AN INVESTIGATION ON ATMOSPHERIC CORROSIVENESS IN HAINAN PROVINCE

WANG Zhenyao; CHEN Hongchuan; YU Guocai (Institute of Corrosion and Protection of Metals; Chinese Academy of Sciences)DING Songnian; LIU Fuzhong (Hainan Meteorological Bureau)

Download:

PDF(367KB)
Export: BibTeX | EndNote (RIS)

Abstract According to the results of 2-4 years' exposure tests of carbon steel samples in Hainan Province, the influences of meteorological factors and Cl- on atmospheric corrosion were investigated. The feature of atmospheric corrosion in this area was summarized. A corrosivity map for the province was drawn. The corrosion products on carbon steel at some typical places were analyzed by XRD and XPS.

Key words: Atmospheric corrosion Carbon steel Environmental factor Product analyses

Received: 25 June 1996

	Service

	E-mail this article
	Add to citation manager
	E-mail Alert
	RSS
	（）
	Articles by authors

Cite this article:

WANG Zhenyao; CHEN Hongchuan; YU Guocai (Institute of Corrosion and Protection of Metals; Chinese Academy of Sciences)DING Songnian; LIU Fuzhong (Hainan Meteorological Bureau). AN INVESTIGATION ON ATMOSPHERIC CORROSIVENESS IN HAINAN PROVINCE. J Chin Soc Corr Pro, 1996, 16(3): 225-229.

URL:

https://www.jcscp.org/EN/ OR https://www.jcscp.org/EN/Y1996/V16/I3/225

1KingCA,MartinKG．MoresyJF．ADetailedCorrosivitySurve．ofMelbourne．PrintedbyBuildResearchMelbourne,19822高素华．海南岛气候．北京:气象出版社,1988．3ISO9223,CorrosionofMetalsandalloys-ClassificationofCorrosivityofAtmospheres

[1]	ZHANG Chen, LU Yuan, ZHAO Jingmao. Synergistic Inhibition Effect of Imidazoline Ammonium Salt and Three Cationic Surfactants in H₂S/CO₂ Brine Solution[J]. 中国腐蚀与防护学报, 2020, 40(3): 237-243.
[2]	FAN Yi,CHEN Linheng,CAI Jiaxing,DAi Qinqin,MA Hongchi,CHENG Xuequn. Corrosion Behavior of Hot-rolled AH36 Plate in Indoor Storage Environment[J]. 中国腐蚀与防护学报, 2020, 40(1): 10-16.
[3]	PAN Chengcheng,MA Chao,XIA Dahai. Estimation for Relevance of Atmospheric Corrosion Initiation with Surface Texture of Several Metallic Materials by Electron Backscattering Diffraction[J]. 中国腐蚀与防护学报, 2019, 39(6): 495-503.
[4]	ZHAO Jinbin,ZHAO Qiyue,CHEN Linheng,HUANG Yunhua,CHENG Xuequn,LI Xiaogang. Effect of Different Surface Treatments on Corrosion Behavior of 300M Steel in Qingdao Marine Atmosphere[J]. 中国腐蚀与防护学报, 2019, 39(6): 504-510.
[5]	DENG Junhao,HU Jiezhen,DENG Peichang,WANG Gui,WU Jingquan,WANG Kun. Effect of Oxide Scales on Initial Corrosion Behavior of SPHC Hot Rolled Steel in Tropical Marine Atmosphere[J]. 中国腐蚀与防护学报, 2019, 39(4): 331-337.
[6]	Yongwei SUN,Yuping ZHONG,Lingshui WANG,Fangxiong FAN,Yatao CHEN. Corrosion Behavior of Low-alloy High Strength Steels in a Simulated Common SO₂-containing Atmosphere[J]. 中国腐蚀与防护学报, 2019, 39(3): 274-280.
[7]	Ping XU,Shuo ZHANG,Shuai SI,Yajun ZHANG,Changzheng WANG. Corrosion Mechanism of Carbon Steel Induced by Protein and Polysaccharide-the Main Components of EPS[J]. 中国腐蚀与防护学报, 2019, 39(2): 176-184.
[8]	Xiankang ZHONG,Junying HU. Corrosion Behavior of X65 Carbon Steel in CO₂Containing Liquids with Constant pH and Ferrous Ion Concentration[J]. 中国腐蚀与防护学报, 2018, 38(6): 573-578.
[9]	Li WANG, Chunyun GUO, Kui XIAO, Tuerxun·Silayiding, Chaofang DONG, Xiaogang LI. Corrosion Behavior of Carbon Steels Q235 and Q450 in Dry Hot Atmosphere at Turpan District for Four Years[J]. 中国腐蚀与防护学报, 2018, 38(5): 431-437.
[10]	Yue QIAO, Zhiping ZHU, Lei YANG, Zhifeng LIU. Monitoring and Simulated Experiments of Oxidation-Reduction Potential of Boiler Feedwater at High Temperatures[J]. 中国腐蚀与防护学报, 2018, 38(5): 487-494.
[11]	Wanjun PENG, Jiheng DING, Hao CHEN, Haibin YU. Corrosion Inhibition of Bio-based Inhibitor Furfuryl Glycidyl Ether[J]. 中国腐蚀与防护学报, 2018, 38(3): 303-308.
[12]	Guofu OU, Lulu ZHAO, Kai WANG, Kuanxin WANG, Haozhe JIN. Dew-Point Corrosion Behavior of 10^# Carbon Steel inHCl-H₂O Environment[J]. 中国腐蚀与防护学报, 2018, 38(1): 33-38.
[13]	Jie ZHANG, Xiuhua HU, Chuanbo ZHENG, Jizhou DUAN, Baorong HOU. Influence of Calcareous Deposit on Corrosion Behavior of Q235 Carbon Steel in Marine Microalgae Containing Medium[J]. 中国腐蚀与防护学报, 2018, 38(1): 18-25.
[14]	Jun WANG, Chao FENG, Bicao PENG, Yi XIE, Minghua ZHANG, Tangqing WU. Corrosion Behavior of Weld Joint of S450EW Steel in NaHSO₃ Solution[J]. 中国腐蚀与防护学报, 2017, 37(6): 575-582.
[15]	Xinxin ZHANG,Zhiming GAO,Wenbin HU,Zhipeng WU,Lianheng HAN,Lihua LU,Yan XIU,Dahai XIA. Correlation Between Corrosion Behavior and Image Information of Q235 Steel Beneath Thin Electrolyte Film[J]. 中国腐蚀与防护学报, 2017, 37(5): 444-450.

No Suggested Reading articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed