合金元素Mg对含RE铝阳极组织与性能的影响

齐公台;郭稚弧;屈钧娥

华中科技大学化学系应用化学教研室

EFFECT OF MAGNESIUM ON MICROSTRUCTURE ANDPERFORMANCE OF CONTAINING RE ALUMINUM ANODE

;;

华中科技大学化学系应用化学教研室

全文: PDF(169 KB)

摘要: 采用恒电流方法，测定了Al-5Zn-0.05In-0.1Sn-0.3RE和Al- 5Zn-0.05In-0.1Sn-Mg-0.3RE两种铝合金牺牲阳极材料电流效率.利用金相显微镜、扫描电镜和能谱分析，研究了它们的金相组织.结果表明：镁对含RE铝阳极性能有较大改善，镁的添加改变了铝合金晶界偏析相的组成；晶界析出物Mg相减轻了铝阳极的晶界腐蚀和晶粒脱落 .

关键词 ：铝阳极, 镁, 金相结构, 电流效率

Abstract：The electrochemical performance of Al-5Zn-0.05In-0. 1Sn-0.3RE and Al-5Zn-0.05In-0.1Sn-Mg-0.3RE alloy sacrificial anodes have been me asured with constant current method, and their microstructures have also been ex amined by metallography, scanning electron microscopy, and energy spectrum analy sis, Results showed that magnesium addition improved the performance of aluminum anode due to the change of the composition of segregation at grain boundary. Mg segregation at grain boundary decreased the corrosion of crystal grain boundary and dropping of crystal grain.

Key words： aluminum anode microstructure current efficiency ma gnesium

收稿日期: 2000-04-10

ZTFLH:

TG174.2

通讯作者: 齐公台

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	齐公台
	郭稚弧
	屈钧娥
44.8K

引用本文:

齐公台; 郭稚弧; 屈钧娥 . 合金元素Mg对含RE铝阳极组织与性能的影响[J]. 中国腐蚀与防护学报, 2001, 21(4): 220-224 .

链接本文:

https://www.jcscp.org/CN/Y2001/V21/I4/220

[1]TangHeqing.Studyandapplicationofaluminumalloysacrificialanode[J].CorrosionandProtectiononChemicalEngineering,1992,18(1):1-9(唐和清.铝合金牺牲阳极的研究与应用[J].化工腐蚀与防护,1992,18(1):1～9)
[2]SunHejian,HuoShizhong.TheroleofindiuminthedissolutionofAl-Zn-Inanodes[J].JournalofChineseSocietyforCor rosionandProtection,1987,7(2):115-120(孙鹤建,火时中.铟在铝基牺牲阳极溶解过程中的作用[J].中国腐蚀与防护学报,1987,7(2):115～120)
[3]ReboulMC ,DelatteDC .ActivationmechanismforsacrificialAl-Zn-Hganodes[J].MaterialsPerformance,1980,9(5):35～40
[4]BessoneJB ,etal.SeawatertestingofAl-Zn,Al-Zn-Sn,andAl-Zn-Insacrificialanodes[J].Corrosion,1981,37(9):533～540
[5]QiGongtai,GuoZhihu,etal.ThemicrostructureofaluminumalloysacrificialanodecontainingdifferentREcontents[J].Cor rosionScienceandProtectionTechnology,1998,10(1):17-22(齐公台,郭稚弧等.不同稀土含量的铝合金牺牲阳极的显微组织研究[J].腐蚀科学与防护技术,1998,10(1):17～22)
[6]GB4948～4949-85,NationalStandardofPRC .Al-Zn-InAlloySacrificialAnodes,1985(GB4948-4949-85,中国人民共和国标准,铝-锌-铟合金牺牲阳极,1985)
[7]GongLeiqing,JinChanggeng,etal.AnMetallographicAtlasofCastingAlAlloy[M ].Changsha:CentralSouthUniversityofTechnologyPress,1987(龚磊清,金长庚等.铸造铝合金金相图谱[M].长沙:中南工业大学出版社,1987)
[8]WuYihua.AstudyoftheeffectofalloyelementsontheactivationofAl-basedsacrificialanode[J].JournalofChineseSoci etyforCorrosionandProtection,1989,9(2):113-120(吴益华.合金元素在铝基牺牲阳极活化过程中的作用[J].中国腐蚀与防护学报,1989,9(2):113～120)
[9]MondolfoLF .Aluminumalloys:StructureandProperties[M ].London:Butterworths,1976(L .F .蒙多尔福著,王祝堂,张振录,郑璇译.铝合金的组织及性能[M ].北京:冶金工业出版社,1988)
[10]ZhuYing.StudyonAl-Zn-In-Snalloysacrificialanode[J].MaterialsProtection,1986,19(4):20-25(朱颖.铝锌铟锡系合金牺牲阳极性能研究[J].材料保护,1986,19(4):20～25)
[11]QiGongtai,GuoZhihu,etal.Microstructureandelectrochemicalperformanceofaluminumalloysforsacrificialanode[J].Cor rosionScienceandProtectionTechnology,1997,9(3):231-235(齐公台,郭稚弧等.铝合金牺牲阳极金相组织与电化学性能关系研究[J].腐蚀科学与防护技术,1997,9(3):231～235)
[12]TangHeqing,ZhengJiashen.ResearchonHTaluminumalloysacrificialanode[J].JournalofHuazhongUniversityofScienceandTechnology,1992,20(4):133-139(唐和清,郑家焱木.HT高温铝合金牺牲阳极的研究[J].华中理工大学学报,1992,20(4):133～139)

[1]	郑黎, 王美婷, 于宝义. 镁合金表面冷喷涂技术研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 22-28.
[2]	魏征, 马保吉, 李龙, 刘潇枫, 李慧. 镁合金表面超声滚压预处理对微弧氧化膜耐蚀性能的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 117-124.
[3]	于浩冉, 张文丽, 崔中雨. 4种镁合金在Cl^--NH₄⁺-NO₃^-溶液体系中的腐蚀行为差异研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 553-559.
[4]	岳亮亮, 马保吉. 超声表面滚压对AZ31B镁合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 560-568.
[5]	郏义征, 王保杰, 赵明君, 许道奎. 固溶处理制度对挤压态Mg-Zn-Y-Nd镁合金在模拟体液中腐蚀和析氢行为的影响规律研究[J]. 中国腐蚀与防护学报, 2020, 40(4): 351-357.
[6]	张尧, 郭晨, 刘妍慧, 郝美娟, 成世明, 程伟丽. 挤压态Mg-2Sn-1Al-1Zn合金在模拟体液中的电化学腐蚀行为[J]. 中国腐蚀与防护学报, 2020, 40(2): 146-150.
[7]	郏义征, 赵明君, 程世婧, 王保杰, 王硕, 盛立远, 许道奎. 模拟人体体液中镁合金的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2019, 39(6): 463-468.
[8]	欧阳跃军,胡婷,王佳音,谢治辉. 镁合金表面层状双氢氧化物的电化学沉积和表征[J]. 中国腐蚀与防护学报, 2019, 39(5): 453-457.
[9]	王保杰,栾吉瑜,王士栋,许道奎. 镁合金应力腐蚀开裂行为研究进展[J]. 中国腐蚀与防护学报, 2019, 39(2): 89-95.
[10]	刘丽,于思荣. 添加Gd对AM60镁合金耐腐蚀性能的影响[J]. 中国腐蚀与防护学报, 2019, 39(2): 185-191.
[11]	李亚琼,马景灵,王广欣,朱宇杰,宋永发,张景丽. NaPO₃与SDBS缓蚀剂对AZ31镁合金空气电池在NaCl电解液中放电性能的影响[J]. 中国腐蚀与防护学报, 2018, 38(6): 587-593.
[12]	樊志民, 于锦, 宋影伟, 单大勇, 韩恩厚. 镁合金点蚀的研究进展[J]. 中国腐蚀与防护学报, 2018, 38(4): 317-325.
[13]	王志虎, 张菊梅, 白力静, 张国君. AZ91镁合金表面微弧氧化与化学镀铜复合处理层的微观组织与性能[J]. 中国腐蚀与防护学报, 2018, 38(4): 391-396.
[14]	陈琳, 钟福荣, 昝金龙. 复合电解液中AZ31B镁合金的放电特性及电压滞后[J]. 中国腐蚀与防护学报, 2018, 38(2): 197-202.
[15]	崔学军, 平静. 微弧氧化及其在镁合金腐蚀防护领域的研究进展[J]. 中国腐蚀与防护学报, 2018, 38(2): 87-104.

Viewed

Full text

Abstract

Cited

Shared

Discussed