钛合金应力腐蚀开裂过程中氢的作用

黄显亚;李永洪;肖纪美

有色金属研究总院;有色金属研究总院;北京钢铁学院

THE ROLE OF HYDROGEN IN SCC OF TITANIUM ALLOY

Huang Xianya Li Yunghung (General Research Institute of Non-ferrous Metals;MMI)Xiao Jinei (Beijing University of Iron and Steel Technology)

全文: PDF(2859 KB)

摘要: 本文用金相显微镜和扫描电镜对 Ti-5Al-2.5Sn 合金在近中性3.5%NaCl 水溶液中 SCC 裂纹形核带的微观形貌进行了观察。通过金相显微镜、透射电镜、X 光衍射仪和离子探针等手段对 SCC断口的研究,证明了 SCC 裂纹尖端生成的氢确实进入了钛合金基体,并且裂纹前端最大三向应力区域形成了 fct 型和 bcc 型氢化物沉淀,导致了 SCC 的快速发展。在实验事实的基础上,对 SCC 过程中氢的来源、输运、氢起作用的位置,以及内氢的作用等问题进行了讨论。

Abstract：The micro-morphology of the initiation zone of SCC of Ti-5A1-2.5Sn alloy in 3.5% NaCl solution has been inspected by OM and SEM.A study of the SCC crack's details by OM,TEM,X-ray diffractometer and ion microanaly- zer has also been made.Based upon the results of these experiments,it is pro- ved that the hydrogen generated during SCC has really penetrated into the metal matrix,then concentrated at the maximum of triaxial stress in front of the crack tip,and precipitated as hydride particles of fct and bee lattice, resulting in rapid development of SCC.The source,transportation and acting position of hydrogen,as well as the role of internal hydrogen in SCC of tita- nium alloy have been discussed.

收稿日期: 1984-02-25

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	黄显亚
	李永洪
	肖纪美
44.8K

引用本文:

黄显亚;李永洪;肖纪美. 钛合金应力腐蚀开裂过程中氢的作用[J]. 中国腐蚀与防护学报, 1984, 4(1): 41-45.
. THE ROLE OF HYDROGEN IN SCC OF TITANIUM ALLOY. J Chin Soc Corr Pro, 1984, 4(1): 41-45.

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y1984/V4/I1/41

[1] Leckie,H.P.Corrosion,23,187(1967)
[2] Beck,T.R.,The Theory of Stress Corrosion Cracking in Alloys,ed.by,J.C.Scully,64(1971)
[3] Scully,J.C.,Corrosion Science,7,197(1967)
[4] 黄显亚、朱祖芳、王得明、肖纪美,中国腐蚀与防护学报,2,4,37(1982)
[5] Powell,D.T.,Scully,J.C.,Corrosion,24,151(1968)
[6] Oriani,R.A.,Ber.Bunsenges.Phys.Chem.,76,848(1972)
[7] Van Leenwen,H.P.,Corrosion,31,154(1975)
[8] Meyn,D.A.,Met.Trans.,5,2405(1974)
[9] 兰州化工机械研究所交流资料,钛制湿氯冷却器缝隙腐蚀试验研究报告,(1978)
[10] Lin;Le-yun;Huang Xian-ya;Li Ya-kun;Hsiao Chi-mei,Scripta Met.,16,12,(1982)
[11] Irwin,G.R.,Proc.of the Sagamose Ordnamoce Materials Research Conf.,IV63,(1961)
[12] 黄显亚等,金属学报,20,(1984)
[13] Williams,J.C.,Effect of Hydrogen on Behavior of Materials,Met.Soc.,AIME,N.Y.,367(1976)
[14] Hsiao Chi-mei;Huang Xian-ya;Wan De-ming;Zhu Zu-fang,Proceedings-8th Inter.Cong.on Metallic Corrosion,594(1981)
[15] Boyd,J.D.,Trans.ASM.62,977(1969)
[16] Brauer,E.et.al.,Proc,of Conf.of Hydrogen in Metals,Munster,(1979)

No related articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed