Preparation and Corrosion Resistance of 1-Tetradecylphosphonic Acid SAMs on 430 Stainless Steel
WANG Hairen, CHEN Feng, QU Jun'e, NIE Dejian
Faculty of Materials Science and Engineering, Hubei University, Wuhan 430062, China
Download:  PDF(932KB) 
Export:  BibTeX | EndNote (RIS)      
Abstract  A kind of 1-tetradecylphosphonic acid (TDPA) SAMs was formed on 430 stainless steel by the immersion method. The adsorption behavior and pitting corrosion inhibition performance were investigated by FT-IR spectrum, electrokinetic potential scanning, contact angle measurement and X-ray photoelectron spectroscopy (XPS) observations. The results showed that after modification by TDPA molecules, the stainless steel surface changed from hydrophilicity to hydrophobicity, and the highest pitting potential was obtained after 6 h self-assembling. The oxidation could enhanced corrosion inhibition of 430SS,and the TDPA SAMs also could form on the oxidized 430SS.
Key words:  430 stainless steel      TDPA SAMs      pitting potential     
ZTFLH:  TG174.4  

Cite this article: 

WANG Hairen,CHEN Feng,QU Jun'e,NIE Dejian. Preparation and Corrosion Resistance of 1-Tetradecylphosphonic Acid SAMs on 430 Stainless Steel. Journal of Chinese Society for Corrosion and protection, 2013, 33(5): 383-387.

URL: 

https://www.jcscp.org/EN/     OR     https://www.jcscp.org/EN/Y2013/V33/I5/383

[1] Brukman M J, Oncins G, Dunbar T D, et al. Nanotribological properties of alkanephosphonic acid self-assembled monolayers on aluminum oxide: effects of fluorination and substrate crystallinity [J]. Langmuir, 2006, 22(9): 3988-3998
[2] Yu L Y, Luo H, Liu L. AFM and electro-chemical analysis of pitting corrosion of 2205 duplex stainless steel in HCl solution [J]. Corros. Prot., 2010, 31(9): 682-684
(喻兰英, 罗宏, 刘莉. 2025双相不锈钢在HCl溶液中点蚀的AFM和电化学分析 [J]. 腐蚀与防护, 2010, 31(9): 682-684)
[3] Li L Q, Jiang P G. The research on phosphating process of iron and steel at room temperature [J]. Corros. Prot., 2005, 26(7): 305-309
(李立清, 蒋平国. 钢铁常温磷化工艺研究 [J]. 腐蚀与防护, 2005, 26(7): 305-309)
[4] Yu C Y. Technology for acid cleaning and passivation of stainless steel equipment and parts [J]. Clean. World, 2004, 20(1): 20-24
(余存烨. 不锈钢设备及零部件酸洗钝化技术 [J]. 清洗世界, 2004,20(1): 20-24)
[5] Kunitsugu A, Tadashi S. An ultrathin polymer coating of carboxylate self-assembled monolayer absorbed on passivated iron to prevent iron corrosion in 0.1M Na2SO4 [J]. Corros. Sci., 2010, 52(1): 1-6
[6] Chen Z M, Lu P, Xing H Y. New technology for self-assembled film formation on aluminum surface [J]. Mater. Corros., 2011, 44(1): 58-66
(陈泽民, 路品, 邢海燕. 铝材表面的自组装成膜新工艺 [J]. 材料保护, 2011, 44(1): 58-66)
[7] Zhai Y, Zhang J L, Wang Y P, et al. Preparation and application of self-assembled monolayers [J]. Prog. Chem., 2004, 16(4): 25-29
(翟怡, 张金利, 王一平等. 自组装单层膜的制备与应用 [J]. 化学进展, 2004, 16(4): 25-29)
[8] Wang H R, Jiang Y, Qu J E, et al. Inhibitive self-assembled monolayers on surfaces of commoly-used metal and research methods [J]. J. Chin. Soc. Corros. Prot., 2012, 32(4): 273-284
(王海人, 江燕, 屈钧娥等. 常用金属表面缓蚀自组装膜及其研究方法 [J]. 中国腐蚀与防护学报, 2012, 32(4): 273-284)
[9] Nozawa K, Nishihara H, Aramaki K. Chemical modification of alkanethiol monolayers for protectioning iron against corrosion [J]. Corros. Sci., 1997, 39(9): 1625-1639
[10] Aramaki K, Shimura T. Self-assembled monolayers of carboxylate ions on passivated iron for preventing passive film breakdown [J]. Corros. Sci., 2004, 46(2): 313-328
[11] Felhosi I, Telegdi J, Palinkas G, et al. Kinetics of self-assembled layer formation on iron [J]. Elctochim. Acta, 2002, 47(13): 2335- 2340
[12] Paszternák A, Felh?si I, Pászti Z, et al. Surface analytical characterization of passive iron surface modified alkyl-phosphonic acid layers [J]. Electochim. Acta. 2010, 55(3): 804-812
[13] Cao Z M. Corrosion inhibition of ethane diamine double-2-hydroxypropane sulfonic acid [J]. Corros. Prot., 2006, 27(12): 627-628
(曹展梅. 一种含氮有机化合物的缓蚀性能及其电化学特征 [J]. 腐蚀与防护, 2006, 27(12): 627-628)
[14] Wu L. Study on synthesis of platinum nanoparticles and their self-assembled films on the surface of iron electrode [D]. Jinan: ShanDong University, 2007
(吴岭. 铂纳米粒子的制备及其在铁电极表面自组装的研究 [D]. 济南: 山东大学, 2007)
[15] Chen G, Qu J E, Liu S B, et. al. Effect of water in the solvent on the corrosion inhibition performance of TDPA SAMs on the surface of 2024 aluminum alloy [J]. Surf. Technol., 2012(2): 5-8
(陈庚, 屈均娥, 刘少波等. 溶剂中水对2024铝合金表面十四烷基膦酸自组装膜缓蚀性能的影响 [J]. 表面技术, 2012(2): 5-8)
[1] Zhanfeng Cao; Ljie Qiao; Wuyang Zhu. STUDY ON EFFECT FACTORS TO PITTING POTENTIAL OF 321 STAINLESS STEEL[J]. 中国腐蚀与防护学报, 2006, 26(1): 22-30 .
[2] FU Chaoyang; PENG Fanging; LU Zhanpeng; ZHENG Jiashen (Huazhong University of Science and Technology; Wuhan 430074). PITTING BEHAVIOUR OF TYPE 43O STAINLESS STEEL IN SOLUTIONS CONTAINING Cl~- AND CO_2[J]. 中国腐蚀与防护学报, 1996, 16(4): 311-315.
No Suggested Reading articles found!