氮改善00Cr18Ni5Mo3Si2双相不锈钢应力腐蚀破裂性能的机制

艾文山;左景伊;吴玖

北京化工学院;北京化工学院;冶金部钢铁研究总院

THE MECHANISM OF NITROGEN EFFECT ON THE SCC BEHAVIOR OF 00Cr18Ni5Mo3Si2 DUPLEX STAINLESS STEEL

Ai Wenshan Zuo Jingyi (Beijing Institute of Chemical Technology)Wu Jiu (Central Iron and Steel Research Institute)

全文: PDF(1466 KB)

摘要: 用 AES 分析了含氮双相不锈钢在30%MgCl_2(沸)溶液中浸泡后的表面膜。结果表明,氮在表面膜中富集.氮量越高,富集的量越多。钼和镍的富集均与钢中的氮含量有关.钼的富集要求氮含量在0.11%以上,镍的富集要求氮含量在0.073%以上,氮和钼的联合作用使钢表面膜的钝化能力得到加强。恒电位浸泡实验表明,阳极极化增厚了表面膜,降低了氮的作用。在0.5V NaCl(50℃,pH=7)溶液中,由模拟闭塞区实验得出:氮对裂缝尖端的化学状态无明显影响,闭塞区内未发现 NH_4~+。透射电镜(TEM)分析表明,氮量提高使位错由层状结构变为网状结构,增加了层错能。

Abstract：After immersion in 30%MgCl_2 solution (boiling),the surface films of the 00CrlSNi5Mo3Si2 steels with different nitrogen contents were analyzed.Nitrogen was found to enrich in the surface film,and the higher the nitrogen content in the duplex stain- less steel was,the more amount of nitrogen was enriched in the surface film.Enrichment of Ni and Mo was influenced by nitrogen content with the content of nitrogen≥0.073% for Ni alone,and≥0.11% for both Ni and Mo.The combined effect of nitrogen and Mo increased the passivation ability of the surface film.The potentiostatic immersion test showed that anodic polarization thickened the surface film and weakened the effect of ni- trogen.A simulated occluded cell (OC) was used to study the chemical changes in the OC of the duplex stainless steel in 0.5N NaCl solution (50℃,pH=7).It was found that nitro- gen had little effect on either the pH fall or Cl~- enrichment in the OC,and that there was no NH_4~+ in the OC.TEM analysis showed that dislocation changed from layer structure in- to net structure and that stacking fault enrgy increased with the increase of nitrogen con- tent.

收稿日期: 1991-02-25

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	艾文山
	左景伊
	吴玖
44.8K

引用本文:

艾文山;左景伊;吴玖. 氮改善00Cr18Ni5Mo3Si2双相不锈钢应力腐蚀破裂性能的机制[J]. 中国腐蚀与防护学报, 1991, 11(1): 9-16.
. THE MECHANISM OF NITROGEN EFFECT ON THE SCC BEHAVIOR OF 00Cr18Ni5Mo3Si2 DUPLEX STAINLESS STEEL. J Chin Soc Corr Pro, 1991, 11(1): 9-16.

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y1991/V11/I1/9

[1] 艾文山.左景伊.吴玖.中国腐蚀与防护学报.11(1) .1(1991)
[2] 金子智.栗本昭仁.新居一男.佐腾羲和.竹田诚一.日本金属学会志.48(5) .534(1984)
[3] 安保秀雄.野口栄.林巨幸.上田全纪.防食技术.23(6) .303(1974)
[4] Manning.P.E.,Corrosion.39(3) .98(1982)
[5] #12
[6] 酒井润一.本田正春.松岛严.铁钢.69(5) .226(1983)
[7] Clark.C.A.,Guha.P..Werkstoffe und Korrosion,34(1) 27(1983)
[8] Osozawa K,Okada,N.,防食技术24,1(1975)
[9] Lu,Y.C.,Bandy,R.,Clayton,C.R.,and Newman R.C.,J.Electrochem.Soc.130,1774(1983)
[10] Newman,R.C.,Lu,Y.C..Bandy,R.and Clayton,C.R,Proc of 9th,International Congress on Metallic Corrosion,TORONTO.P394,(1984)
[11] 冶金部钢铁研究总院等编.00Cr18Ni5Mo3Si2双相不锈钢.化学工业部设备设计技术中心站.P37． (1983)
[12] 邵景华.氮对奥氏体不锈钢在高温水中应力腐蚀的影响,待发表
[13] 左景伊、金志强,化工学报.(4) ,291(1982)

No related articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed