EVXLUTION OF STRESS CORROSION CRACKING THRESHOLD PARAMETER δ_(SCC) WITH CONSTANT-LOAD MULTI-SPECIMENS
Qiu Dihua; Wang Zhenda;Zhang Yiliang and Yao Ximeng(Beijing Polytechnic University)
Download:  PDF(288KB) 
Export:  BibTeX | EndNote (RIS)      
Received:  25 February 1994     
Service
E-mail this article
Add to citation manager
E-mail Alert
RSS
Articles by authors

Cite this article: 

Qiu Dihua; Wang Zhenda;Zhang Yiliang and Yao Ximeng(Beijing Polytechnic University). EVXLUTION OF STRESS CORROSION CRACKING THRESHOLD PARAMETER δ_(SCC) WITH CONSTANT-LOAD MULTI-SPECIMENS. J Chin Soc Corr Pro, 1994, 14(1): 73-76.

URL: 

https://www.jcscp.org/EN/     OR     https://www.jcscp.org/EN/Y1994/V14/I1/73

[1]Brown,B.F,MaterlialsResearchandStandards;6(3),120(1966)[2]Novak,S.R.andRolfe,ST,JournaofMaterials;JMLSA;4(3);710(1969)[3]王宽福,化工机械,2,24(1983)[4]姚希梦,中国腐蚀与防护学报,5(3),222(1985)[5]Kumar,A.N.andPandey,R.K,EngineeringFractureMechanics,22(4),625(1985)[6]高镇同编著,疲劳应用统计学,国防工业出版社,1986[7]中华人民共和国国家标准,裂纹张开位移(COD)试验方法(GB2358-80),1981,
No related articles found!
No Suggested Reading articles found!