EFFECT OF NITRIDE COATINGS ON THE CYCLIC OXIDATION BEHAVIOR OF TI6AL4V ALLOY

J Chin Soc Corr Pro

2012, Vol. 32

Issue (1): 7-12 DOI:

Current Issue | Archive | Adv Search

EFFECT OF NITRIDE COATINGS ON THE CYCLIC OXIDATION BEHAVIOR OF TI6AL4V ALLOY

CHEN Qian^1,2, XIN Li², TENG Yingyuan¹, ZHU Shenglong², WANG Fuhui²

1. Shenyang Aerospace University, School of Aerospace Engineering, Shenyang 110136
2. State Key Laboratory for Corrosion and Protection, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016

Download:

PDF(3200KB)
Export: BibTeX | EndNote (RIS)

Abstract Ti_0.5Al_0.5N/Ti_0.7Al_0.3N double-layered film and Ti_0.6Al_0.3Si_0.1N film were deposited on Ti6Al4V alloy by the arc ion plating (AIP) method. It was found that the deposition of the films of the two types significantly improved cyclic oxidation resistance of the Ti6Al4V alloy at 550℃ and 650℃, due to the formation of a thin and continuous Al₂O₃-rich scale. At 750℃, a good cyclic oxidation resistance still remained for the Ti_0.6Al_0.3Si_0.1N-coated Ti6Al4V but not for the Ti_0.5Al_0.5N/Ti_0.7Al_0.3N-coated alloy.

Key words: arc ion plating(AIP) Ti_0.5Al_0.5N/Ti_0.7Al_0.3N double-layered film TiAlSiN film Ti6Al4V alloy cyclic oxidation

Received: 21 October 2010

ZTFLH:

TG139

Corresponding Authors: CHEN Qian E-mail: cq1106@163.com

	Service

	E-mail this article
	Add to citation manager
	E-mail Alert
	RSS
	（）
	Articles by authors
	CHEN Qian

Cite this article:

CHEN Qian, XIN Li, TENG Yingyuan, ZHU Shenglong, WANG Fuhui. EFFECT OF NITRIDE COATINGS ON THE CYCLIC OXIDATION BEHAVIOR OF TI6AL4V ALLOY. J Chin Soc Corr Pro, 2012, 32(1): 7-12.

URL:

https://www.jcscp.org/EN/ OR https://www.jcscp.org/EN/Y2012/V32/I1/7

[1] Shida Y, Anada H. The influence of ternary element addition on the oxidation behavior of TiAl intermetallic compound in high-temperature air [J]. Corros. Sci., 1993, 35 (5-8): 945-953

[2] Du H L, Datta P K, Bumell-Gray J S. Effect of Nb coating on the sulphidation oxidation behavior of Ti and Ti-6Al-4V alloy [J]. J. Mater. Sci., 1995, 10(30): 2640-2647

[3] Tang Z L, Wang F H, Wu W T. Effect of a sputtered TiAlCr coating on hot corrosion resistance of gamma-TiAl [J].Intermetallics, 1999, 7: 1271-1274

[4] Leyens C, Peters M, Kaysser W A. Intermetallic Ti-Al coatings for protection of titanium alloys: oxidation and mechanical behavior [J].Surf. Coat. Technol., 1997, 94-95: 34-40

[5] Tang Z L, Wang F H, Wu W T, et al. Effect of coatings on oxidation resistance and mechanical performance of Ti60 alloy [J].Mater. Sci. Eng., 1998, A255: 133-138

[6] Liu H P, Hao S S, Wang X H, et al. Interaction of a near-α type titanium alloy with NiCrAlY protective coating at high temperatures [J]. Scr. Mater., 1998, 39: 1443-1450

[7] Zhou C G, Cai R, Gong S K, et al. Hot corrosion of AlCuFeCr quasicrystalline coating on titanium alloys with NaCl deposit [J]. Surf. Coat. Technol., 2006, A201(3-4): 1718-1723

[8] Gurappa I. Protection of titanium alloy components against high temperature corrosion [J]. Mater. Sci. Eng., 2003, A356(1-2): 372-380

[9] Xiong H P, Mao W, Ma W L, et al. Liquid-phase aluminizing and siliconizing at the surface of a Ti60 alloy and improvement in oxidation resistance [J]. Mater. Sci. Eng., 2006, A433: 108-113

[10] Xiong Y M, Zhu S L, Wang F H. The oxidation behavior and mechanical performance of Ti60 alloy with enamel coating [J]. Surf.Coat. Technol., 2005,190: 195-199

[11] Leyens C, Peters M, Hvsepian P E, et al. Novel coating systems produced by the combined cathodic arc/unbalanced magnetron sputtering for environmental protection of titanium alloys [J]. Surf. Coat. Technol., 2002, 155: 103-111

[12] Vennemann A, Stock H R, Kohlscheen J, et al. Oxidation resistance of titanium-aluminium-silicon nitride coatings[J]. Surf. Coat. Technol., 2003, 174-175: 408-415

[13] Li M S, Wang F H. Effects of nitrogen partial pressure and pulse bias voltage on (Ti,Al)N coatings by arc ion plating [J].Surf. Coat. Technol., 2003, 167: 197-202

[14] Shalev S, Boxman R L, Goldsmith S. Velocities and emission rates of cathode-produced molybdenum macroparticles in a vacuum arc [J]. J. Appl. Phys., 1985, 58(7): 2503-2507

[15] Boxman R L, Goldsmith S. Macroparticles contamination in cathodic arc coatings: generation, transport and control [J]. Surf.Coat. Technol., 1992, 52(39): 39-59

[16] Feng C J , Li M S , Xin L, et al. Mechanical properties and oxidation behavior of a graded (Ti,Al)N coating deposited by arc-ion plating [J]. Oxid. Met., 2006, 65(5/6): 307-327

[1]	Bin XIAO,Junhuai XIANG,Honghua ZHANG. Cyclic and Static Oxidation Behavior of Fe-Cu-Ni-Al Alloy at 900 ℃[J]. 中国腐蚀与防护学报, 2017, 37(1): 69-73.
[2]	. Study on High Temperature Oxidation of Al60Mn13Ti25V2 Intermetallic[J]. 中国腐蚀与防护学报, 2004, 24(3): 129-134 .
[3]	Zhongyuan Zhang; Meiheng Li; Xiaofeng Sun. CYCLIC OXIDATION BEHAVIOR OF THERMAL BARRIERCOATINGS ON SINGLE CRYSTAL SUPERALLOYS[J]. 中国腐蚀与防护学报, 2002, 22(2): 111-114 .
[4]	Fuhe Yuan; Xiaofeng Sun; Hengrong Guan. CYCLIC OXIDATION BEHAVIOR OF A COBALT-BASE SUPERALLOY[J]. 中国腐蚀与防护学报, 2002, 22(2): 115-117 .
[5]	TANG Zhao-lin WANG Fu-hui WU Wei-tao(State Key Laboratory for Corrosion and Protection; Institute of Corrosion and Protection of Metals; Young Scientists Lab of Surface Engineering; Chinese Academy of Sciences; Shenyang 110015). EFFECT OF TiAlCr COATING ON OXIDATION RESISTANCE OF TiAl INTERMETALLICS[J]. 中国腐蚀与防护学报, 1998, 18(1): 35-40.
[6]	HU Wushing; LI Tiefan; SHEN Jianian (State Key Laborutory Of Corrosion and Protection; Institute of Corrosion and Protection of Metals; Chinese Academy of Sciences; Shenyang 110015). HIGH TEMPERATURE OXIDATION OF SEVERAL Ni-Cr-Al LOW SEGREGATION SUPERXLLOYS[J]. 中国腐蚀与防护学报, 1996, 16(4): 293-297.

No Suggested Reading articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed