电化学噪声分析方法的研究进展 |
张 涛1,2 杨延格1 邵亚薇1,2 孟国哲1,2 王福会1,2 |
1. 中国科学院金属研究所 金属腐蚀与防护国家重点实验室 沈阳 110016; 2. 哈尔滨工程大学材料科学与化学工程学院腐蚀与防护实验室 哈尔滨 150001 |
|
Advances of the Analysis Methodology for Electrochemical Noise |
ZHANG Tao1,2, YANG Yange1, SHAO Yawei1,2, MENG Guozhe1,2, WANG Fuhui1,2 |
1. State Key Laboratory for Corrosion and Protection, Institute of Metals Research, Chinese Academy of Sciences, Shenyang 110016, China; 2. Corrosion and Protection Laboratory, College of Materials Science and Chemical Engineering, Harbin Engineering University, Harbin 150001, China |
[1] Bertocci U, Huet F. Noise analysis applied to electrochemical systems [J]. Corrosion, 1995, 51: 131-144 [2] Legat A, Zevnik C. The electrochemical noise of mild and stainless steel in various water solutions [J]. Corros. Sci., 1993, 35: 1661-1666 [3] Legat A. Influence of electrolyte movement on measured electrochemical noise [J]. Corrosion, 2000, 56: 1086-1092 [4] Gouveia-Caridade C, Pereira M, Brett C. Electrochemical noise and impedance study of aluminium in weakly acid chloride solution [J]. Electrochim. Acta, 2004, 49: 785-793 [5] Zhang Z, Leng W, Cai Q, et al. Study of the zinc electroplating process using electrochemical noise technique [J]. J. Electroanal. Chem., 2005, 578: 357-367 [6] Lafront A, Ghali E, Morales A. Corrosion behavior of two bipolar plate materials in simulated PEMFC environment by electrochemical noise technique [J]. Electrochim. Acta, 2007, 52: 5076-5085 [7] H?rlé S, Malki B, Baroux B. Corrosion current fluctuations at metastable to stable pitting transition of aluminum [J]. J. Electrochem. Soc., 2006, 153: B527-B532 [8] Girija S, Mudali U, Raju V, et al. Determination of corrosion types for AISI type 304L stainless steel using electrochemical noise method [J]. Mater. Sci. Eng., 2005, A407: 188-195 [9] Cappeln F, Bjerrum N, Petrushina I. Electrochemical noise measurements of steel corrosion in the molten NaCl-K2SO4 system [J]. J. Electrochem. Soc., 2005, 152: B228-B235 [10] Tan Y, Bailey S, Kinsella B, et al. Mapping corrosion kinetics using the wire beam electrode in conjunction with electrochemical noise resistance measurements [J]. J. Electrochem. Soc., 2000, 147: 530-539 [11] Girija S, Mudali U, Khatak H, et al. The application of electrochemical noise resistance to evaluate the corrosion resistance of AISI type 304 SS in nitric acid [J]. Corros. Sci., 2007, 49: 4051-4068 [12] Schmitt G. Listen to corrosion at work—A newly developed versatile corrosion monitoring tool ready for plant application [J]. Mater. Corros., 2007, 58: 924-939 [13] Yang Z, Zhang Z, Leng W, et al. In-situ monitoring of nickel electrodeposit structure using electrochemical noise technique [J]. Trans. Nonferrous Met. Soc. China, 2006, 16: 209-216 [14] Wang D, Zhang T, Shao Y, et al. A new criterion to determine the critical pitting temperature (CPT) based on electrochemical noise measurement [J]. Corros. Sci., 2012, 58: 202-210 [15] Yu J, Luo J, Norton P. Investigation of hydrogen-promoted pitting by the electrochemical noise method and the scanning reference electrode technique [J]. Langmuir, 2002, 18: 6637-6646 [16] Zhang J Q, Zhang Z, Wang J M, et al. Analysis and application of electrochemical noise-I. Theory of electrochemical noise analysis [J]. J. Chin. Soc. Corros. Prot., 2001, 21(5): 310-320 (张鉴清, 张昭, 王建明等. 电化学噪声的分析与应用-I. 电化学噪声的分析原理 [J]. 中国腐蚀与防护学报, 2001, 21(5): 310-320) [17] Zhang J Q, Zhang Z, Wang J M, et al. Analysis and application of electrochemical noise-II. Application of electrochemical noise ana- lysis [J]. J. Chin. Soc. Corros. Prot., 2002, 22(4): 241-248 (张鉴清, 张昭, 王建明等. 电化学噪声的分析与应用-II. 电化学噪声的应用 [J]. 中国腐蚀与防护学报, 2002, 22(4): 241-248) [18] Mabbutt S, Simms N, Oakey J. High temperature corrosion monitoring by electrochemical noise techniques [J]. Corros. Eng. Sci. Technol., 2009, 44(3): 186-195 [19] Ashassi-Sorkhabi H, Seifzadeh D, Hosseini M. EN, EIS and polarization studies to evaluate the inhibition effect of 3H-phenothiazin-3-one, 7-dimethylamin on mild steel corrosion in 1 M HCl solution [J]. Corros. Sci., 2008, 50: 3363-3370 [20] Klapper H, Goellner J. Electrochemical noise from oxygen reduction on stainless steel surfaces [J]. Corros. Sci., 2009, 51: 144-150 [21] Cottis R. Interpretation of electrochemical noise data [J]. Corrosion, 2001, 57(3): 265-285 [22] Tan Y, Bailey S, Kinsella B. The monitoring of the formation and destruction of corrosion inhibitor films using electrochemical noise analysis (ENA) [J]. Corros. Sci., 1996, 38: 1681-1695 [23] Mansfeld F, Sun Z, Hsu C, et al. Concerning trend removal in electrochemical noise measurements [J]. Corros. Sci., 2001, 43: 341-352 [24] Bertocci U, Huet F, Nogueira R, et al. Drift removal procedures in the analysis of electrochemical noise [J]. Corrosion, 2002, 58(4): 337-347 [25] Zhang T, Shao Y, Meng G, et al. Electrochemical noise analysis of the corrosion of AZ91D magnesium alloy in alkaline chloride solution [J]. Electrochim. Acta, 2007, 53: 561-568 [26] Cao F, Zhang Z, Su J, et al. Electrochemical noise analysis of LY12-T3 in EXCO solution by discrete wavelet transform technique [J]. Electrochim. Acta, 2006, 51: 1359-1364 [27] Liu X, Zhang T, Shao Y, et al. In-situ study of the formation process of stannate conversion coatings on AZ91D magnesium alloy using electrochemical noise [J]. Corros. Sci., 2010, 52: 892-900 [28] Rosero-Navarro N, Curioni M, Bingham R, et al. Electrochemical techniques for practical evaluation of corrosion inhibitor effectiveness. Performance of cerium nitrate as corrosion inhibitor for AA2024T3 alloy [J]. Corros. Sci., 2010, 52: 3356-3366 [29] Huang J, Qiu Y, Guo X. Comparison of polynomial fitting and wavelet transform to remove drift in electrochemical noise analysis [J]. Corros. Eng. Sci. Technol., 2010, 45(4): 288-294 [30] Nagiub A, Mansfeld F. Evaluation of microbiologically influenced corrosion inhibition using electrochemical noise analysis [J]. Corros. Sci., 2001, 43: 2001-2009 [31] Nagiub A, Mansfeld F. Evaluation of corrosion inhibition of brass in chloride media using EIS and ENA [J]. Corros. Sci., 2001, 43: 2147-2171 [32] Nagiub A, Mansfeld F. Evaluation of microbiologically influenced corrosion inhibition (MICI) with EIS and ENA [J]. Electrochim. Acta, 2002, 47: 2319-2333 [33] Mansfeld F, Han L, Lee C, et al. Analysis of electrochemical impedance and noise data for polymer coated metals [J]. Corros. Sci., 1997, 37(2): 255-279 [34] Xiao H, Han L, Lee C, et al. Collection of electrochemical impedance and noise data for polymer-coated steel from remote test sites [J]. Corrosion, 1997, 53(5): 412-422 [35] Mansfeld F, Lee C, Zhang G. Comparison of electrochemical impedance and noise data in the frequency domain [J]. Electrochim. Acta, 1998, 43(3/4): 435-438 [36] Mansfeld F, Sun Z, Hsu C. Electrochemical noise analysis (ENA) for active and passive systems in chloride media [J]. Electrochim. Acta, 2001, 46: 3651-3664 [37] Morlet J, Arens G, Fourgeau E, et al. Wave propagation and sampling theory—Part II: Sampling theory and complex waves [J] . Geophysics, 1982, 47(2): 222-236 [38] Aballe A, Bethencourt M, Botana F, et al. Wavelet transform-based analysis for electrochemical noise [J]. Electrochem. Commun., 1999, 1: 266-270 [39] Duran O, Vera E, Ortiz C A, et al. Use of the wavelet method for analyzing electrochemical noise data [J]. Mater. Corros., 2007, 58 (12): 997-999 [40] Shi Y, Zhang Z, Su J, et al. Electrochemical noise study on 2024-T3 Aluminum alloy corrosion in simulated acid rain under cyclic wet-dry condition [J]. Electrochim. Acta, 2006, 51: 4977-4986 [41] Liu L, Li Y, Wang F. Pitting mechanism on an austenite stainless steel nanocrystalline coating investigated by electrochemical noise and in-situ AFM analysis [J]. Electrochim. Acta, 2008, 54: 768-780 [42] Dong Z, Guo X, Zeng J, et al. Calculation of noise resistance by use of the discrete wavelets transform [J]. Electrochem. Commun., 2001, 3: 561-565 [43] Cai C, Zhang Z, Cao F, et al. Analysis of pitting corrosion behavior of pure Al in sodium chloride solution with the wavelet technique [J]. J. Electroanal. Chem., 2005, 578: 143-150 [44] Aballe A, Bethencourt M, Botana F, et al. Electrochemical noise applied to the study of the inhibition effect of CeCl3 on the corrosion behaviour of Al-Mg alloy AA5083 in seawater [J]. Electrochim. Acta, 2002, 47: 1415-1422 [45] Zhao B, Li J, Hu R, et al. Study on the corrosion behavior of reinforcing steel in cement mortar by electrochemical noise measurements [J]. Electrochim. Acta, 2007, 52: 3976-3984 [46] Lafront A, Zhang W, Ghali E, et al. Electrochemical noise studies of the corrosion behaviour of lead anodes during zinc electrowinning maintenance [J]. Electrochim. Acta, 2010, 55: 6665-6675 [47] Zhang Z, Leng W, Cai Q, et al. Study of the zinc electroplating process using electrochemical noise technique [J]. J. Electroanal. Chem., 2005, 578: 357-367 [48] Darowicki K, Zakowski K. A new time-frequency detection method of stray current field interference on metal structures [J]. Corros. Sci., 2004, 46: 1061-1070 [49] Yang Y G. In situ study of hydrochloric acid dew point corrosion of carbon steel and stainless steel [D]. Harbin: Harbin Engineering University, 2013 (杨延格. 碳钢及不锈钢盐酸露点腐蚀的原位研究 [D]. 哈尔滨: 哈尔滨工程大学, 2013) [50] Homborg A, van Westing E, Tinga T, et al. Novel time–frequency characterization of electrochemical noise data in corrosion studies using Hilbert spectra [J]. Corros. Sci., 2013, 66: 97-110 [51] Burstein G, Souto R. Improvement in pitting resistance of stainless steel surfaces by prior anodic treatment in metasilicate solution [J]. J. Electrochem. Soc., 2004, 151(10): B537-B542 [52] Burstein G, Vines S. Repetitive nucleation of corrosion pits on stainless steel and the effects of surface roughness [J]. J. Electrochem. Soc., 2001, 148(12): B504-B516 [53] Burstein G, Liu C, Souto R, et al. Origins of pitting corrosion [J]. Corros. Eng. Sci. Technol., 2004, 39(1): 25-30 [54] Ilevbare G, Burstein G T. The inhibition of pitting corrosion of stainless steels by chromate and molybdate ions [J]. Corros. Sci., 2003, 45: 1545-1569 [55] Williams D, Stewart J, Balkwill P. The nucleation, growth and stability of micropits in stainless steel [J]. Corros. Sci., 1994, 36: 1213-1235 [56] Ilevbare G, Burstein G T. The role of alloyed molybdenum in the inhibition of pitting corrosion in stainless steels [J]. Corros. Sci., 2001, 43: 485-513 [57] Tang Y, Zuo Y, Zhao H. The current fluctuations and accumulated pitting damage of mild steel in NaNO2-NaCl solution [J]. Appl. Surf. Sci., 2005, 243: 82-88 [58] Tang Y, Zhao X, Mao J, et al. The electrochemical characteristics of pitting for two steels in phosphate buffer solution with chloride [J]. Mater. Chem. Phys., 2009, 116: 484-488 [59] Tang Y, Zuo Y, Zhao X. The metastable pitting behaviors of mild steel in bicarbonate and nitrite solutions containing Cl- [J]. Corros. Sci., 2008, 50: 989-994 [60] Tang Y, Zuo Y. The metastable pitting of mild steel in bicarbonate solutions [J]. Mater. Chem. Phys., 2004, 88: 221-226 [61] Wang H, Xie J, Yan K, et al. The nucleation and growth of metastable pitting on pure iron [J]. Corros. Sci., 2009, 51: 181-185 [62] Zuo Y, Wang H, Zhao J, et al. The effects of some anions on metastable pitting of 316L stainless steel [J]. Corros. Sci., 2002, 44: 13-24 [63] Cottis R, Al-Awadhi M, Al-Mazeedi H, et al. Measures for the detection of localized corrosion with electrochemical noise [J]. Electrochim. Acta, 2001, 46: 3665-3674 [64] Sánchez-Amaya J, Cottis R A, Botana F J. Shot noise and statistical parameters for the estimation of corrosion mechanisms [J]. Corros. Sci., 2005, 47: 3280-3299 [65] Al-Mazeedi H, Cottis R. Practical evaluation of electrochemical noise parameters as indicators of corrosion type [J]. Electrochim. Acta, 2004, 49: 2787-2793 [66] Sánchez-Amaya J, Bethencourt M, González-Rovira L, et al. Noise resistance and shot noise parameters on the study of IGC of aluminium alloys with different heat treatments [J]. Electrochim. Acta, 2007, 52: 6569-6583 [67] Zhang J. Research on crevice corrosion behaviour of 5083 and 6061 aluminium alloys [D]. Harbin: Harbin Engineering University, 2013 (张晋. 5083和6061铝合金缝隙腐蚀行为研究 [D]. 哈尔滨: 哈尔滨工程大学, 2013) [68] Na K, Pyun S. Effect of sulphate and molybdate ions on pitting corrosion of aluminium by using electrochemical noise analysis [J]. J. Electroanal. Chem., 2006, 596: 7-12 [69] Na K, Pyun S. Evaluation of pitting susceptibility of aluminum anodized in borate and phosphate solutions using EN analysis [J]. J. Electrochem. Soc., 2007, 154(7): C355-C361 [70] Na K, Pyun S. Effects of sulphate, nitrate and phosphate on pit initiation of pure aluminium in HCl-based solution [J]. Corros. Sci., 2007, 49: 2663-2675 [71] Na K, Pyun S. Electrochemical noise analysis of corrosion of pure aluminium in alkaline solution in the presence of SO42- ion, NO3-ion and Na2S additives [J]. Electrochim. Acta, 2007, 52: 4363-4373 [72] Na K, Pyun S, Kim H. Analysis of electrochemical noise obtained from pure aluminium in neutral chloride and alkaline solutions [J]. Corros. Sci., 2007, 49: 220-230 [73] Trueman A. Determining the probability of stable pit initiation on aluminium alloys using potentiostatic electrochemical measurements [J]. Corros. Sci., 2005, 47: 2240-2256 [74] Valor A, Caleyo F, Alfonso L, et al. Stochastic modeling of pitting corrosion: A new model for initiation and growth of multiple corrosion pits [J]. Corros. Sci., 2007, 49: 559-579 [75] Engelhardt G, Macdonald D. Unification of the deterministic and statistical approaches for predicting localized corrosion damage. I. Theoretical foundation [J]. Corros. Sci., 2004, 46: 2755-2780 [76] Zhang T, Chen C, Shao Y, et al. Corrosion of pure magnesium under thin electrolyte layers [J]. Electrochim. Acta, 2008, 53: 7921-7931 [77] Zhang T, Liu X, Shao Y, et al. Electrochemical noise analysis on the pit corrosion susceptibility of Mg-10Gd-2Y-0.5Zr, AZ91D alloy and pure magnesium using stochastic model [J]. Corros. Sci., 2008, 50: 3500-3507 [78] Chen C, Zhang T, Shao Y, et al. Corrosion behavior of Mg-10Gd-2Y-0.4Zr alloy under thin electrolyte layers [J]. Mater. Corros., 2010, 61: 388-397 [79] Meng G, Wei L, Shao Y, et al. High pitting corrosion resistance of pure aluminum with nanoscale twins [J]. J. Electrochem. Soc., 2009, 156(8): C240-C245 [80] Meng G, Wei L, Zhang T, et al. Effect of microcrystallization on pitting corrosion of pure aluminium [J]. Corros. Sci., 2009, 51: 2151-2157 [81] Xia D H. Deterioration process and corrosion detection of metal packaging materials [D]. Tianjin: Tianjin University, 2012 (夏大海. 金属包装材料的腐蚀失效过程和腐蚀检测 [D]. 天津: 天津大学, 2012) [82] Xia D, Song S, Wang J, et al. Determination of corrosion types from electrochemical noise by phase space reconstruction theory [J]. Electrochem. Commun., 2012, 15: 88-92 [83] Legat A, Dole?ek V. Chaotic analysis of electrochemical noise measured on stainless-steel [J]. J. Electrochem. Soc., 1995, 142(6): 1851-1858 [84] Cazares-Ibá?ez E, Vázquez-Couti?o G, García-Ochoa E. Application of recurrence plots as a new tool in the analysis of electrochemical oscillations of copper [J]. J. Electroanal. Chem., 2005, 583: 17-33 [85] García-Ochoa E, González-Sánchez J, Acu?a N, et al. Analysis of the dynamics of intergranular corrosion processof sensitised 304 stainless steel using recurrence plots [J]. J. Appl. Electrochem., 2009, 39: 637-645 [86] Acu?a-González N, García-Ochoa E, González-Sánchez J. Assessment of the dynamics of corrosion fatigue crack initiation applying recurrence plots to the analysis of electrochemical noise data [J]. Int. J. Fatigue, 2008, 30: 1211-1219 [87] López-Meléndez C, Garcia-Ochoa E M, Flores-Zamora M, et al. Dynamic study of current fluctuations of nanostructured films [J]. Int. J. Electrochem. Sci., 2012, 7: 1160-1169 [88] Montalbán L, Aivihentiu P. Recurrence quantification analysis of electrochemical noise data during pit development [J]. Int. J. Bifurcation Chaos, 2007, 17(10): 3725-3728 [89] Yang Y, Zhang T, Shao Y, et al. Effect of hydrostatic pressure on the corrosion behaviour of Ni-Cr-Mo-V high strength steel [J]. Co- rros. Sci., 2010, 52: 2697-2706 [90] Turcotte D. Fractals and Chaos in Geology and Geophysics [M]. Cambridge: Cambridge University Press, 1997 [91] Zhang L, Zhu X, Zhang Z, et al. Electrochemical noise characteristics in corrosion process of AZ91D magnesium alloy in neutral chloride solution [J]. Trans. Nonferrous Met. Soc. China, 2009, 19: 496-503 [92] Sarmiento E, González-Rodriguez J, Uruchurtu J, et al. Fractal analysis of the corrosion inhibition of carbon steel in a bromide solution by lithium chromate [J]. Int. J. Electrochem. Sci., 2009, 4: 144-155 [93] García-Ochoa E, Corvo F. Copper patina corrosion evaluation by means of fractal geometry using electrochemical noise (EN) and image analysis [J]. Electrochem. Commun., 2010, 12: 826-830 [94] Sarmiento E, González-Rodriguez J, Uruchurtu J. A study of the corrosion inhibition of carbon steel in a bromide solution using fractal analysis [J]. Surf. Coat. Technol., 2008, 203: 46-51 [95] Horváth A, Schiller R. Rescaled range analysis of the corrosion potential noise [J]. Corros. Sci., 2003, 45: 597-609 [96] Luciano G, Traverso P, Letardi P. Applications of chemometric tools in corrosion studies [J]. Corros. Sci., 2010, 52: 2750-2757 [97] Huang J, Guo X, Qiu Y, et al. Cluster and discriminant analysis of electrochemical noise data [J]. Electrochim. Acta, 2007, 53: 680-687 [98] Huang J, Qiu Y, Guo X. Cluster and discriminant analysis of electrochemical noise statistical parameters [J]. Electrochim. Acta, 2009, 54: 2218-2223 [99] Hu Q, Qiu Y, Guo X, et al. Crevice corrosion of Q235 carbon steels in a solution of NaHCO3 and NaCl [J]. Corros. Sci., 2010, 52: 1205-1212
|
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|
Cited |
|
|
|
|
|
Shared |
|
|
|
|
|
Discussed |
|
|
|
|