EFFECT OF MAGNETIC FIELD AND Cl~- ON ANODIC POLARIZATION BEHAVIOR OF IRON IN NEUTRAL 0.5mol/LNa_2SO_4 SOLUTION
LU Zhanpeng CHEN Junming (Shanghai Institute of Metallurgy; Chinese Academy of Sciences)
Download:  PDF(444KB) 
Export:  BibTeX | EndNote (RIS)      
Abstract  The effect of magnetic feild and Cl- on anodic polarization behavior of iron in neutral 0.5mol/L Na2so4 solution was studied using potentiodynamic method. It was shown that iron in Na2SO4+Cl-solution exhibited active- passive-transpassive characteristics in the presence or absence of magnetic field, although Cl- in the solution would hinder the formation of passive layer. The applied magnetic field would cause shift of passivation potential Ep and flade potential EF towards noble direction, increase the critical current density for passivation imax and the passive current density imin, and narrow the passive region. A synergistic effect of imposed magnetic field and Cl- on breakdown of the passive layer was reported.
Key words:  Fe/Na2SO4 corrosion      Effect of magnetic field      Effect of Cl-     
Received:  25 February 1997     
Service
E-mail this article
Add to citation manager
E-mail Alert
RSS
Articles by authors

Cite this article: 

LU Zhanpeng CHEN Junming (Shanghai Institute of Metallurgy; Chinese Academy of Sciences). EFFECT OF MAGNETIC FIELD AND Cl~- ON ANODIC POLARIZATION BEHAVIOR OF IRON IN NEUTRAL 0.5mol/LNa_2SO_4 SOLUTION. J Chin Soc Corr Pro, 1997, 17(1): 25-30.

URL: 

https://www.jcscp.org/EN/     OR     https://www.jcscp.org/EN/Y1997/V17/I1/25

1 Ghabashy M A. Anti-Corrosion, 1988, 35(1): 12
2 吕战鹏,陈俊明.中国腐蚀与防护学报,1996, 16(2): 115
3 Bockris J O'M, Drazic O, Despric A R. Electrochimica Acta, 1961, 4:325
4 Epelboin I, Keddam M. Electrochimica Acta, 1972, 17:177
5 Brusic V. In: Brubaker G R, Phipps P. ed. Corrosion Chemistry, Washington, D. C.: ACS,1979. Ch.6
6 Lorentz W J. Corros. Sci., 1965, 5:121
7 Evans U R. The Corrosion and Oxidation of Metals. London, Edward Arnold Ltd. 1960, p230
8 宋光铃,曹楚南,高卫红,李瑛,陈慎豪.中国腐蚀与防护学报,1994, 14(3): 175
9 曹楚南,王佳,林海潮.中国腐蚀与防护学报,1989, 9(4): 261
10 Aaboubi O, Chopart J P, Donglade J, Olivier A, etal. J Electrochem. Soc., 1990, 137:1796
[1] CHEN Jun-ming LU Zhan-peng (Shanghai Institute of Metallurgy; Chinese Academy of Science; Shanghai 200050). ANODIC POLARIZATION BEHAVIOR OF Fe/Na_2SO_4 SYSTEM IN THE PRESENCE OF MAGNETIC FIELD AND ADDITIONAL IONS[J]. 中国腐蚀与防护学报, 1998, 18(2): 119-125.
[2] CHEN Junming LU Zhanpeng (Shanghai Institute of Metallurgy; Chinese Academy of Sciences). INSTANTANEOUS AND MEMORIAL CHARACTERISTICS OF THE EFFECT OF MAGNETIC FIELD ON POLARIZATIONBEHAVIOR OF IRON[J]. 中国腐蚀与防护学报, 1997, 17(4): 276-280.
[3] Lu Zhanpeng;Chen Junming. THE EFFECT OF MAGNETIC FIELD AND FERRIC IONS ON CATHODIC POLARIZATION BEHAVIOR OF IRON IN 0.5mol/L H_2SO_4 SOLUTION[J]. 中国腐蚀与防护学报, 1996, 16(1): 37-41.
[4] Lu Zhanpeng;Chen Junming(Shanghai Institute of Metallurgy; Chineae Academy of Sciences). EFFECTS OF TEMPERATURE AND ACID CONCENTRATION ON MAGNETIC-INDUCED HYDROGEN EVOLUTION OVERPOTENTIAL OF IRON IN HYDROCHLORIC ACID SOLUTIONS[J]. 中国腐蚀与防护学报, 1995, 15(4): 303-307.
No Suggested Reading articles found!