LY12铝合金的长期大气腐蚀行为

孙霜青;郑弃非;李德富;陈杰;温军国

北京有色金属研究总院北京 100088

LONG-TERM ATMOSPHERIC CORROSION BEHAVIOR OF LY12 ALUMINIUM ALLOY

SUN Shuangqing; ZHENG Qifei; LI Defu; CHEN Jie; WEN Junguo

General Research Institute for Nonferrous Metals; Beijing 100088; China

全文: PDF(716 KB)

摘要:

通过5种典型大气环境下为期20年的现场暴露试验，研究了LY12 铝合金在我国长期大气腐蚀的规律和行为。结果表明，LY12在湿热的万宁和琼海分别暴露6年和10年后就发生了剥蚀，暴露20年后几乎丧失了力学性能，而在北京暴露20年后未出现剥蚀，仍保持良好的力学性能。LY12在大气污染物较多的江津和青岛腐蚀失重较大，在北京的腐蚀失重最小。剥蚀发生之前，LY12的腐蚀失重随暴露时间的变化遵循幂函数C=KTⁿ。剥落腐蚀产物中除Al屑之外主要为γ-Al(OH)₃和α-Al₂O₃．3H₂O。

关键词 ：长期大气腐蚀, LY12, 剥蚀, 腐蚀失重, 力学性能

Abstract：

Atmospheric corrosion behavior of LY12 was investigated in five typical atmospheres in China over 20 years. Mass loss and loss in mechanical properties were measured; Appearance, cross-section photomicrograph and corrosion products were observed and analyzed by optical microscope and XRD. The results show that in hot and humid atmosphere of Wanning and Qionghai exfoliation corrosion occurred on LY12 after 6 and 10 years, respectively, and almost lost its mechanical properties after 20 years exposure. While in Beijing atmosphere, LY12 still performed excellent mechanical properties after 20 years exposure. The mass loss data were higher in Jiangjin and Qingdao due to higher average RH and SO₂ or Cl^- contamination of the atmosphere, and lowest in Beijing atmosphere because of lower average RH. Before exfoliation corrosion occurred, the mass loss data with exposure time obeyed well with power function C=KTⁿ. The main exfoliation corrosion products are γ-Al(OH)₃ and α-Al₂O₃．3H₂O.

Key words： long-term atmospheric corrosion LY12 exfoliation corrosion mass loss mechanical property

收稿日期: 2008-09-08

ZTFLH:

TG172.3

基金资助:

国家自然科学基金项目(50499331)和国家科技部基础条件平台建设项目(2005DKA10400-cj-2)资助

通讯作者: 郑弃非 E-mail: zhengqf@grinm.com

Corresponding author: ZHENG Qifei E-mail: zhengqf@grinm.com

作者简介: 孙霜青, 1981年生,男, 博士生, 研究方向为铝及铝合金的大气腐蚀

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	孙霜青
	郑弃非
	陈杰
	温军国
	李德富
44.8K

引用本文:

孙霜青郑弃非李德富陈杰温军国. LY12铝合金的长期大气腐蚀行为[J]. 中国腐蚀与防护学报, 2009, 29(6): 442-446.
XUN Shuang-Jing, ZHENG Qi-Fei, CHEN Jie, YUN Jun-Guo, LI De-Fu. LONG-TERM ATMOSPHERIC CORROSION BEHAVIOR OF LY12 ALUMINIUM ALLOY. J Chin Soc Corr Pro, 2009, 29(6): 442-446.

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2009/V29/I6/442

[1] Xiao Y Q, Xie S S, Liu J A, et al. Practical Directory of Aluminium Alloys Technology [M]. Beijing: Metallurgical Industry Press, 2005
    (肖亚庆, 谢水生, 刘静安等. 铝加工技术实用手册[M]. 北京: 冶金工业出版社, 2005)
[2] Guillaumin V, Mankowski G. Localized corrosion of 2024 T351 aluminium alloy in chloride media [J]. Corros. Sci., 1998, 41(3): 421-438
[3] Schmidt W, Stratmann M. Scanning kelvinprobe investigations of filiform corrosion on aluminum alloy 2024-T3 [J].Corros. Sci., 1998, 40(8): 1441-1443
[4] Zhang Z, Song S Z, Lu Y Z, et al. Corrosion behaviors of LY12CZ and LC4CS alumnium alloys in simulated atmosphere [J]. J. Chin. Soc. Corros. Prot., 2007, 27(3): 129-133
    (张正，宋诗哲，卢玉琢等. 模拟污染潮湿大气环境下LY12CZ、 LC4CS铝合金腐蚀行为研究 [J]. 中国腐蚀与防护学报，2007, 27(3): 129-133)
[5] An B G, Zhang X Y, Song S Z, et al. A study of electrochemical impedance spectrum for corrrosion behavior of LY12 aluminium alloy in simulated acid rain [J]. J. Chin. Soc. Corros. Prot., 2003, 23(3): 167-170
    (安百刚，张学元，宋诗哲等. LY12铝合金在模拟酸雨溶液中的阻抗谱研究 [J]. 中国腐蚀与防护学报，2003, 23(3): 167-170)
[6] Mikhailovsky Y N, Strekalov P V. Atmospheric corrosion testing in USSR. In: Ailor W H ed. Atmospheric Corrosion [M]. New York: John Wiley and Sons. 1982: 923-942
[7] Southwell C R, Bultman J D. Atmospheric Corrosion Testing in Tropics. Ailor W H. Atmospheric Corrosion [M]. New York: John Wiley and Sons, 1982: 943-967
[8] Fukushima T, Sato N, Hisamatsu Y,et al. Atmospheric Corrosion Testing in Japan.Ailor W H. Atmospheric Corrosion [M]. New York: John Wiley and Sons,1982: 841-872
[9] Sowinski G, Sprowls D O. Weathering of Aluminium Alloys. Ailor W H. Atmospheric Corrosion [M]. New York: John Wiley and Sons, 1982: 297-328
[10] Han D S, Li D. Correlation study ofaccelerated corrosion testing and outfield testing of aluminum alloy [J]. Corros. Prot, 2008, 29(3): 119-132
     (韩德盛, 李荻. LY12铝合金在海洋大气环境下加速腐蚀试验和外场暴露试验的相关性[J]. 腐蚀与防护, 2008, 29(3): 119-132
[11] Gan Z, Wang Y. Influence of microstructure on exfoliation corrosion of 2024 aluminium alloy[J]. Corros. Sci. Prot. Technol. 1995, 7(3):208-209
(甘株, 王云. 微观结构对LY12铝合金剥蚀的影响 [J]. 腐蚀科学与防护技术, 1995, 7(3): 208-209)
[12] Pourbaix M. The Linear Bilogarithmic Law for Atmospheric Corrosion. In: Ailor W H ed. Atmospheric Corrosion [M]. New York: John Wiley and Sons, 1982: 107-122
[13] Fuente D de la, Otero-Huerta E,Morcillo M. Studies of long-term weathering of aluminium in the atmosphere [J]. Corros. Sci., 2007, 49(7): 3134-3148
[14] Robinson M J, Role of wedging stresses in the exfoliation corrosion of high strength aluminium alloys [J]. Corros. Sci., 1983,23(8): 887-899
[15] Kelly D J, Robinson M J. Influence of heat treatment and grain shape on exfoliation corrosion of Al-Li alloy 8090 [J]. Corrosion. 1993, 49(10): 787-795
[16] Su J X, Zhang Z, Cao F H, et al. Review on the intergranular corrosion and exfoliation corrosion of aluminium alloys [J]. J. Chin. Soc. Corros. Prot., 2005, 25(3): 197-192
     (苏景新, 张昭, 曹发和等. 铝合金的晶间腐蚀与剥蚀 [J]. 中国腐蚀与防护学报, 2005, 25(3): 197-192)

[1]	陈磊,裴志亮,肖金泉,宫骏,孙超. 磁过滤电弧离子镀制备TiAlN涂层的结构与性能表征[J]. 中国腐蚀与防护学报, 2017, 37(3): 241-246.
[2]	元辛, 岳珠峰, 温世峰, 李磊. 铝合金表面有机硅环氧涂层的腐蚀电化学行为[J]. 中国腐蚀与防护学报, 2014, 34(4): 375-381.
[3]	王彬彬, 王振尧, 曹公望, 钟西舟, 柯伟. 受力的LY12和LC4铝合金在中国西部盐湖大气环境中的腐蚀行为[J]. 中国腐蚀与防护学报, 2014, 34(3): 287-293.
[4]	冯勇何德良龚德胜李菲吴建新. 国产825合金的耐腐蚀性能研究[J]. 中国腐蚀与防护学报, 2013, 33(2): 164-170.
[5]	吴进怡,罗琦,肖伟龙,柴柯,曹阳. 海水环境中弧菌对45钢腐蚀行为及力学性能的影响[J]. 中国腐蚀与防护学报, 2012, 32(4): 343-348.
[6]	钟曼英. 氢对2(1/4)Cr-1Mo钢力学性能的影响[J]. 中国腐蚀与防护学报, 2011, 31(3): 236-239.
[7]	李凤歧，田冲，曹小明，张劲松. 泡沫SiC/Cu双连续相复合材料在NaCl溶液中的腐蚀行为[J]. 中国腐蚀与防护学报, 2011, 31(2): 111-115.
[8]	黄昌龙，万小朋，赵美英，徐海蓉. 正应力对7150铝合金剥蚀行为的影响[J]. 中国腐蚀与防护学报, 2011, 31(2): 135-138.
[9]	黄昌龙,徐海蓉. 不同时效态对7150铝合金剥蚀行为的影响[J]. 中国腐蚀与防护学报, 2010, 30(6): 487-490.
[10]	赵羽习,任海洋. 基于固结试验和接触理论分析的铁锈力学性能[J]. 中国腐蚀与防护学报, 2010, 30(5): 383-390.
[11]	肖伟龙,柴柯,杨雨辉,吴进怡. 25钢在热带海洋环境下海水中的微生物腐蚀及其对力学性能的影响[J]. 中国腐蚀与防护学报, 2010, 30(5): 359-363.
[12]	薛艳;赵国仙;董会;赵大伟. 5Cr油管电化学充氢后的力学行为[J]. 中国腐蚀与防护学报, 2010, 30(1): 89-92.
[13]	俞芳高克玮路民旭. 流动状态下X65管线钢CO₂腐蚀产物膜结构和力学性能的评价[J]. 中国腐蚀与防护学报, 2009, 29(6): 401-404.
[14]	仝基斌饶思贤朱立群钟群鹏. 有/无应力下LY12CZ铝合金点蚀数据的关联规律[J]. 中国腐蚀与防护学报, 2009, 29(6): 504-508.
[15]	范林蔡健平张琦. LY12铝合金在周浸试验中的腐蚀行为[J]. 中国腐蚀与防护学报, 2009, 29(3): 215-219.

Viewed

Full text

Abstract

Cited

Shared

Discussed