| STRESS CORROSION CRACKING OF A HIGH STRENGTH PRESTRESSING STEEL WIRE IN SATURATED Ca(OH)_2+NaCl SOLUTIONS |
| Qiu Mingshi Wen Lichang Lü Huibing Din Yunlong Chou Chunrong and Li Guofang(Shanghai Institute of Metallurgy; Academia Sinica) |
|
|
|
|
Abstract The SCC behavior of a high strength prestressing steel wire in saturated Ca(OH)_2+NaCl solutions and the effects of various factors including concentration of NaCl, potentials, pH values of solution and other additives were studied by cantilever beam test or slow strain rate test.The results showed that the presence of NaCl or Na_2SO_4 in saturate Ca(OH)_2 solution promoted SCC of the steel wire. The susceptibility to SCC increased with the increase of NaCl concentration and with the decrease of pH values of solution. The addition of NaNO_2 in solution effectively prevented the deleterious action of chloride ions,Based on the effect of potentials on SCC behavior of steel wire and the pH value of solution in an occluded cell which simulated the conditions of crack tip, it is thought that the SCC of prestressing steel wire in saturated Ca(OH)_2+NaCl solutions at free potential is mainly controlled by anodic dissolution mechanism. The effects of the spectrum of loading on threshold stress intensity factor are discussed in the light of the action of strain rate at the crack tip.
|
|
Received: 25 April 1983
|
Cite this article:
Qiu Mingshi Wen Lichang Lü Huibing Din Yunlong Chou Chunrong and Li Guofang(Shanghai Institute of Metallurgy; Academia Sinica). STRESS CORROSION CRACKING OF A HIGH STRENGTH PRESTRESSING STEEL WIRE IN SATURATED Ca(OH)_2+NaCl SOLUTIONS. J Chin Soc Corr Pro, 1983, 3(2): 76-84.
URL:
https://www.jcscp.org/EN/ OR https://www.jcscp.org/EN/Y1983/V3/I2/76
|
[1] H.J.Engell,1978年访问上海冶金所时的学术报告
[2] K.McGuinu,J.G.Griffiths,冷拉预应力钢丝耐应力腐蚀开裂性能的合理试验《高强钢在预应力混凝土中的腐蚀与防腐》译丛第一辑 南京水科所编译,P.1
[3] R.S.Gilmour etc.,断裂力学用预应力钢丝应力腐蚀敏感性,同上,P.23
[4] J. Gilckrist, R. Narayan, Corrosion Science. 12, 5, 281(1971)
[5] J. Eickemeyer,Corrosion Science. 19, 4, 397(1978)
[6] R. N.Parkins,Environment Sensitive Cracking of Pre-stressing Steels,待发表,(1981)
[7] R. Piccinini et al.,Localized Corrosion NACE Houston, Texas 179(1971)
[8] R. W. Judy, NRL Report 7865 AD-4008, 119 (1975)
[9] OTaKor Jonas, Corrosion, 29, 8, 299(1973)
[10] P. A. Parrish, 《Stress Corrosion-New Approaches 》 ed. by H. L. Craig, Jr., ASTM STP 610, 189 (1976)
[11] C. Chen, ibid, P. 289
[12] R.N.Parkins,1981年访问上海时的学术报告
[13] R.N.Parkins,恒应变应力腐蚀试验(译文)(1978)
[14] R. N. Parkins, 《Mechanics and Mechanism of Cracking Growth》 84(1973) |
| No Suggested Reading articles found! |
|
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|
Cited |
|
|
|
|
| |
Shared |
|
|
|
|
| |
Discussed |
|
|
|
|