOYS. J Chin Soc Corr Pro, 2011, 31(6): 409-413.

URL:

https://www.jcscp.org/EN/ OR https://www.jcscp.org/EN/Y2011/V31/I6/409

[1] Horsley G, Cairns J. The inhibition of carbon deposition on stainless steel by prior selective oxidation [J]. Appl. Surf.Sci., 1984, 18(3): 273-286

[2] Millward G R, Evans H E, Aindow M, et al. The influence of oxide layers on the initiation of carbon deposition on stainless steel [J]. Oxid. Met., 2001, 56(3): 231-250

[3] Kofstad P, High Temperature Corrosion [M]. London/New York: Elsevier Applied Science, 1988

[4] Saunders S R J, Monteiro M, Rizzo F. The oxidation behavior of metals and alloys at high temperatures in atmospheres containing water vapour: A review [J]. Prog. Mater. Sci., 2008, 53:775-837

[5] Sebastien F, Sebastien C, Gilles C. Metallic interconnects for solid oxide fuel cell: Effect of water vapour on oxidation resistance of differently coated alloys [J]. J. Power Sources, 2009, 193: 136-145

[6] Larring Y, Haugsrud R, Norby T. H T. corrosion of Cr-5wt%Fe-1wt% Y₂O₃ alloy and conductivity of the oxide scale-effects of water vapor[J]. J. Electrochem. Soc., 2003, 150:374-379

[7] Quadakkers W J, Zurek J, Hansel M. Effect of water vapour on high temperature oxidation of FeCr alloys [J]. JOM, 2009, 61(7):44-50

[8] Prescott R, Graham M J. The formation of aluminum oxide scales on high-temperature alloys [J]. Oxid. Met., 1992, 38(3-4):233-254

[9] Smialek J L, Robinson R C, Opila E J, et al. SiC and Si₃N₄ recession due to SiO₂ scale volatility under combustor conditions [J]. Adv. Compos. Mater, 1999, 8(1): 33-45

[10] Zhou C G, Yu J S, Gong S K, et al. Influence of water vapor on the isothermal oxidation behavior of low pressure plasma sprayed NiCrAlY coating at high temperature [J]. Surf. Coat.Technol., 2002, 161: 86-91

[11] Al-Badairy H, Tatlock G J. The influence of moisture content of the atmosphere on alumina scale formation and growth during high temperature oxidation of PM2000 [J]. Mater. High Temp.,2000, (17): 133-137

[12] Simms N J, Norton J F, Encinas-Oropesa A, et al. An evaluation of the performance of candidate gas turbine abradeable seal materials exposed to a high temperature combustion atmosphere [J]. Mater. Sci. Forum, 2004, 461-464: 875-882

[13] Chevalier S, Juzon1 P, Przybylski K, et al. Water vapor effect on high-temperature oxidation behavior of Fe₃Al intermetallics[J]. Sci. Technol. Adv. Mat., 2009, (10): 7-12

[14] Canovic S, Engkvist J, Liu F, et al. Microstructural investigation of the initial oxidation of the FeCrAlRE alloy Kanthal AF in dry and wet O₂ at 600 and 800℃[J]. J. Electrochem. Soc.,2010, 157(6): 223-230

[15] Kvernes I, Oliveira M, Kofstad P. High temperature oxidation of Fe-13Cr-xAl alloys in air/water vapor mixtures [J].Corros. Sci., 1977, 17: 237-52

[16] Cheng S Y, Kuan S, Tsai W. Effect of water vapor on annealing scale formation on 316SS [J]. Corros. Sci., 2006, 48(3):634-649

[17] Janakiraman R, Meier G H, Pettit F S. The effect of water vapour on the oxidation of alloys that develop alumina scales for protection[A].Tri-Service Conference on Corrosion, Proceedings [C].Wrightsville Beach: N.C, 1997. 1-15

[18] Molins R, Huntz A M. Recent improvements in the understanding of alumina film formation and durability [J]. Mater.Sci. Forum, 2004, 461-464: 29-36

[19] Liu F, Josefsson H, Svensson J E, et al. Cyclic oxidation of two FeCrAIRE foils at 1100 deg C-The influence of the concentration of minor alloying elements on scale [J]. Mater. Sci.Forum, 2008, 595-598 (part 2): 707-716

[20] Pijolat M, Dauzat M, Soustelle M. Influence of additives and water vapour on the transformation of transition aluminas into alpha alumina [J]. Thermochim. Acta, 1987, 122(1): 71-77

[21] Gotlind H, Liu F, Svensson J E, et al. The effect of water vapor on the initial stages of oxidation of the FeCrAl alloy Kanthal AF at 900℃[J]. Oxid. Met., 2007, 67: 251-266

[22] Opila E J, Myers D L. Alumina volatility in water vapor at elevated temperatures [J]. J. Am. Ceram. Soc., 2004, 87: 1701-1705

[23] Opila E J, Jacobson N S, Myers D L, et al. Predicting oxide stability in high-temperature water vapor [J]. JOM, 2006, 1:22-28

[24] Bansal N P, Zhu D. Thermal conductivity of zirconia alumina composites [J]. Ceram. Int., 2005, 31: 911-916

[25] Krikorian O H. Thermochemical hydrogen production studies at LLNL: a status report[A]. International Energy Agency Annex 1 Workshop on Thermochemical Hydrogen[C]. United States: High Temp High Press, 1982. 1-7

[26] John Y. High temperature oxidation and corrosion of metals, Chapter 10: Effects of water vapour on oxidation, Corrosion Series [J], 2008, 1: 455-495

[27] Douglass D L, Kofstad P, Rahmel A, et al. International workshop on high temperature oxidation-subject area 1: the role of water vapour in the oxidation of metals and alloys[J]. Oxid. Met.,1996, 45(5/6): 529-620

[28] Buscail H, Heinze S, Dufour Ph, et al. Water-vapor-effect on the oxidation of Fe 21.5 wt.% Cr, 5.6 wt.% Al at 1000℃[J]. Oxid.Met., 1997, 47(5-6): 445-64

[29] Pint B A, Haynes J A, Zhang Y, et al. The effect of water vapor on the oxidation behavior of Ni-Pt-Al coatings and alloys [J].Surf. Coat. Technol., 2006, 201(7): 3852-3856

[30] Leyens C, Fritscher K, Gehrling R, et al. Oxide scale formation on a MCrAlY coating in various H₂-H₂O atmospheres[J]. Surf. Coat. Technol., 1996, 82: 133-144

[31] Gunnar H, Tveten B, Hornlund E. Hydrogen in chromium: influence on the high-temperature oxidation kinetics in H₂O, oxide-growth mechanisms, and scale adherence [J]. Oxid.Met., 2000, 54(1-2): 1-10

[32] Henry S, Mougin J, Wouters Y, et al. Characterization of chromia scales grown on pure chromium in different oxidizing atmospheres [J]. Mater. High Temp., 2000, 17: 231-4

[33] Hudson L K, Misra C, Perrotta A J, et al. Aluminium Oxide[A]. In Ullmann's Encyclopedia of Industrial Chemistry [C]. New York: Wiley-VCH Verlag, 2002

[34] Janakiraman R, Meier G H, Pettit F S. The effect of water vapour on the oxidation of alloys that develop alumina scales for protection[A]. Cyclic oxidation of high temperature materials-mechanisms, testing methods, characterization and life time estimation [C]. European: European federation of corrosion publications, 1999. 27: 38-62

[35] Maris-Sida M C, Meier G H, Pettit F S. Some water vapor effects during the oxidation of alloys that are α-Al₂O₃ formers [J]. Metall. Mater. Trans., 2003,34A: 2609-2619

[36] Brady M P, Yamamoto Y, Santella Ml, et al. Composition, microstructure, and water vapor effects on internal/external oxidation of alumina-forming austenitic stainless steels[J]. Oxid.Met., 2009, 72(5-6): 311-333

[37] Onal K, Maris-Sida M C, Meier G H, et al. Water vapor effects on the cyclic oxidation resistance of alumina forming alloys [J]. Mater. High Temp., 2003, 20: 81-91

[38] Janakiraman R, Meier G H, Pettit F S. The effect of water vapor on the oxidation of alloys that develop alumina scales for protection [J]. Metall. Mater. Trans., 1999, 30A: 2905-13

[39] Smialek J L, Morscher G N. Delayed alumina scale spallation on Rene'N5+Y: moisture elects and acoustic emission [J].Mater. Sci. Eng., 2002, 332A: 11-24

[40] Tallman R L, Gulbransen E A. Crystal morphology and mechanisms of growth of α-Fe (III) oxide whiskers on iron [J]. J. Electrochem. Soc., 1967, 114(12): 1227-1230

[41] RuDiger D. Solution and transport of water in oxides [J]. Mater. High Temp., 2005, 22: 93-103

[42] Raynaud G M, Rapp R A. In situ observation of whiskers, pyramids and pits during the high-temperature oxidation of metals [J]. Oxid. Met., 1984, 21: 89-102

[43] Huntz A M, Hou P Y, Molins R. Study by deflection of the oxygen pressure influence on the phase transformation in alumina thin films formed by oxidation of Fe₃Al [J]. Mater. Sci. Eng.,2007, 467A (1-2): 59-70

[44] Engkvist J, Canovic S, Hellstrom K, et al. Alumina scale formation on a powder metallurgical FeCrAl alloy (Kanthal APMT) at 900-1100℃ in dry O₂ and in O₂+H₂O [J].Oxid. Met., 2010, 73: 233-253

[1]	Qingpeng LI,Qian XU,Jianguo LIU,Chuanwei YAN,Liang ZHANG,Yuejun YIN,Changzhi HAN. Preparation and Performance of Water-based Chromium-free Dacromet Coating[J]. 中国腐蚀与防护学报, 2016, 36(6): 559-565.
[2]	Wenjie SUI,Wenjie ZHAO,Xing ZHANG,Liguang QIN,Shusen PENG,Xuedong WU,Qunji XUE. Influence of TEOS Content on Anti-corrosion Property of Mercapto Functional Organic Silane Based Sol-gel Coatings on Copper Alloy Surface[J]. 中国腐蚀与防护学报, 2016, 36(1): 52-58.
[3]	SONG Qin^,,WU Junwei^,,ZHANG Hui^,,DU Cuiwei. Performance of Ti-based Dimensionally Stable Anode for Chromium Plating Application[J]. 中国腐蚀与防护学报, 2013, 33(6): 507-514.
[4]	XIAO Wei, SHAN Dayong, CHEN Rongshi. EFFECT OF PROCESS OF ELECTROLESS PLATING ON INVESTMENT CASTING ZA93 MAGNESIUM ALLOY[J]. 中国腐蚀与防护学报, 2012, 32(2): 90-94.
[5]	Hui Yu; Saying Dong; Guosheng Huang. CORROSION BEHAVIOR OF Al-BRONZE IN 3.5% NaCl SOLUTION[J]. 中国腐蚀与防护学报, 2003, 23(6): 345-349 .
[6]	LI Lingchuan (Dept. of Materials Science & Engineering; Tsinghua University; Beijing 100084). CONSTRUCTION OF PHASE STABILITY DIAGRAMS OF QUATERNARY HOT CORROSION TYPE BASED ON CALCULATION OF TERNARY MIXED ENVIRONMENT TYPE[J]. 中国腐蚀与防护学报, 1997, 17(1): 58-62.
[7]	Wang Jiajun(Tsinghua University)Sun Yufang(Central Non-Reffous Research Institute)Ye Ruizeng(University of Science and Technology Beijing). THE STRUCTURE AND HIGH TEMPERATURE STABILITY OF Ti-N FILM AS A DIFFUSION BARRIER[J]. 中国腐蚀与防护学报, 1994, 14(3): 247-251.

No Suggested Reading articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed