THE SYNERGETIC EFFECT OF NaCl AND WATER VAPORON THE CORROSION BEHAVIOR OF K38G ALLOYAND ITS NANOCRYSTALLINE COATING AT 600℃-700℃

J Chin Soc Corr Pro

2003, Vol. 23

Issue (4): 193-197 DOI:

Research Report

Current Issue | Archive | Adv Search

THE SYNERGETIC EFFECT OF NaCl AND WATER VAPORON THE CORROSION BEHAVIOR OF K38G ALLOYAND ITS NANOCRYSTALLINE COATING AT 600℃-700℃

Shujiang Geng;Shenglong Zhu;Fuhui Wang

中科院金属所;金属腐蚀与防护国家重点实验室

Download:

PDF(192KB)
Export: BibTeX | EndNote (RIS)

Abstract The sputtered nanocrystalline coating of K38G alloy was obtained by means of magnetron sputtering.The corrosion behavior of cast K3 8G alloy and its sputtered nanocrystalline coating with a solid NaCl deposit in dry air or in wet oxygen at 600℃～700℃ was studied.The results indicated that the mass gain of the coating was higher than that of the cast alloy.Nanocrystall ization reduced corrosion resistance of the K38G alloy.The relevant corrosion me chanisms were discussed.

Key words: K38G sputtered nanocrystalline coating NaCl water vapo r corrosion

Received: 26 November 2001

ZTFLH:

TG174.4

Corresponding Authors: Shujiang Geng

	Service

	E-mail this article
	Add to citation manager
	E-mail Alert
	RSS
	（）
	Articles by authors
	Shujiang Geng
	Shenglong Zhu
	Fuhui Wang

Cite this article:

Shujiang Geng; Shenglong Zhu; Fuhui Wang. THE SYNERGETIC EFFECT OF NaCl AND WATER VAPORON THE CORROSION BEHAVIOR OF K38G ALLOYAND ITS NANOCRYSTALLINE COATING AT 600℃-700℃. J Chin Soc Corr Pro, 2003, 23(4): 193-197 .

URL:

https://www.jcscp.org/EN/ OR https://www.jcscp.org/EN/Y2003/V23/I4/193

[1]HossainMK ,SaundersSRJ .Conf.HighTemperatureAlloysGasTurbines,1978:239
[2]ShinataY ,TakahashiF ,HashiuraK .NaCl-inducedhotcorrosionofstainlesssteels[J].Mater.Sci.Eng.,1987,87:399
[3]ShuY ,WangF ,WuW .CorrosionbehaviorofpureCrwithasolidNaCldepositinO2 pluswatervapor[J].Oxid.Met.,2000,54:457
[4]ShuY ,WangF ,WuW .SynergeticeffectofNaClandwatervaporonthecorrosionofTi60alloyat500～700℃[J].Oxid.Met.,1999,52:463
[5]ShuY ,WangF ,WuW .SynergeticeffectofNaClandwatervaporonthecorrosionof1Cr11Ni2W 2MoVsteelat500～700℃[J].Ox id.Met.,1998,51:97
[6]LouH ,WangF ,XiaB ,ZhangL .High-temperatureoxidationre sistanceofsputteredmicro-grainsuperalloyK38G [J].Oxid.Met.,1992,38:299
[7]LouH ,WangF ,ZhuS ,XiaB ,ZhangL .OxideformationofK38Gsuperalloyanditssputteredmicrograinedcoating[J].Surf.Coat.Tech.,1994,63:105
[8]WangF .TheeffectofnanocrystallizationontheselectiveoxidationandadhesionofAl2O3 scales[J].Oxid.Met.,1997,48:215
[9]WangF ,YoungDJ .EffectofnanocrystallizationonthecorrosionresistanceofK38GsuperalloyinCO +CO2 atmospheres[J].Oxid.Met.,1997,48:497
[10]GengS ,WangF ,ZhuS ,WuW .Hotcorrosionresistanceofasput teredK38Gnanocrystallinecoatinginmoltensulfateat900℃[J].Oxid.Met.,(accepted)
[11]HiramatsuN ,UematsuY ,TanakaT ,KinugasaM .Effectsofalloy ingelementsonNaCl-inducedhotcorrosionofstainlesssteel[J].Mater.Sci.Eng.,1989,A120:3190

[1]	ZHENG Li, WANG Meiting, YU Baoyi. Research Progress of Cold Spraying Coating Technology for Mg-alloy[J]. 中国腐蚀与防护学报, 2021, 41(1): 22-28.
[2]	WEI Zheng, MA Baoji, LI Long, LIU Xiaofeng, LI Hui. Effect of Ultrasonic Rolling Pretreatment on Corrosion Resistance of Micro-arc Oxidation Coating of Mg-alloy[J]. 中国腐蚀与防护学报, 2021, 41(1): 117-124.
[3]	YU Hongfei, SHAO Bo, ZHANG Yue, YANG Yange. Preparation and Properties of Zr-based Conversion Coating on 2A12 Al-alloy[J]. 中国腐蚀与防护学报, 2021, 41(1): 101-109.
[4]	HUANG Peng, GAO Rongjie, LIU Wenbin, YIN Xubao. Fabrication of Superamphiphobic Surface for Nickel-plate on Pipeline Steel by Salt Solution Etching and Its Anti-corrosion Properties[J]. 中国腐蚀与防护学报, 2021, 41(1): 96-100.
[5]	DONG Xucheng, GUAN Fang, XU Liting, DUAN Jizhou, HOU Baorong. Progress on the Corrosion Mechanism of Sulfate-reducing Bacteria in Marine Environment on Metal Materials[J]. 中国腐蚀与防护学报, 2021, 41(1): 1-12.
[6]	TANG Rongmao, ZHU Yichen, LIU Guangming, LIU Yongqiang, LIU Xin, PEI Feng. Gray Correlative Degree Analysis of Q235 Steel/conductive Concrete Corrosion in Three Typical Soil Environments[J]. 中国腐蚀与防护学报, 2021, 41(1): 110-116.
[7]	HAN Yuetong, ZHANG Pengchao, SHI Jiefu, LI Ting, SUN Juncai. Surface Modification of TA1 Bipolar Plate for Proton Exchange Membrane Fuel Cell[J]. 中国腐蚀与防护学报, 2021, 41(1): 125-130.
[8]	ZHANG Yuxuan, CHEN Cuiying, LIU Hongwei, LI Weihua. Research Progress on Mildew Induced Corrosion of Al-alloy[J]. 中国腐蚀与防护学报, 2021, 41(1): 13-21.
[9]	RAN Dou, MENG Huimin, LIU Xing, LI Quande, GONG Xiufang, NI Rong, JIANG Ying, GONG Xianlong, DAI Jun, LONG Bin. Effect of pH on Corrosion Behavior of 14Cr12Ni3WMoV Stainless Steel in Chlorine-containing Solutions[J]. 中国腐蚀与防护学报, 2021, 41(1): 51-59.
[10]	BAI Yunlong, SHEN Guoliang, QIN Qingyu, WEI Boxin, YU Changkun, XU Jin, SUN Cheng. Effect of Thiourea Imidazoline Quaternary Ammonium Salt Corrosion Inhibitor on Corrosion of X80 Pipeline Steel[J]. 中国腐蚀与防护学报, 2021, 41(1): 60-70.
[11]	ZUO Yong, CAO Mingpeng, SHEN Miao, YANG Xinmei. Effect of Mg on Corrosion of 316H Stainless Steel in Molten Salts MgCl₂-NaCl-KCl[J]. 中国腐蚀与防护学报, 2021, 41(1): 80-86.
[12]	WANG Yating, WANG Kexu, GAO Pengxiang, LIU Ran, ZHAO Dishun, ZHAI Jianhua, QU Guanwei. Inhibition for Zn Corrosion by Starch Grafted Copolymer[J]. 中国腐蚀与防护学报, 2021, 41(1): 131-138.
[13]	WANG Xintong, CHEN Xu, HAN Zhenze, LI Chengyuan, WANG Qishan. Stress Corrosion Cracking Behavior of 2205 Duplex Stainless Steel in 3.5%NaCl Solution with Sulfate Reducing Bacteria[J]. 中国腐蚀与防护学报, 2021, 41(1): 43-50.
[14]	SHI Kunyu, WU Weijin, ZHANG Yi, WAN Yi, YU Chuanhao. Electrochemical Properties of Nb Coating on TC4 Substrate in Simulated Body Solution[J]. 中国腐蚀与防护学报, 2021, 41(1): 71-79.
[15]	ZHANG Hao, DU Nan, ZHOU Wenjie, WANG Shuaixing, ZHAO Qing. Effect of Fe³⁺ on Pitting Corrosion of Stainless Steel in Simulated Seawater[J]. 中国腐蚀与防护学报, 2020, 40(6): 517-522.

No Suggested Reading articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed