DEPOSITION OF ALUMINIUM-CHROMIUM ALLOYCOATING BY ELECTRON BEAM EVAPORATION PLATING
Cui Lin;Nan Du;Xiaogang Li
北京科技大学材料科学与工程学院腐蚀与防护中心;北京市腐蚀、磨蚀与 表面技术重点实验室
Download:  PDF(193KB) 
Export:  BibTeX | EndNote (RIS)      
Abstract  In this present paper,the operation technology for preparation of aluminium-chromium alloy coating by electron beam evaporation pla ting was studied.Corrosion resistance of the coatings was investigated,meanwhile the phase,morphology and the effect of heat treatment on the diffusion between the Al-Cr coating and the matrix were discussed.The analysis of ingredients of t he coating and the target shows that the chromium contents of the coating are ve ry different from that of the target.It is proved that Al-Cr alloy coating of th e chromium contents of 1.5%~5% can be regarded as the anodic coatings for norma l steel matrix,which accordingly has good electrochemical protection function i n 283K,30 g/L NaCl solution.The major phases of the coating are Al and a small q uality of Cr9Al17.Cr9Al17 in the coating increases with the Cr c ontent of the target.The deposited coating takes on the orientation.After 600℃, 1 h heat treatment,ingredients of the coating and matrix diffuse each other.
Key words:  electron beam evaporation plating      Al-Cr alloy coating      corrosion resistance      
Received:  04 March 2002     
ZTFLH:  TG174  
Corresponding Authors:  Cui Lin   

Cite this article: 

Cui Lin; Nan Du; Xiaogang Li. DEPOSITION OF ALUMINIUM-CHROMIUM ALLOYCOATING BY ELECTRON BEAM EVAPORATION PLATING. J Chin Soc Corr Pro, 2003, 23(5): 257-261 .

URL: 

https://www.jcscp.org/EN/     OR     https://www.jcscp.org/EN/Y2003/V23/I5/257

[1]MondolfLF .TheStructureandFunctionofAluminumAlloy[M].Beijing:MetallurgyIndustryPress,1988(L .F蒙多尔福著.铝合金的组织与性能[M ].北京:冶金工业出版社,1988)
[2]SanchetteF .Structure-propertiesrelationshipofmetastableAl-CrandAl-Tialloysdepositedbyr.f.magnetronsputtering:roleofnitrogen[J].Surf.Coat.Technol.,1995,74/75(1-3):903
[3]SanchetteF .Depositionofmetastablealuminium-chromiumalloysbyr.f.magnetronsputteringfrommixed-powdertargets[J].Surf.Coat.Technol.,1993,57(2-3):179-182
[4]SanchetteF .Mechanicallyreinforcedandcorrosion-resistantsputteredamorphousaluminiumalloycoatings[J].Surf.Coat.Tech nol.,1998,98(1/3):1162-1168
[5]LuYanping,YuFuzhou.InfiltrationPlating[M ].Beijing:Machin eryIndustryPress,1985(卢燕平,于福州合编.渗镀[M ].北京:机械工业出版社,1985)
[6]ZhangYaming,etal.Theeffectofcalorizationonanti-oxidationathightemperatureoftitaniumalloy[J].J .Chin.Soc.Corros.Prot.,1997,5(supplement):502-507(张亚明等.渗铝对钛合金抗高温氧化性能的影响[J].中国腐蚀与防护学报,1997,5(增刊):502-507)
[7]ZhuRizhang,etal.CorrosionofMetal[M ].Beijing:MetallurgyIn dustyPress,1989(朱日彰等编.金属腐蚀学[M ].北京:冶金工业出版社,1989)
[8]CaoTieliang,etal.Thediscussiononsomeproblemsofaluminumanditsmodifiedcoatings.thenewdevelopmentofcorrosionscienceandcorrosionresistanceengineeringtechnology[A].TheSympo siumonEstablishment20-yearofChineseCorrosionandProtec tion[C].Beijing:ChemicalIndustryPress,1999(曹铁梁等.铝及其改性保护层中某些问题的探讨.腐蚀科学与防腐蚀工程技术新进展[A].中国腐蚀与防护成立20周年学术论文集[C].北京:化学工业出版社,1999)
[9]LiMeiheng,SunXiaofeng,etal.OxidationandphasestructureofthebondcoatinEB -PVDthermalbarriercoatingsduringthermalcycling[J].ActaMetall.Sin.,2002,38(1):79-83(李美,孙晓峰等.EB -PVD热障涂层热循环过程中粘结层的氧化和相结构[J].金属学报,2002,38(1):79-83)
[1] Yafei Kuang. Correlation of Corrosion Protection of Porous Membrane on Metal Surface with Electrolytes in Solution[J]. 中国腐蚀与防护学报, 2000, 20(2): 118-122 .
No Suggested Reading articles found!