REVIEW OF RESEARCH ON CORROSION BEHAVIOR OF Al-Li ALLOYS

Jinfeng Li;Zhao Zhang;Jianjing Zhang

中南大学材料科学与工程学院

Cite this article:

Jinfeng Li; Zhao Zhang; Jianjing Zhang. REVIEW OF RESEARCH ON CORROSION BEHAVIOR OF Al-Li ALLOYS. J Chin Soc Corr Pro, 2003, 23(5): 316-320 .

Download:

PDF(173KB)
Export: BibTeX | EndNote (RIS)

Abstract Current research status of pitting corrosion,interg ranular corrosion,stress-corrosion cracking(SCC) and exfoliation corrosion of Al -Li alloys are reviewed in this paper.The effect of processing,heat treatment,mi crostructure and corrosion medium on the pitting and intergranular corrosion beh avior and SCC susceptibility of some Al-Li alloys are given,the correlated effec t mechanisms are described and some new test methods for Al-Li alloy exfoliation are reported.Meanwhile,the next research objective is outlined.

Key words: Al-Li alloys corrosion exfoliation

Received: 30 January 2002

ZTFLH:	TG174.3
	O646

	Service

	E-mail this article
	Add to citation manager
	E-mail Alert
	RSS
	（）
	Articles by authors
	Jinfeng Li
	Zhao Zhang
	Jianjing Zhang

URL:

https://www.jcscp.org/EN/ OR https://www.jcscp.org/EN/Y2003/V23/I5/316

[1]ZhangLingquan.Currentstatusofaluminum-lithiumalloys[J].LightAlloysFabricationTechnol.,1986,(7):23-28(张灵泉.铝-锂合金的发展现状[J].轻合金加工技术,1986,(7):23-28)
[2]XiaDeshun.Developmentandapplicationofaluminum-lithiumal loys[J].AstronavigationCraft.,1998,(1):50-54(夏德顺.铝锂合金的发展和应用[J].航天工艺,1998,(1):50-54)
[3]QiuHuizhong.Al-LialloysandtheirmanufacturingtechniquesforaerospaceproductsoutsideChina[J].AerospaceMater.Technol.,1998,(4):39-43(邱惠中.国外Al-Li合金及其航天产品的制造技术[J].宇航材料工艺,1998,(4):39-43)
[4]TianRongzhang,WangZhutang.AluminumAlloysandTheirFabri cation[M].Changsha:CentralSouthUniversityPublicationPress,2000.(田荣璋,王祝堂主编.铝合金及其加工技术[M ].长沙:中南大学出版社,2000)
[5]LiuJing’an,ZhuXianwen.Developmentandapplicationofalu minum-lithiumalloys[J].LightAlloyFabricationTechnol.,1996,24(5):2-5,10(刘静安,朱献文.Al-Li合金的发展与应用[J].轻合金加工技术,1996,24(5):2-5,10)
[6]ColvinEL ,CahhenGL ,StonerGE .EffectofgermaniumadditionsonthecorrosionbehaviorofanAl-Lialloy[J].Corrosion,1986,42(7):416-421
[7]NiskanenP ,SandersTH ,RinkerJG ,etal.Corrosionofaluminumalloyscontaininglithium[J].Corros.Sci.,1982,22(4):283-304
[8]MoranJP ,StarkeEA ,StonerGE ,etal.Theinfluenceofcomposi tionandmicrostructureonthecorrosionbehavioroftwoAlLiXal loys[J].Corrosion,1987,43(6):374-382
[9]BuchheitRG ,MoranJP ,StonerGE .Electrochemic
[21]JinkerJG ,MaraekMM ,SandersTH .Microstructures,toughnesssionofAl-2%Li-3%Cualloys[J].Corrosion,1994,50(2):120-130
[10]BuchheitRG ,MoranJP ,StonerGE .Localizedcorrosionbehaviorofalloy2090-theroleofmicrostructureheterogeneity[J].Corro sion,1990,46(8):610-617
[11]KumaiC ,KusinskiJ,ThomasG ,etal.Influenceofagingat200℃onthecorrosionresistanceofAl-LiandAl-Cu-Lialloys[J].Corrosion,1989,45(4):294-302
[12]AmbatR ,DwarakadasaES .Effectofchlorideionconcentrationduringcorrosionofmediumstrengthaluminumalloys8090,2091and2014[J].Br.Corros.J .,1993,28(2):142-148
[13]AmbatR ,DwarakadasaES .TheinfluenceofpHonthecorrosionofmediumstrengthaerospacealloys8090,2091and2014[J].Cor ros.Sci.,1992,32(5):681-690
[14]SrivastanTS ,SudarshanTS ,BobeckGE .CorrosionbehaviorofaquaternaryAl-Li-Cu-Mgalloyin3.5%NaClsolution[J].Br.Corros.J .,1990,25(1):39-45
[15]TraversoP ,BeccariaAM ,PoggiG .Corrosionbehaviorofalu minum-lithium8090-T81inseawater[J].Br.Corros.J.,1995,30(3):227-231
[16]MurthyKSN ,AmbatR ,DwarakadasaES .Theroleofmetalcationsinthecorrosionbehaviorof8090-T851alloyinapH 2.0solution[J].Corros.Sci.,1994,36(10):1765-1775
[17]MurthyKSN ,DwarakadasaES .RoleofLi+ionsincorrosionbe haviorof8090Al-LialloyandaluminuminpH 12aqueoussolu tions[J].Br.Corros.J.,1995,30(2):111-115
[18]MarsacS ,MankowskiG ,DabosiF .Stresscorrosioncrackingbe haviorof2091Al-Lialloyinsulphateandchloridecontainingso lutions[J].Br.Corros.J.,1992,27(1):50-58
[19]BurleighTD .Thepostulatedmechanismsofstresscorrosioncrackingofaluminumalloys,areviewoftheliterature1980-1989[J].Corrosion,1991,47(2):89-98
[20]DorawrdRC ,HasseKR .StresscorrosioncharacteristicsofAlCuLiAA2090alloy[J].Corrosion,1988,44(12):932-941
[21]JinkerJG ,MaraekMM ,SandersTH .Microstructures,toughnessandstresscorrosioncrackingbehaviorofaluminumalloy2020[J].Mater.Sci.Eng.,1984,64:203-221
[22]MeletisEI.Microstructureandstresscorrosioncrackingrelation shipinanAl-Li-Cu-Zralloy[J].Mater.Sci.Eng.,1987,93:235-245
[23]LumsdenJB ,AllenAT .ThestresscorrosioncrackingofAlLial loy8090[J].Corros.Sci.,1988,44(4):527-532
[24]DorwardRC .InfluenceofgrainstructureonstresscorrosioncrackingandtensilepropertiesofAl-2Li-2Cu-1.5Mgalloysheet[J].Corrosion,1990,46(4):348-352
[25]BuisA ,SchijveJ.StresscorrosioncrackingbehaviorofAl-Li2090-T83alloyinartificialseawater[J].Corrosion,1992,48(11):898-909
[26]CondeA ,FernandezBJ,DamboreneaJJde.CharacterizationoftheSCCbehaviorof8090Al-Lialloybymeansoftheslow-strain-ratetechnique[J].Corros.Sci.,1998,40(1):91-102
[27]LiDi,ZuoShangzhi,GuoBaolan.StudyontheexfoliationcorrosionofLY12alloy[J].J .Chin.Soc.Corros.Prot.,1995,15(3):203-208(李荻,左尚志,郭宝兰.LY12铝合金剥蚀行为的研究[J].中国腐蚀与防护学报,1995,15(3):203-208)
[28]ZhengZiqiao.Processingofthe2 ndNationalAluminum-Lithiumalloys[C].Changsha:CentralSouthUniversityofTechnologyPub licationPress,1993(郑子樵主编.第二届全国铝锂合金会议论文集[C].长沙:中南工业大学出版社,1993)
[29]Standardtestmethodforexfoliationcorrosionsusceptibilityin2×××and7×××seriesaluminumalloys(EXCOTest)[S].ASTM 34-79.
[30]KellyDJ,RobinsonMJ.InfluenceofheattreatmentandgrainshapeonexfoliationcorrosionofAl-Lialloy8090[J].Corrosion,1993,49(10):787-795
[31]HabashiM ,BonteE ,GallandJ ,etal.Quantitativemeasurementsofthedegreeofexfoliationonaluminumalloys[J].Corros.Sci.,1993,35(4):168-183
[32]CondeA ,DamboneaJde.Electrochemicalmodellingofexfoliationcorrosionbehaviorof8090alloy[J].Electrochimi.Acta,1998,43(8):849-860

[1]	LI Min, WEI Gaofei, DENG Shuduan, LI Xianghong. Progress and Prospects of Scanning Electrochemical Microscope (SECM) in Corrosion Inhibitor Research[J]. 中国腐蚀与防护学报, 2026, 46(5): 1326-1342.
[2]	XIE Jingli, WANG Youzhi, QIAO Shuzhen, NIU Jiayu, HAO Long, CAO Shengfei, WANG Jianqiu. Recent Advances in Evolution of Carbon Steel Corrosion Products in Near-field Environment of Geological Repositories for High-level Radioactive Waste[J]. 中国腐蚀与防护学报, 2026, 46(5): 1343-1352.
[3]	ZHOU Shuyu, LIU Changpu, YANG Liuyang, GENG Jie, FAN Haiming, ZHANG Dalei, JU Hong. Research Progress on Corrosion Mechanism and Protection Technology of Pipeline Steel Under Combined lnfluence of Supercritical CO₂ Conditions and Typical Environmental Factors[J]. 中国腐蚀与防护学报, 2026, 46(5): 1353-1368.
[4]	HUANG Hui, LI Shuli, DENG Shuduan, LI Xianghong. Research Progress and Prospects of Smart Materials for Protective Coatings[J]. 中国腐蚀与防护学报, 2026, 46(5): 1369-1388.
[5]	ZENG Qi, YU Wenjun, MEN Xiangnan, FENG Baojing, YANG Yao, ZHU Kai, GE Yulin, YING Tao, ZENG Xiaoqin. Recent Research Progress of Rare-earth Mg-alloys with High Strength and Corrosion Resistance[J]. 中国腐蚀与防护学报, 2026, 46(5): 1415-1424.
[6]	ZHANG Qiang, LU Yiliang, JIN Yan, CHEN Yun, YANG Bingkun, WANG Xiaofang, HAN Yu. Research Progress on Environmental Corrosion Classification and Mapping Technologies for Atmospheric/Surface Soil Corrosion[J]. 中国腐蚀与防护学报, 2026, 46(5): 1425-1436.
[7]	XU Jiacheng, LIU Jiabing, HUANG Shiyu, JIN Linghao, TAN Wei, GUO Na, LIU Tao. Mechanical Property Damage and Stress Corrosion Behavior of EH40 Steel Ship Plate in Artificial Polar Marine Environments[J]. 中国腐蚀与防护学报, 2026, 46(5): 1437-1451.
[8]	ZHENG Kai, WANG Yitao, WANG Dongsheng, LIU Wei, JIANG Yingchang, HUANG Rong, CHANG Xueting. Influence of Corrosion-stress Coupling Effect on Corrosion and Failure of Low-carbon Martensitic Stainless Steel for Polar Marine Propellers[J]. 中国腐蚀与防护学报, 2026, 46(5): 1452-1462.
[9]	ZHANG Chunyan, ZHANG Yuxin, CHEN Bixiu, YU Baoxing, ZHOU Peng. Effect of Shrinkage Cavities of Cast AZ91D Mg-alloy on Corrosion Resistance of Its Chemical Conversion Coating Prepared with Permanganate-phosphate[J]. 中国腐蚀与防护学报, 2026, 46(5): 1475-1484.
[10]	TANG Min, DU Pengfei, XU Juan, LEI Ran, LI Xingxin, LI Xianghong. *Corrosion Inhibition Effect and Mechanism of Invasive Species Bidens pilosa* L. Extract on ST12 Steel in H₂SO₄ Medium**[J]. 中国腐蚀与防护学报, 2026, 46(5): 1485-1496.
[11]	QI Xiaohan, ZHAI Haimin, LI Wensheng, HONG Hao, CAO Yuan, YU Lei, CHEN Bohan. Influence of Adding Nano-Al₂O₃ to Wet Enamel Frit Powder Slurry on Microstructure and Corrosion Resistance Enamel Coatings Applied on Al-alloy[J]. 中国腐蚀与防护学报, 2026, 46(5): 1497-1507.
[12]	JIA Mengyao, ZHANG Weiqiang, WANG Yuan, TAN Jibo, QIU Jianke, HAO Yantian, WU Xinqiang. Effect of Pressure Variation on Stress Corrosion Behavior of Ti80 Alloy in 3.5%NaCl Solution[J]. 中国腐蚀与防护学报, 2026, 46(5): 1508-1516.
[13]	LI Xiaofeng, LI Yanru, LU Yunfei, ZHANG Taihua, CHANG Xueting, AN Yan. Polypyrrole-modified Aramid Fiber/Epoxy Composite Coating with Synergistically Enhanced Mechanical and Anti-corrosion Properties[J]. 中国腐蚀与防护学报, 2026, 46(5): 1517-1526.
[14]	CAO Tianhui, YANG Yanqi, LIU Yuwei, WU Lei, GUO Quanzhong, JIA Zhigang, CAO Gongwang, WANG Chuan. Corrosion Behavior of 23MnNiMoCr54 Steel in Artificial High-mineralized Mine Waters of Different pH Values[J]. 中国腐蚀与防护学报, 2026, 46(5): 1537-1548.
[15]	ZHAO Xianrui, DAI Zhongguo, LI Zhanjiang, XU Yulang, ZHANG Huixia, LI Wang. Effect of Adding Y and Hf on Corrosion Behavior of AlCoCrFeNi High-entropy Alloy Coatings in NaCl Solution[J]. 中国腐蚀与防护学报, 2026, 46(5): 1549-1559.

No Suggested Reading articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed