Study on high temperature oxidation resistance of Al-Si coating on K4104 Superalloy

J Chin Soc Corr Pro

2006, Vol. 26

Issue (6): 371-375 DOI:

Research Report

Current Issue | Archive | Adv Search

Study on high temperature oxidation resistance of Al-Si coating on K4104 Superalloy

;Haitao Liu;;

哈尔滨工程大学

Download:

PDF(394KB)
Export: BibTeX | EndNote (RIS)

Abstract The Al－Si coating on the surface of K4104 superalloy were prepared by using slurry process. Two different coating were formed by changing the CrO3 content of agglomerant. According to HB5258－2000, the high temperature performance of these coating have been investigated by high temperature oxidation test.The oxidation kinetics curve was drawn. The surface morphology of the Al－Si coating were studied by using SEM. The results indicate that the Al－Si coating on the surface of K4104 superalloy have transformed to compact oxidized film α－Al2O3 and β－NiAl compound scale in the process of high temperature oxidation and all of them have good adhesivity. The Al－Si coatings have excellent high temperature oxidation resistance.

Key words: K4104 superalloy Al－Si coating high temperature oxidation

Received: 27 June 2005

ZTFLH:

TG172.8

Corresponding Authors: Haitao Liu

	Service

	E-mail this article
	Add to citation manager
	E-mail Alert
	RSS
	（）
	Articles by authors
	Haitao Liu

Cite this article:

Haitao Liu. Study on high temperature oxidation resistance of Al-Si coating on K4104 Superalloy. J Chin Soc Corr Pro, 2006, 26(6): 371-375 .

URL:

https://www.jcscp.org/EN/ OR https://www.jcscp.org/EN/Y2006/V26/I6/371

[1]Lou H Y.Interdiffusion between high temperature coating and su-peralloy substrate[J].J.Chin.Soc.Corros.Prot.,1997,17(suppl.):464-469(楼翰一.高温合金涂层与基体界面上的互扩散[J].中国腐蚀与防护学报,1997,17(增刊):464-469)
[2]Liu P S.Status of study on high-temperature oxidation law for alu-minide coatings[J].Rare Metal Materials and Engineering,2003,32(9):681-685(刘培生.铝化物高温防护涂层的现状[J].稀有金属材料与工程,2003,32(9):681-685)
[3]Doychak J,Smialek J L,Mitchell T E.Transient oxidation of single-crystalβ-NiAl[J].Metall.Trans.A,1989,20A:499-518
[4]Schumann E.Effect of Y-ion implantation on the oxidation ofβ-NiAl[J].Oxidation of Metals,1995,43:157-172
[5]Yang Z L.High temperature performance of the Al-Si coating[J].J.Chin.Soc.Corros.Prot.,1981,1(4):28-37(杨忠林.铝-硅涂层防护性能的研究[J].中国腐蚀与防护学报,1981,1(4):28-37)
[6]Yang S W.Study on high temperature oxidation of Al-Si coating onsuperalloy[J].Trans.Mater.Heat Treatment,2004,25(1):66-68(杨世伟.高温合金Al-Si涂层抗高温氧化性能的研究[J].材料热处理学报,2004,25(1):66-68)
[7]Zhu R Z,He Y D,Qi H B.The High Temperature Corrosion andMaterials of High Temperature Corrosion Resistance[M].Shanghai:Shanghai Science&Technology Press,1993:344-348(朱日彰,何业东,齐慧滨.高温腐蚀及耐高温腐蚀材料[M].上海:上海科学技术出版社,1993:344-348)
[8]Yang Z L,Yu X F.Effect of Si distribution on hot corrosion behaviorof Al-Si coating[J].J.Aeronautical Materials,1994,14(2):38-40(杨忠林,余霞飞.硅的分布对铝-硅涂层抗热腐蚀性能的研究[J].航空材料学报,1994,14(2):38-40)

[1]	XIE Dongbai, HONG Hao, WANG Wen, PENG Xiao, DUO Shuwang. Oxidation Behavior of Stainless Steel 1Cr11Ni2W2MoV in a Simulated Kerosene Combustion Environment[J]. 中国腐蚀与防护学报, 2020, 40(4): 358-366.
[2]	XU Xunhu,HE Cuiqun,XIANG Junhuai,WANG Ling,ZHANG Honghua,ZHENG Xiaodong. High Temperature Oxidation Behavior of Co-20Re-25Cr-1Si Alloy in 0.1 MPa Pure Oxygen[J]. 中国腐蚀与防护学报, 2020, 40(1): 75-80.
[3]	AI Peng,LIU Lixiang,LI Xiaogang,JIANG Wentao. Influence of TiAlSiN Coatings on High Temperature Oxidation Resistance of γ-TiAl Based Alloys[J]. 中国腐蚀与防护学报, 2019, 39(4): 306-312.
[4]	Junjie XIA,Hongzhi NIU,Min LIU,Huazhen CAO,Guoqu ZHENG,Liankui WU. Enhancement of High Temperature Oxidation Resistance of Ti48Al5Nb Alloy via Anodic Anodization in NH₄F Containing Ethylene Glycol[J]. 中国腐蚀与防护学报, 2019, 39(2): 96-105.
[5]	Dongbai XIE,Youyu ZHOU,Jintao LU,Wen WANG,Shenglong ZHU,Fuhui WANG. Effect of Al/Si Content on Corrosion of Ni-based Alloys in Supercritical Water[J]. 中国腐蚀与防护学报, 2019, 39(1): 68-76.
[6]	Ling WANG,Junhuai XIANG,Honghua ZHANG,Songlin QIN. High Temperature Oxidation Behavior of Three Co-20Re-xCr Alloys in 3.04×10^-5 Pa Oxygen at 1000 and 1100 ℃[J]. 中国腐蚀与防护学报, 2019, 39(1): 83-88.
[7]	Dongbai XIE, Youyu ZHOU, Jintao LU, Wen WANG, Shenglong ZHU, Fuhui WANG. Effect of Cr Content on Oxidation of Ni-based Alloy in Supercritical Water[J]. 中国腐蚀与防护学报, 2018, 38(4): 358-364.
[8]	Yue LI, Jian WANG, Yong ZHANG, Jingang BAI, Yadi HU, Yongfeng QIAO, Caili ZHANG, Peide HAN. Analysis of Initial Oxidation Process of 2205 Duplex Stainless Steel in Closed Container at High Temperature[J]. 中国腐蚀与防护学报, 2018, 38(3): 296-302.
[9]	Zhan ZHAO,Jingyang LI,Jianxin DONG,Zhihao YAO,Maicang ZHANG. Oxidation Behavior during High Temperature Homo-genization Treatment of Cast Ni-Fe Based Corrosion Resistant 925 Alloy[J]. 中国腐蚀与防护学报, 2017, 37(1): 1-8.
[10]	Dongbai XIE,Guo SHAN. Rapid Identification of Liquid Accelerant in Fire Scene Environment[J]. 中国腐蚀与防护学报, 2017, 37(1): 74-80.
[11]	Tiantian YANG,Jingjun XU,Yuhai QIAN,Meishuan LI. Preparation and Ultra-high Temperature Oxidation Resistance of Micro-laminated ZrC/MoSi₂ Coating on Siliconized Graphite[J]. 中国腐蚀与防护学报, 2016, 36(5): 476-482.
[12]	Jiapeng HUANG,Bin YANG,Hang WANG. Effect of Multiple Addition of Y, La and Ce on Oxidation Behavior of Ni-10Cr-5Al Alloy at 1000 ℃ in Air[J]. 中国腐蚀与防护学报, 2016, 36(5): 489-496.
[13]	YUAN Juntao, WANG Wen, ZHU Shenglong, WANG Fuhui. Oxidation Behavior of Super 304H Steel in Steam at 700~900 ℃[J]. 中国腐蚀与防护学报, 2014, 34(3): 218-224.
[14]	YUAN Juntao,WU Ximao,WANG Wen,ZHU Shenglong,WANG Fuhui. Effect of Grain Size on Oxidation of Heat-resistant Steels in High Temperature Water Steam[J]. 中国腐蚀与防护学报, 2013, 33(4): 257-264.
[15]	FU Guangyan, YANG Ningning, WANG Yanyan. AIR OXIDATION OF Fe-Y ALLOYS AT 800℃[J]. 中国腐蚀与防护学报, 2010, 30(6): 453-456.

No Suggested Reading articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed