金属陶瓷涂层耐蚀性能及影响因素的研究

李青;陈艳

重庆仪表材料研究所

Stuey on Corrosion Resistance and Affecting Factors of Metal Ceramic Coating

Qing Li;Yan Chen

重庆仪表材料研究所

全文: PDF(286 KB)

摘要: 研究了溶胶制备中所用催化剂种类、基体金属前处理及涂层厚度对用溶胶-凝胶法制得的陶瓷涂层耐蚀性能的影响，探讨获得最佳耐蚀性能的陶瓷涂层厚度所需的溶胶粘度及提拉速度范围。对不锈钢基体上SiO2、ZrO2、TiO2、SiO2-TiO2 陶瓷涂层，采用多种电化学及化学评价方法，在不同腐蚀介质中就不同组合试样的耐酸蚀、抗眯蚀和抗氧化性能等作了比较。结果表明在不锈钢上采用溶胶-凝胶浸渍提拉法制得连续而致密的陶瓷涂可有效保护基体金属。

关键词 ：陶瓷涂层, 溶胶-凝胶薄膜, 耐蚀性能

Abstract：The effect sol preparation with different catalysts,substrate prtreatment and coatings thickness on corrosion tesistance of sol-gel ceramic coatings was studied.The range of sol viscosity and the withdrawal speed for preparing the necessary ceramic coating thickness which could bring optimum corrosion resistance was also explored.By comparing the acid resistance,pitting resistance and oxidation resistance in different corrosive media with various standard electrochemical and chemical corosion evaluation methods for different assembly samples, including SiO2、ZrO2、TiO2、AlO3、SiO2-TiO2 ceramic coatings on stainless steel substrate, it could be concluded that the contineous and dense ceramic coating on stainless steel prepared with sol-gel dipping withdrawal method could provide effective protection.

Key words： ceramic coating sol-gel film corrosion resistance

收稿日期: 1999-06-15

ZTFLH:

TG174.453

Corresponding author: Qing Li

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	李青
	陈艳
44.8K

引用本文:

李青; 陈艳 . 金属陶瓷涂层耐蚀性能及影响因素的研究[J]. 中国腐蚀与防护学报, 2000, 20(3): 167-176 .
Qing Li, Yan Chen. Stuey on Corrosion Resistance and Affecting Factors of Metal Ceramic Coating. J Chin Soc Corr Pro, 2000, 20(3): 167-176 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2000/V20/I3/167

[1]李青 ,黄元龙 .溶胶凝胶法与金属表面改性 [J].腐蚀科学与防护技术 ,1997,9(3) :2 14 2 2 2
[2 ]AtikM ,LimaNetoPDe,AvacaLZ ,etal.MechanicalStabilityofSol GelFilms[J].JMaterSci,1991,2 6 :386 9 3873
[3]SanctisODe ,GomezL ,PellegriN .ProtectiveGlassCoatingsonMetallicSubstrates[J].JNon CrystSolids ,1990 ,12 1:338～ 343
[4 ]SanctisODe ,HomezL ,Duran .BehaviourinHotAmmoniaAtmosphereofSiO2 CoatedStainlessSteelsProducedbyaSol GelProcedure[J].SurfaceandCoatingTechnology ,1995.70 :2 51 2 55
[5]DamborenerJDe ,PellegriN ,SanctisODe ,etal.ElectrochemicalBehaviourofSiO2 Sol GelCoatingsonStainlessSteel[J],JSol GelSciTechnol,1995,4 :2 39 2 4 4
[6 ]AtikM ,LimaNetoPDe ,AvacaLA ,etal.Protectionof316LStainlessSteelAgainstCorrosionbySiO2 Coatings[J].JMaterSciLett,1994 ,13:10 81 10 85
[7]AtikM ,ZarzyckiJ,R’khaC .ProtectionofFerriticStainlessSteelAgainstOxidationbyZirconiaCoatings[J].JMaterSciLett1994 ,13:2 6 6 2 6 9
[8]AtikM ,’KhaCR ,LimaNetoPDe ,etal.Protectionof316LStainlessSteelbyZirconiaSol GelCoatingsin 15%H2 SO4Solutions[J].JMaterSciLett,1995,14:178 181
[9]NelsonRL ,RamsayJDF ,WoodheadJL .TheCoatingofMetalsWithCeramicOxidesViaColloidalIntermediates[J].ThinSolidFilms ,1981,81:32 9～ 337
[10 ]DiGiampaoloCondeAR ,PuertaM ,RuizH ,etal.ThickAluminosilicateCoatingsonCarbonSteelViaSol Gel[J].JNon CrystSolids,1992 ,147&148:4 6 7 4 73
[11]ShaneM ,MecartneyL .Sol GelSynthesisofZirconiabarrierCoatings[J].JMaterSci,1990 ,2 5:1537 1544
[12 ]AtikM ,AegerterMA .CorrosionResistantSol GelZrO2 CoatingsonStainlessSteel[J].JNon CrystSolids ,1992 ,147&148:813 819
[13]InnocenziPC ,GuglielmiM ,GobbinM ,etal.CoatingofMetalsbytheSol GelDip coatingMethod[J].JEurCeramSci,1992 ,10 :4 31 4 36
[14]MiyazawaK ,SuzukiK ,WegMY .Microstructureandoxidation ResistantPropertyofSol Gel DerivedZrO2 Y2 O3FilmsPreparedonAusteniticStainlessSteelSubstrates[J].JAmCeramSoc ,1995,78(2 ) :347 355
[15]加藤直树 ,谷口滋次 ,柴田俊夫ゾル—グル法によるSiO2 被膜の保护性に及ばよ溶液の粘度の影响 [J].Zairyo to Kankyo ,1992 ,4 1:535 541
[16 ]ZhongJi pin ,DavidEClark .InteractionBetweenColloidalParticlesinSiO2 andTiO2 Sols[J].JNon CrystSolids,1993,16 0 :2 4 7 2 54
[17]宫氵尺薰一 ,系井一博 ,佐久间健人 .ゾル—グル法によるオ—ステナィトステンレス钢のアルミナコ—テトング [J].日本金属学会志 ,1991,55:1345 1352
[18]KawashimaA ,WangY ,AkiyamaE ,etal.PreparationofProtectiveMultilayerSiO2 andAl2 O3CoatingsonAusteniticStainlessSteelbySol GelMethod[J].Zairyo to Kankyo ,1994 ,4 3:6 54 6 59
[19]王颖 ,秋山英二 ,幅崎浩树 ,等 .ゾル—グル法によη316ステンレス钢上に作制レゼアルミナ被覆の保护性[J].Zairyo to Kankyo ,1993,4 2 :158 16 5
[2 0 ]KatoK .PreparationofSiO2 FilmsfromSi(DC2 H5) 4 C2 H5OH H2 OSolutionsWithoutCatalysts[J].JMaterSci,1992 ,2 7:144 5 144 8
[2 1]KamiyaK ,YotaniJ,SenbaR ,etal.Sol GelPreparationofAluminaGelsFormingaaluminaAround 50 0℃ [J].JCer amSocJap ,1996 ,10 4 (7) :6 85 6 87
[2 2 ]PilzM ,RomichH .Sol GelforElectrochemitry[J].ChemMater ,1997,9(11) :2 345 2 375
[2 3]KatoK .EnhancementofthecorrosionresistanceofsubstratesbythinSiO2 coatingpreparedfromalkoxidesolutionswith outcatalysts[J].JMaterSci,1993,2 8:4 0 33～ 4 0 366

[1]	任岩, 钱余海, 张鑫涛, 徐敬军, 左君, 李美栓. 热震对包覆ZrB₂-SiC-La₂O₃/SiC涂层渗硅石墨力学性能的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 29-35.
[2]	刘海霞, 黄峰, 袁玮, 胡骞, 刘静. 690 MPa级高强贝氏体钢在模拟乡村大气中的腐蚀行为[J]. 中国腐蚀与防护学报, 2020, 40(5): 416-424.
[3]	陈超,梁艳芬,梁天权,满泉言,罗毅东,张修海,曾建民. 稀土复合掺杂ZrO₂陶瓷涂层抗Na₂SO₄+NaVO₃热腐蚀性能的研究进展[J]. 中国腐蚀与防护学报, 2019, 39(4): 291-298.
[4]	黄勇, 王善林, 王帅星, 龚玉兵, 柯黎明. 含硫化物夹杂铁基块体非晶合金在HCl溶液中的腐蚀行为[J]. 中国腐蚀与防护学报, 2018, 38(2): 203-209.
[5]	李广宇, 雷明凯. γ_Ν相在硼酸溶液中钝化膜的组成及其半导体特性研究[J]. 中国腐蚀与防护学报, 2018, 38(1): 47-53.
[6]	张新芳,欧孝通,刘雷,雷惊雷,李凌杰. 镁合金表面无机-有机杂化硅膜的制备及其防护性能研究[J]. 中国腐蚀与防护学报, 2017, 37(5): 435-443.
[7]	谭何灵,周成,刘希辉,曹国明,张菁. Cr对Q420钢在高盐度大气环境下耐蚀性的影响[J]. 中国腐蚀与防护学报, 2017, 37(3): 267-372.
[8]	徐相英,葛芳芳,李朋,舒瑞,黄峰,李谋成. 非晶Ti-B基涂层的力学和耐蚀性能研究[J]. 中国腐蚀与防护学报, 2016, 36(6): 573-579.
[9]	马旭,李全安,井晓天. 热处理对Mg-10Gd-2.5Nd-0.5Zr合金组织和耐蚀性能的影响[J]. 中国腐蚀与防护学报, 2016, 36(2): 143-149.
[10]	睢文杰,赵文杰,张星,秦立光,彭叔森,乌学东,薛群基. 铜合金表面巯基官能有机硅溶胶-凝胶涂层中TEOS含量对其防腐性能的影响[J]. 中国腐蚀与防护学报, 2016, 36(1): 52-58.
[11]	胡新芳, 李辛庚, 樊志彬, 王晓明, 王学刚. 新型Zn-22Al-Mg-Re合金涂层性能研究[J]. 中国腐蚀与防护学报, 2013, 33(6): 521-526.
[12]	王淑艳,夏永平刘莉. C₃H₈O₃含量对AZ91D镁合金微弧氧化过程及膜层特性的影响[J]. 中国腐蚀与防护学报, 2013, 33(3): 235-240.
[13]	王应发,黄国胜,程旭东,李相波,邢路阔,郭娟,马焱. 热喷涂Zn-Ni复合涂层在海水中的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2013, 33(1): 29-35.
[14]	肖正涛,李相波,王佳,黄国胜,周雄. 冷喷涂铬锆铜涂层在海水中的耐蚀性能[J]. 中国腐蚀与防护学报, 2012, 32(1): 18-22.
[15]	李守彪, 许立坤,沈承金,李相波. 等离子喷涂耐冲蚀陶瓷涂层的性能研究[J]. 中国腐蚀与防护学报, 2011, 31(3): 196-201.

Viewed

Full text

Abstract

Cited

Shared

Discussed